Reinforcement induced microcracking during the conversion of polymer-derived ceramics

This study investigates the role of discontinuous reinforcement on the microcracking of a preceramic polymer matrix during polymer to ceramic conversion. The material system comprised a carbosilane-based, preceramic polymer reinforced with mullite particles. The preceramic resin slurry was formulated for photopolymerization on a digital light projection 3D printer. Micro X-ray computed tomography, using a synchrotron light source, monitored a printed composite part during pyrolysis. The conversion of the carbosilane matrix into Si(O)C generated microcracks in the matrix that radially extended from particles. The likelihood of microcrack formation positively correlated with particle size. The largest particles (>10 4 µm 3 volume or >60 µm side length) always abutted microcracks, while the matrix surrounding smaller particles (<5 µm) was free of microcracks. Numerical calculations showed the particles resist the shrinking matrix during its conversion. This created tensile stresses within the matrix. The driving force for microcrack growth was also analyzed with regard to the influence of matrix material parameters, particle form-factor and crack length. These results reveal the need to consider the form factor of discontinuous reinforcements, with regard to the material properties of the polymer-derived ceramic, in order to reduce or eliminate defects in the final part.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Cracking during pyrolysis of preceramic polymers within glass microtubes

Abstract Cracking of preceramic polymers during pyrolysis under highly‐constrained conditions is examined by X‐ray computed tomography of fine glass microtubes containing the pyrolyzing material. The microtubes represent model geometries that mimic the long channels between fibers during production of ceramic composites by precursor impregnation and pyrolysis. Complementary fracture mechanics analyses of interface cracking and crack kinking are used to glean insights into the conditions under which periodic alternating cracks form. A key finding is that alternating cracks are an inherent feature of constrained pyrolysis . This feature is attributable in large part to the high energy release rates for interface cracks to kink into the pyrolyzing material under the hydrostatic tension developed during pyrolysis. It also requires interfaces with toughness comparable to that of the pyrolyzing material, to prevent large‐scale interface separation. The results further indicate the need for small uniform spaces for pyrolysis within fiber preforms in order to produce networks of fine periodic pyrolysis cracks; these networks in turn facilitate impregnation and pyrolysis in subsequent processing cycles.

Larson, Natalie M.↗