Dual-stage K + ion intercalation in V 2 O 5 -conductive polymer composites
We reported that the incorporation of a conductive polymer into V 2 O 5 materials resulted in an increased interlayer distance of 2.2 nm, favoring K + ion storage in aqueous electrolyte. In situ X-ray diffraction showed that during charging, K + ions were first inserted into the interlayer region of V 2 O 5 through pseudocapacitive intercalation and then continued to be inserted into the [VO 6 ] bi-layer region via diffusion-limited intercalation. Furthermore, this reversible dual-stage insertion/extraction mechanism provides new battery chemistry allowing the storage of around 50% more alkali ions in the intralayer region besides van der Waals gaps.
Could Irradiation Introduce Oxidized Oxygen Signals in Resonant Inelastic X-ray Scattering of Battery Electrodes?
The characterization of oxidized oxygen states through high-efficiency mapping of resonant inelastic X-ray scattering (mRIXS) has become a crucial approach for studying the oxygen redox activities in high-energy battery cathodes. However, this approach has been recently challenged due to the concern of irradiation damage. In this work, we revisited a typical Li-rich electrode, Li 1.144 Ni 0.136 Mn 0.544 Co 0.136 O 2 , in both lithiated and delithiated states and evaluated the X-ray irradiation effect in the lengthy mRIXS experiments. Our results show that irradiation cannot introduce any oxidized oxygen feature, and the features of oxidized oxygen are weakened with a high X-ray dose. The results confirm again that mRIXS detects the intrinsic oxidized oxygen state in battery electrodes. However, the distinct irradiation effects in different systems imply that irradiation could selectively target the least stable elemental or chemical states, which should be analyzed with caution in the study of active chemical states.
Resonant doping for high mobility transparent conductors: the case of Mo-doped In2O3
Explore the source record for details and available documents.
Influence of Polymorphism on the Electronic Structure of Ga 2 O 3
The search for new wide-band-gap materials is intensifying to satisfy the need for more advanced and energy-efficient power electronic devices. Ga 2 O 3 has emerged as an alternative to SiC and GaN, sparking a renewed interest in its fundamental properties beyond the main β-phase. Here, three polymorphs of Ga 2 O 3 , α, β, and ε, are investigated using X-ray diffraction, X-ray photoelectron and absorption spectroscopy, and ab initio theoretical approaches to gain insights into their structure–electronic structure relationships. Valence and conduction electronic structure as well as semicore and core states are probed, providing a complete picture of the influence of local coordination environments on the electronic structure. State-of-the-art electronic structure theory, including all-electron density functional theory and many-body perturbation theory, provides detailed understanding of the spectroscopic results. The calculated spectra provide very accurate descriptions of all experimental spectra and additionally illuminate the origin of observed spectral features. This paper provides a strong basis for the exploration of the Ga 2 O 3 polymorphs as materials at the heart of future electronic device generations.
Ultrafast ion transport at a cathode–electrolyte interface and its strong dependence on salt solvation
Not provided.
Mapping Competitive Reduction upon Charging in LiNi 0.8 Co 0.15 Al 0.05 O 2 Primary Particles
Side reactions involving surface reduction play a critical role in the failure of LiNi 0.8 Co 0.15 Al 0.05 O 2 to reach its theoretical capacity as a cathode material for Li-ion batteries. While macroscopic consequences are known, the underlying nanoscopic mechanisms are not fully elucidated. By coupling X-ray spectroscopy with several X-ray microscopy modalities, we have spatially resolved the extent of Ni oxidation at several states of charge and uncovered heterogeneity that is hidden when considering ensemble measurements alone. The use of morphologically controlled particles enabled high-resolution imaging of these materials, uncovering gradients of Ni oxidation states within individual primary particles. At high states of charge, these gradients revealed regions of possible oxygen deficiency extending deeper into the particle than previously observed. Surface-sensitive X-ray coupled scanning tunneling microscopy allows oxidation states to be measured at the material's surface, showing predominantly Ni II in the first atomic layer and mixtures of Ni II with Ni III /Ni IV already appearing 1.5 nm into the particle. These results reveal the subtle interplay between irreversible surface transformations and the bulk reactions that ultimately define function, which will refine strategies of surface passivation that are key to overcoming current performance limitations.
Revisiting the charge compensation mechanisms in LiNi[subscript 0.8]Co[subscript 0.2;#8722;y]Al[subscript y]O[subscript 2] systems
Abstract not provided
How Bulk Sensitive is Hard X-ray Photoelectron Spectroscopy: Accounting for the Cathode–Electrolyte Interface when Addressing Oxygen Redox
Sensitivity to the `bulk' oxygen core orbital makes hard X-ray photoelectron spectroscopy (HAXPES) an appealing technique for studying oxygen redox candidates. Various studies have reported an additional O 1s peak (530-531 eV) at high voltages, which has been considered a direct signature of the bulk oxygen redox process. Here, we find the emergence of a 530.4 eV O 1s HAXPES peak for three model cathodes, Li 2 MnO 3 , Li-rich NMC, and NMC 442, that shows no clear link to oxygen redox. Instead, the 530.4 eV peak for these three systems is attributed to transition metal reduction and electrolyte decomposition in the near-surface region. Claims of oxygen redox relying on photoelectron spectroscopy must explicitly account for the surface sensitivity of this technique and the extent of the cathode degradation layer.