Insight into the interfacial microstructure and chemistry of hot isostatically pressed AA6061-AA6061 bonds for U-10Mo fuel cladding application

Here, in the present study, hot isostatic pressing (HIP) bonding was carried out using AA6061-AA6061 plates for U-10Mo monolithic fuel cladding application. HIP was performed at 560°C with an applied isostatic pressure of 103 MPa for 90 min. Interfacial microstructure characterizations were performed using scanning electron microscopy (SEM) combined with electron backscatter diffraction (EBSD) to quantify precipitate fractions and study recrystallization, grain growth, and orientation relationships across the interface. EBSD results confirmed that no interfacial grain growth occurred during the HIP process. Transmission electron microscopy (TEM) was also employed to quantify composition and identify phases of various precipitates and an oxide layer that formed at the interface during HIP bonding. Microstructural analyses revealed the formation of a large fraction of Mg 2 Si precipitate and a ~50 nm thick Mg-oxide layer at the interface. Further TEM analysis confirmed that the oxide layer was not continuous, and Mg 2 Al 2 O 5 oxide particles with an average size of 18 nm were present in the oxide layer. Finite element modeling analysis was performed to study the stress distribution at the interface during HIP processing.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Correlation between Interface Microstructure and Bond Strength of Al6061/Al6061 HIP-Bonded Plates for Fuel Cladding Application

The effects of hot isostatic pressing (HIP) processing parameters on microstructure and bond strength of Al6061/Al6061 plate interfaces were systemically investigated at the micro- and nanoscale. The HIP bonding of the two aluminum plates was performed at four temperatures: 350°C, 400°C, 450°C, and 560°C. The results reveal the formation of micron scaled Mg 2 Si precipitate and uniform nano scaled Mg 2 Al 2 O 5 oxide at the interface. The formation of Mg 2 Al 2 O 5 is closely associated with the fast bulk diffusion of Mg from the Al matrix to the amorphous Al 2 O 3 /Al interface and subsequent reaction between Mg and Al 2 O 3 . Finally, the highest and lowest bond strengths were observed in samples HIP bonded at 450°C and 350°C, respectively.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Microstructural-Level Fuel Performance Modeling of U-Mo Monolithic Fuel

As the physics that governs the microstructural evolution of nuclear fuel span various time and spatial scales, to fully understand the fuel behavior inevitably involves atomic to mesoscale resolution that can be difficult to determine experimentally. Microstructural-level modeling and simulations can be used to develop physics-based materials models that can provide physical understanding to inform fabrication process control, as well as a valuable feedback mechanism between post-irradiation examination (PIE) results and fabrication parameters. In accordance with the program schedule, the primary goals of the microstructure modeling effort are to: 1. Address critical microstructural questions and provide practical guidance to the fabricator via the fuel product specification; 2. Provide mechanistic inputs for the existing fuel performance code to improve its descriptive and predictive capability at the macroscopic scale. In fiscal year (FY)-21, the work scope consisted of six main facets: (1) the effect of carbides on fuel performance; (2) gas diffusivity in different phases; (3) integration of microstructural fuel performance modeling; (4) property degradation; (5) irradiation creep; and (6) historical analysis of microstructure data. Brief summaries of each are included below.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2020

Microstructural and micro-mechanical analysis of 14YWT nanostructured Ferritic alloy after varying thermo-mechanical processing paths into tubing

Microstructural analyses and micro-pillar compression were conducted on 14YWT nanostructured ferritic alloy (NFA) to compare different processing pathways: hydrostatic extrusion and Pilger processing with varying annealing temperatures into thin walled tubing, and after hot extrusion and cross-rolling into a plate. Hydrostatic extrusion at 815 °C resulted in the smallest grain sizes and highest yield strength of 1.20 GPa. Pilger processing with annealing at 800 °C had fine grained regions and bands of coarse grains, leading to a large variation in yield strength of 0.9–1.40 GPa. Higher annealing temperatures of 1200 °C after pilger processing significantly increased the grain size and lowered the yield strength to 1.01 GPa. These tubes showed a stronger (111) crystallographic texture in the normal direction and elongated grains in the extrusion direction. Characterization of the nano-oxides using TEM reveals more numerous, smaller oxides present in tubing processed at lower temperatures. Overall, this work shows NFA tubing after hydrostatic extrusion and pilger processing can lead to fine grained microstructures and texturing leading to higher yield strengths at lower annealing temperatures (e.g. 800 °C).

14YWT↗