Dielectric composites incorporating enthalpy stabilization for NbTi windings

Composites of ceramic powders in epoxies appropriate for both insulating and impregnating NbTi windings are studied. Specific heat, thermal conductivity, thermal contraction, and magnetocaloric measurements on composites are presented. Thermal contractions well matched to copper are found and thermal shock resistance is greatly enhanced. Enthalpies, 4.2-6 K, range up to 80 mJ/cu cm and are 20-50 times larger than that of the pure epoxies. Results are not specific to the epoxies used but apply to composites with any amorphous matrices.

Lawless, W. N.↗
NASA NTRS1981

Evaluation of ceramic packed-rod regenerator matrices

An extensive evaluation of a modified cryocooler with various regenerator matrices is reported. The matrices examined are 0.015 in. diam. Pb spheres and 0.008, 0.015, and 0.030 in. diam. rods of a 0.2% SnCl2 doped ceramic labelled LS-8A. Specific heat and thermal conductivity data on these rod materials are also reported. The chronic pulverization/dusting problem common to Pb spheres was investigated. During a 1000 hr life test with 0.0008 in. diam. rods there was no degradation of the refrigerator performance, and a subsequent examination of the rods themselves revealed no evidence of breakage or pulverization. The load temperature characteristics for the rod packed regenerators were inferior to that for the Pb spheres, the effect being to shift the Pb spheres load curve up in temperature. This temperature shift was 5.0, 7.4, and 11.6K for the 0.0008, 0.015, and 0.030 in. diam. rods, respectively.

Lawless, W. N.↗
NASA NTRS1979

Evaluation of high specific-heat ceramic for regenerator use at temperatures between 2-30 K

Specific heat, thermal conductivity (both in the range 2-30 K), and microhardness data were measured on the ceramics labelled LS-8, LS-8A, and LS-8A doped with CsI, SnCl2, and AgCl. A work hardened sample of LS-8A was also studied in an effort to determine the feasibility of using these types of LS-8 materials to replace Pb spheres in the regenerator of the JPL cryocooler. The LS-8A materials are all more than an order of magnitude harder than Pb, and the dopants do not significantly improve the hardness. However, the SnCl2 dopant has a remarkable effect in improving the specific heat and thermal conductivity of LS-8A. The SnCl2 doping level which maximized the regenerator enthalpy change in going from an unloaded to a loaded condition was found to be 0.2 percent SnCl2 in LS-8A. It was also found that the enthalpy change for a regenerator employing the LS-8A material is more than three times larger than for the Pb spheres case. The use of rods, rather than spheres, of optimally doped LS-8A in regenerators is discussed.

Lawless, W. N.↗