DOE OSTI2025

Nanoindentation’s imprint on an advanced society: Toward application conditions at the extremes

Abstract As society strives for a more sustainable future, key technologies depend on advanced materials development. Nanoindentation enables highly localized nanoscale measurement of mechanical properties, crucial for optimizing the performance of functional materials. Coupled with chemical charging, variable temperatures, or high deformation speeds, it offers insights into pressing materials science challenges necessary for sustainable energy transitions. This article explores the role of nanoindentation in advancing vital next-generation technologies. Graphical abstract

36 MATERIALS SCIENCE↗

DOE OSTI2024

Tension-compression asymmetry in superelasticity of SrNi 2 P 2 single crystals and the influence of low temperatures

ThCr 2 Si 2 -type intermetallic compounds are known to exhibit superelasticity associated with structural transitions through lattice collapse and expansion. These transitions occur via the formation and breaking of Si-type bonds, respectively, under uniaxial loading along the [0 0 1] direction. Unlike most ThCr 2 Si 2 -type intermetallic compounds, which have either an uncollapsed tetragonal structure or a collapsed tetragonal structure, SrNi 2 P 2 possesses a third type of collapsed structured: a one-third orthorhombic structure, for which one expects the occurrence of unique structural transitions and superelastic behavior. In this study, uniaxial compression and tension tests were conducted on micron-sized SrNi 2 P 2 single crystalline columns at room temperature, 200 K, and 100 K, to investigate the influence of loading direction and temperature on the superelasticity of SrNi 2 P 2 . Experimental data and density functional theory calculations revealed the presence of tension-compression asymmetry in the structural transitions and superelasticity, as well as an asymmetry in their temperature dependence, due to the opposite superelastic process associated with compression (forming P-P bonds) and tension (breaking P-P bonds). Additionally, following thermodynamics, the observations suggest that this asymmetric superelasticity could lead to an opposite elastocaloric effect between compression and tension, which could be beneficial potentially in obtaining large temperature changes compared to conventional superelastic solids that show the same elastocaloric effect regardless of loading direction. Furthermore, these results provide an important fundamental insight into the structural transitions, superelasticity processes, and potential elastocaloric effects in SrNi 2 P 2 .

36 MATERIALS SCIENCE↗

DOE OSTI2023

High-strength, lightweight nano-architected silica

Continuous nanolattices are an emerging class of mechanical metamaterials that are highly attractive due to their superior strength-to-weight ratios, which originate from their spatial architectures and nanoscale-sized elements possessing near-theoretical strength. Rational design of frameworks remains challenging below 50 nm because of limited methods to arrange small elements into complex architectures. Here, we fabricate silica frameworks with ~4- to 20-nm-thick elements using self-assembly and silica templating of DNA origami nanolattices and perform in situ micro-compression testing to examine the mechanical properties. We observe strong effects of lattice dimensions on yield strength (σ $\mathcal{y}$ ) and failure mode. Silica nanolattices are found to exhibit yield strengths higher than those of any known engineering materials with similar mass density. The robust coordination of the nanothin and strong silica elements leads to the combination of lightweight and high-strength framework materials offering an effective strategy for the fabrication of nanoarchitected materials with superior mechanical properties.

77 NANOSCIENCE AND NANOTECHNOLOGY↗

DOE OSTI2023

Effects of rhodium doping on dislocation nucleation in a [001] SrNi 2 P 2 single crystal under spherical nanoindentation

Nanoindentation was performed on SrNi 2 P 2 single crystals and their dilute solid solutions, Sr(Ni 1–x Rh x ) 2 P 2 (x = 0 ~ 0.055), under [001] loading to investigate the effects of elemental doping on Young’s modulus and dislocation nucleation stress. The results show that Young’s modulus and the dislocation nucleation stress decrease as the Rh content increases, and their Rh content dependence also varies with the Rh content. Electron diffraction analysis and the anisotropic lattice distortion calculations revealed that a local structural transition from the orthorhombic superstructure to the tetragonal structure and local compressive residual stresses could be the main reasons for the decrease in Young’s modulus and dislocation nucleation stress, respectively. The overlap of stress–strain fields between Rh atoms and the associated local structural transition contribute to their Rh content dependence. Here, the results also indicate that elemental doping does not necessarily strengthen materials if the incipient plasticity is controlled by dislocation nucleation, unlike conventional solid solution strengthening.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Pseudoelasticity of SrNi2P2 Micropillar via Double Lattice Collapse and Expansion

The maximum recoverable strain of most crystalline solids is less than 1% because plastic deformation or fracture usually occurs at a small strain. In this work, we show that a SrNi 2 P 2 micropillar exhibits pseudoelasticity with a large maximum recoverable strain of ~14% under uniaxial compression via unique reversible structural transformation, double lattice collapse–expansion that is repeatable under cyclic loading. Its high yield strength (~3.8 ± 0.5 GPa) and large maximum recoverable strain bring out the ultrahigh modulus of resilience (~146 ± 19 MJ/m 3 ), a few orders of magnitude higher than that of most engineering materials. The double lattice collapse–expansion mechanism shows stress–strain behaviors similar to that of conventional shape-memory alloys, such as hysteresis and thermo-mechanical actuation, even though the structural changes involved are completely different. Our work suggests that the discovery of a new class of high-performance ThCr 2 Si 2 -structured materials will open new research opportunities in the field of pseudoelasticity.

77 NANOSCIENCE AND NANOTECHNOLOGY↗

DOE OSTI2020

Uniaxial compression of [001]-oriented CaFe 2 As 2 single crystals:the effects of microstructure and temperature on superelasticity Part I: Experimental observations

Micropillar compression experiments on [001]-oriented CaFe 2 As 2 single crystals have recently revealed the existence of superelasticity with a remarkably high elastic limit of over 10%. The collapsed tetragonal phase transition, which is a uni-axial contraction process in which As-As bonds are formed across an intervening Ca-plane, is the main mechanism of superelasticity. Usually, superelasticity and the related structural transitions are affected strongly by both the microstructure and the temperature. As such, in this study, we investigated how the microstructure and temperature affect the superelasticity of [001]-oriented CaFe 2 As 2 micropillars cut from solution-grown single crystals, by performing a combination of in-situ cryogenic micromechanical testing and transmission electron microscopy studies. Our results show that the microstructure of CaFe 2 As 2 is influenced strongly by the crystal growth conditions and by subsequent heat treatment. The presence of Ca and As vacancies and FeAs nanoprecipitates affect the mechanical behavior significantly. In addition, the onset stress for the collapsed tetragonal transition decreases gradually as the temperature decreases. These experimental results are discussed primarily in terms of the formation of As-As bonds, which is the essential feature of this mechanism for superelasticity. Our research outcomes provide a more fundamental understanding of the superelasticity exhibited by CaFe 2 As 2 under uni-axial compression.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Low-temperature failure mechanism of [001] niobium micropillars under uniaxial tension

The plasticity of body-centered cubic (bcc) metals is dependent of temperature as well as sample dimension at the micrometer scale, but the effects of cryogenic temperature on the plasticity and the related failure process in micron-sized bcc metals have not been studied under uniaxial tension. In this work, we utilized in situ cryogenic micro-tensile tests, transmission electron microscopy, and dislocation dynamic simulations to examine the plasticity and failure processes of [001]-oriented bcc niobium micropillars. Our study reveals that a strong suppression of cross-slip at low temperatures prevents dislocation multiplication and leads to a dislocation starvation state, at which no mobile dislocation exists due to the rapid annihilation of dislocations at free surfaces. New dislocations are then nucleated until stress concentration at a slip step creates a micro-crack, the propagation of which leads to catastrophic failure. As a result, this unique failure process results from the combined effects of sample dimension and temperature.

36 MATERIALS SCIENCE↗