Disorder-Induced Magnetotransport Anomalies in Amorphous and Textured Co 1– x Si x Semimetal Thin Films
Not Available
Engineering topics
Publications and source records attributed to Lavoie, Christian.
Not Available
Material properties of Ga–Sb binary alloy thin films deposited under ultra-high vacuum conditions were studied for analog phase change memory (PCM) applications. Crystallization of this alloy was shown to occur in the temperature range of 180–264 °C, with activation energy >2.5 eV depending on the composition. X-ray diffraction (XRD) studies showed phase separation upon crystallization into two phases, Ga-doped A7 antimony and cubic zinc-blende GaSb. Synchrotron in situ XRD analysis revealed that crystallization into the A7 phase is accompanied by Ga out-diffusion from the grains. X-ray absorption fine structure studies of the local structure of these alloys demonstrated a bond length decrease with a stable coordination number of 4 upon amorphous-to-crystalline phase transformation. Mushroom cell structures built with Ga–Sb alloys on ø110 nm TiN heater show a phase change material resistance switching behavior with resistance ratio >100 under electrical pulse measurements. TEM and Energy Dispersive Spectroscopy (EDS) studies of the Ga–Sb cells after ∼100 switching cycles revealed that partial SET or intermediate resistance states are attained by the variation of the grain size of the material as well as the Ga content in the A7 phase. A mechanism for a reversible composition control is proposed for analog cell performance. These results indicate that Te-free Ga–Sb binary alloys are potential candidates for analog PCM applications.
Abstract The performance of next-generation, nanoelectronic devices relies on a precise understanding of strain within the constituent materials. However, the increased flexibility inherent to these three-dimensional device geometries necessitates direct measurement of their deformation. Here we report synchrotron x-ray diffraction-based non-destructive nanoscale mapping of Si/SiGe nanosheets for gate-all-around structures. We identified two competing mechanisms at different length scales contributing to the deformation. One is consistent with the in-plane elastic relaxation due to the Ge lattice mismatch with the surrounding Si. The second is associated with the out-of-plane layering of the Si and SiGe regions at a length scale of film thickness. Complementary mechanical modeling corroborated the qualitative aspects of the deformation profiles observed across a variety of nanosheet sample widths. However, greater deformation is observed in the SiGe layers of the nanosheets than the predicted distributions. These insights could play a role in predicting carrier mobilities of future devices.