Surface characterization and failure analysis of thermally aged, polyimide bonded titanium
This study of high temperature stable adhesive systems using 6Al-4V titanium adherends found that certain adhesive/adherends exhibit a change from cohesive to adhesive failure mode during long term 450 F thermal aging. Lap-shear specimens which exhibited adhesive failures were subjected to failure analysis using scanning transmission electron microscopy (STEM) and surface analysis techniques. Data is presented which supports the conclusion of interfacial failures for these samples.
Peters, P. D.↗