NASA NTRS1992

Reduction of thermal stresses in continuous fiber reinforced metal matrix composites with interface layers

The potential of using interface layer to reduce thermal stresses in the matrix of composites with a mismatch in coefficients of thermal expansion of fiber and matrix has been investigated. It was found that compliant layers, with properties of readily available materials, do not have the potential to reduce thermal stresses significantly. However, interface layers with high coefficient of thermal expansion can compensate for the mismatch and reduce thermal stresses in the matrix significantly.

Jansson, S.↗

NASA NTRS1991

Mechanical behavior of a continuous fiber reinforced aluminum matrix composite subjected to transverse and thermal loading

The transverse properties of an aluminum alloy metal matrix composite reinforced by continuous alumina fibers were investigated. The composite is subjected to both mechanical and cyclic thermal loading. The results of an experimental program indicate that the shakedown concept of structural mechanics provides a means of describing the material behavior. When the loading conditions are within the shakedown region, the material finally responds in an elastic manner after initial plastic response, and for loading conditions outside the shakedown region, the material exhibits a rapid incremental plastic strain accumulation. The failure strain varies by an order of magnitude according to the operating conditions. Hence, for high mechanical and low thermal loading, the failure strains is small; for low mechanical and high thermal loading, the failure strain is large.

Jansson, S.↗

NASA NTRS1991

Elasto-plastic analysis of interface layers for fiber reinforced metal matrix composites

The mismatch in coefficients of thermal expansion (CTE) of fiber and matrix in metal matrix composites reinforced with ceramic fibers induces high thermal stresses in the matrix. Elasto-plastic analyses - with different degrees of simplification and modelization - show that an interface layer with a sufficiently high CTE can reduce the tensile hoop stress in the matrix substantially.

Doghri, I.↗

NASA NTRS1991

Long term integrity for space station power systems

A study was made of the High Temperature Design Codes ASME N47, British R5, and the French RCC-MR Rules. It is concluded that all these codes provide a good basis of design for space application. The new British R5 is the most complete since it deals with the problem of defects. The ASME N47 was subjected longer to practical application and scrutiny. A draft code is introduced, and a proposed draft for high temperature design in which attempts were made to identify gaps and improvements is suggested. The design is limited by creep characteristics. In these circumstances, life is strongly affected by the selected value of the factor of safety. The factor of safety of primary loads adopted in the codes is 1.5. Maybe a lower value of 1.25 is permissible for use in space. Long term creep rupture data for HAYNES 188 is deficient and it is suggested that extrapolation methods be investigated.

Leckie, F. A.↗

NASA NTRS1991

Transverse ductility of metal matrix composites

The role of the fiber matrix interface bond on the transverse ductility of continuous fiber reinforced composites has been investigated. Two specific systems have been considered: an Aluminum alloy matrix reinforced by Alumina fibers, characterized by a strong interface and a Titanium alloy reinforced by coated Silicon Carbide fibers, characterized by a weak interface. A micro-mechanical study indicates that the bond condition has a significant effect on the state of stress in the matrix which in turn dictates the available matrix ductility. The micro-mechanical predictions are in good agreement with the experimental results for the two systems.

Gunawardena, S. R.↗

NASA NTRS1990

Inhomogeneous deformation in INCONEL 718 during monotonic and cyclic loadings

The paper concentrates on the relation between microstructural observations of the dislocation structures and the macroscopic deformation responses of both aged and homogenized precipitate-hardened alloys at room temperature. The deformation responses are compared to the cyclic deformation response of an aged precipitate-hardened alloy. Early in the deformation, one deformation band per grain and little evidence of work hardening are observed; with increased deformation, work hardening begins, more bands nucleate, and their spacing becomes similar to that in the aged material. It is pointed out that the degree of coarseness of inhomogeneous deformation is not a result of a softening process within the bands due to precipitate shearing, but it is a function of the amount of work hardening within the bands.

Worthem, D. W.↗

NASA NTRS1990

Optimization of interface layers in the design of ceramic fiber reinforced metal matrix composites

The potential of using an interface layer to reduce thermal stresses in the matrix of composites with a mismatch in coefficients of thermal expansion (CTE) of fiber and matrix was investigated. It was found that the performance of the layer can be defined by the product of the CTE and the thickness, and that a compensating layer with a sufficiently high CTE can reduce the thermal stresses in the matrix significantly. A practical procedure offering a window of candidate layer materials is proposed.

Doghri, I.↗

NASA NTRS1990

Reduction of thermal stresses in continuous fiber reinforced metal matrix composites with interface layers

The potential of using an interface layer to reduce thermal stresses in the matrix of composites with a mismatch in coefficients of thermal expansion of fiber and matrix was investigated. It was found that compliant layers, with properties of readily available materials, do not have the potential to reduce thermal stresses significantly. However, interface layers with high coefficient of thermal expansion can compensate for the mismatch and reduce thermal stresses in the matrix significantly.

Jansson, S.↗

NASA NTRS1990

Materials with periodic internal structure: Computation based on homogenization and comparison with experiment

The combination of thermal and mechanical loading expected in practice means that constitutive equations of metal matrix composites must be developed which deal with time-independent and time-dependent irreversible deformation. Also, the internal state of composites is extremely complicated which underlines the need to formulate macroscopic constitutive equations with a limited number of state variables which represent the internal state at the micro level. One available method for calculating the macro properties of composites in terms of the distribution and properties of the constituent materials is the method of homogenization whose formulation is based on the periodicity of the substructure of the composite. A homogenization procedure was developed which lends itself to the use of the finite element procedure. The efficiency of these procedures, to determine the macroscopic properties of a composite system from its constituent properties, was demonstrated utilizing an aluminum plate perforated by directionally oriented slits. The selection of this problem is based on the fact that, extensive experimental results exist, the macroscopic response is highly anisotropic, and that the slits provide very high stress gradients which severely test the effectiveness of the computational procedures. Furthermore, both elastic and plastic properties were investigated so that the application to practical systems with inelastic deformation should be able to proceed without difficulty. The effectiveness of the procedures was rigorously checked against experimental results and with the predictions of approximate calculations. Using the computational results it is illustrated how macroscopic constitutive equations can be expressed in forms of the elastic and limit load behavior.

Jansson, S.↗