DOE OSTI2024

Length scale effects of micro- and meso-scale tensile tests of unirradiated and irradiated Zircaloy-4 cladding

Zircaloy-4 is an essential material for cladding structures within fission-based reactors. To explore the changes in properties measured on differing length scales, FIB-machined micro-scale tensile tests were performed on both irradiated and control groups of Zircaloy-4. This was correlated with tensile testing on femtosecond laser-machined meso-scale specimens. Pronounced size effects were found when varying specimen geometry. Increases in tensile geometry size were associated with a reduction in measured yield stress for both irradiated and unirradiated samples. Here, meso-scale testing found strength and strain values similar to that of bulk-scale testing.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Femto-second Laser’s Enabling New Length Scale Fabrications for Rapid Post Irradiation Examination of Materials: Concluding LDRD Project Poster

Mechanical testing campaigns are required to qualify materials for advanced reactor conditions, yet economical and safety limitations restrict the number of standardized mechanical tests that can be performed. Reducing the size of the sample is one approach to addressing these challenges and to accelerating testing. Previous research has shown that smaller mechanical test samples produce higher yield and ultimate stress values compared to values measured from standard sample sizes: the “smaller is stronger” effect. Specimens used in accelerated material testing campaigns must reflect bulk material performance to enable engineering scale material property measurement. The objective of this research project was to determine if engineering scale mechanical behavior—the yield stress—could be measured with micro-tensile test samples smaller than traditional standard testing geometries. The relationship between yield stress and sample size was explored with two different nuclear-relevant structural materials: Zircaloy-4 and tungsten. Mechanical testing of both metals demonstrated decreasing yield stress values with increasing sample gauge size across three different sizes. Yield stress values from the largest gauge size, fabricated with a femto-second laser ablation system, approach bulk material yield stress values reported in published literature. Preliminary analysis of the tungsten samples indicates the yield stress value depends on the grain characteristics within the gauge section, in addition to the gauge size. Accompanying modeling efforts, including response surface generation and crystal plasticity approaches, further demonstrated that the size of the sample gauge section alone cannot explain the change in yield stress values.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Dynamic fracture processes in hydrogen embrittled iron

Mechanistic understanding of hydrogen embrittlement is critical to the transport and storage of hydrogen as a sustainable fuel. Experimental observation of dynamic fracture processes in hydrogen environments has been challenging. Here, in-situ transmission X-ray microscopy is used to image polycrystalline iron foils that are concurrently strained and electrochemically charged with hydrogen. Using this technique, voids and microcracks down to ∼30 nm in size are identified at or near the crack tip and tracked as strain is increased. We observe both hydrogen-induced transgranular failure and hydrogen-induced intergranular failure with distinct fracture processes. We find that transgranular fracture occurs through the formation of sharp branched structures at the main crack tip that are reminiscent of slip band formation. This is followed by void growth and coalescence, and interaction with secondary cracks that lead to propagation of the main crack. Intergranular fracture is found to occur through void coalescence along grain boundaries, along with significant secondary cracking near the crack tip. The crack growth rate is greater for void-mediated intergranular failure than for slip-mediated transgranular failure. Additionally, the removal of hydrogen results in recovered ductility for a crack initially propagated under hydrogen charging.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Detection of voids in hydrogen embrittled iron using transmission X-ray microscopy

Hydrogen embrittlement remains a barrier to widespread adoption of hydrogen as a carbon-neutral energy source. Here, hydrogen embrittlement mechanisms are investigated across length scales in iron using transmission X-ray microscopy (TXM), digital image correlation (DIC), and notched tensile testing during in-situ electrochemical hydrogen charging. TXM reveals void size and spatial distribution ahead of a propagating crack. We find hydrogen charging leads to voids within ~10 μm of the crack tip and suppression of voids beyond this distance. Near the crack tip, voids are elongated in the direction of the crack and are smaller than voids in an uncharged sample. In the presence of hydrogen, these voids lead to quasi-cleavage fracture and a sharper crack tip. DIC shows localization and reduction of plastic strain with hydrogen charging, and tensile testing reveals a reduction in fracture energy and elongation at failure. Finally, these results are discussed in the context of hydrogen embrittlement mechanisms.

08 HYDROGEN↗

DOE OSTI2022

Corrosion behavior of a series of combinatorial physical vapor deposition coatings on SiC in a simulated boiling water reactor environment

Here, the simulated boiling water condition corrosion properties of multilayer and combinatorial physical vapor deposition metal coatings (Zr, Cr, and/or Ti) deposited on a SiC f -SiC composite were investigated. Various compositions within the ternary system were corroded to the most suitable composition preventing underlying SiC f -SiC from further attack. Mass measurements and visual observations were conducted to identify which coatings formed protective oxides and which coatings spalled. Transmission electron microscopy was conducted to observe the microstructure of the physical vapor deposition metal layer before and after corrosion as well as identify the oxide which were forming.

36 MATERIALS SCIENCE↗