Mechanical and thermal behavior of additively manufactured Invar 36 using a laser hot wire hybrid DED process

Invar 36 alloy is a material of high interest in the composite tooling sector due to its low coefficient of thermal expansion. Current production of Invar 36 tooling using traditional manufacturing such as casting and forging is associated with long lead times due to a multitude of factors such as labor and component shortages, high material costs, foreign competition, and supply chain issues. An attractive alternate process is the use of an integrated 5-axis CNC hybrid Laser Hot Wire Deposition System (LHWD) for manufacturing invar molds. Here, the hybrid process provides a combination of the additive and subtractive technologies resulting in a synergistic platform for producing and repairing structures and molds. The main novelty and goal of this work is to study the properties of Invar deposited by a LHWD and to provide guidelines for the manufacture of parts using this process. In this study, the thermal expansion behavior of the manufactured specimens has been analyzed and related to its printing parameters and direction. Multiple specimens were extracted for mechanical, dilatometry and metallographic testing. A thermal IR recording of the printing process was also carried out to observe the thermal history of the produced parts to establish thermal influence on performance-property-processing relationship. The results of these tests show the advantage of LHWD technology for the manufacture of Invar alloy parts, as it presents similar thermal expansion behavior as those commercially available with minimal presence of precipitates and no macrostructural failures such as pores, cracks and lacks of fusion.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Integrated top-down process and voxel-based microstructure modeling for Ti-6Al-4V in laser wire direct energy deposition process

Laser-wire metal additive manufacturing (AM) is one of the ideal direct energy deposition (DED) processes for creating large-scale parts with a medium level of complexity. However, the DED process involves complex thermal signatures and wide length scales making the fabrication of realistic AM components and part qualification often reliant on experimental trial-and-error optimization. While experimental measurements over the full volume of a part are valuable and necessary, measuring the entire area of a part is significantly laborious and practically infeasible, particularly for large parts in terms of cost and rapid qualification. Therefore, in this work, we developed an effective thermal and microstructure modeling framework based on the Johnson–Mehl-Avrami-Kolmogorov (JMAK) and Koistinen & Marburger (KM) models through a top-down approach that considers plate distortion-affected thermal profiles. A voxel-by-voxel simulation method is used to predict individual phase fractions of Ti-6Al-4 V. The predicted results were validated through detailed metallurgical measurements. A combined voxel-by-voxel approach with a sparse data reconstruction technique produced a near-perfect reconstruction of the original data. This approach anticipates a significant reduction in data points and computation time and resources. Lastly, we conclude with potential extensions of this work to other modeling efforts.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Strength-ductility synergy through microstructural and compositional heterogeneity in directed energy deposition additive manufacturing of face-centered cubic materials

Directed energy deposition (DED) is an additive manufacturing (AM) process based on welding technology and offers the advantages of large build volume, high deposition rate, and ability to fabricate multi-material parts. Epitaxial continuous columnar grain growth is a characteristic microstructural feature of DED processed alloys. In this study, a bamboo-like microstructure (periodic alternation of equiaxed and columnar structure) was produced by adopting an intermittent deposition strategy in 316L stainless steel and Inconel 625. The formation of a bamboo-like alternating microstructure was confirmed through electron backscattered diffraction (EBSD) analysis. Hardness mapping showed that the columnar to equiaxed transition (CET) occurred at the region right below the fusion line. A finite element (FE) model was used to investigate the relationship between the temperature gradient (G) and the solidification rate (R). The FE model showed a low G/R ratio at the region right below the interface promoting the CET. The grain size and material-dependent deformation behaviors are analyzed using digital image correlation (DIC). The lower deformation on the fine-grain regions observed in DIC analysis is attributed to a higher strain hardening rate, which is confirmed through dislocation density analysis on a tensile-interrupted specimen. The periodically alternating grain size coupled with the microstructural changes caused by intermittent deposition strategy result in a better strength-ductility synergy in both single-material and bimetallic specimens.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Controlling microstructure and B2 ordering kinetics in Fe–Al system through additive manufacturing

Multi-material fabrication between steel and aluminum is challenging because of the formation of several intermetallic phases. Embrittling B2 ordered intermetallics form in the steel rich side and are stable till about 60% of Al dilution in steel. In this work by using multi-length scale characterization coupled with integrated computational process and thermokinetic modeling, we show that the ordered B2 intermetallics in the steel rich side of the Fe–Al system forms via a nucleation and growth mechanism. The extent of B2 ordered intermetallics can be controlled by modifying the directed energy deposition-additive manufacturing (DED-AM) process parameters. Our findings lay the foundation for enabling fabrication of crack-free functionally graded compositions between the two alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Influence of printing parameters on the mechanical behavior of 3D-printed SS316L parts manufactured using laser hot wire directed energy deposition

Hybrid manufacturing combines the simultaneous benefits of additive manufacturing (complex geometries, part consolidation, and mass customization) with the advantages of subtractive manufacturing (superior surface finish and enhanced dimensional accuracies) by integrating a suite of complementary traditional processes into a base platform of additive manufacturing. The use of hybrid technology has grown in recent years given its capabilities on repairing metallic structures, producing parts with conformal cooling features, and manufacturing functionally graded products. These kinds of capabilities are of great interest to the medical implant, energy, automotive, maritime, and aerospace industry sectors, among many other fields. This work investigated the mechanical properties of stainless steel (SS) 316L as a function of different tool paths strategies using an integrated 5-axis CNC hybrid Mazak system with a laser hot wire deposition system (LHWDS). This study includes the evaluation of different printing parameters and their impact on the quality of the printed bead as well as the incorporation of a structure–property material relationship based on the mechanical performance of the manufactured coupons.

36 MATERIALS SCIENCE↗
DOE OSTI2024

The potential of wire arc directed energy deposition

A diverse team of materials scientists, systems engineers and computational scientists at the Manufacturing Demonstration Facility at Oak Ridge National Laboratory (ORNL) is working closely with industry to employ WA-DED to transform the current manufacturing supply chains and change industry perception of metal-AM-fabricated components.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Considering interplay between multiple physical phenomena to elucidate single crystal-like texture, phase transformations, and mechanical behavior of directed energy deposited SS316L

A widespread implementation of large scale additive manufacturing (AM) processes, such as wire arc-directed energy deposition (WA-DED) AM can transform the current manufacturing supply chain networks. Naturally, such implementation requires control of the microstructural attributes, such as texture and phase evolution in the processed alloys. Currently, the texture evolution in fusion-based AM (F-BAM) processes is majorly rationalized by the phenomena occurring only during solidification. However, such rationalization is insufficient for understanding the evolution of primary and secondary crystallographic orientations, and consequently, fails to offer a comprehensive understanding and control of overall texture in F-BAM processed alloys. To this end, we report a single crystal (SX)-like texture in WA-DED processed SS316L for the first time. Furthermore, we assess the physical phenomena that may lead to such unique microstructural evolution during WA-DED AM. Subsequently, using microstructural characterization spanning the build height and thermomechanical simulations we investigate the effect of competitive growth and epitaxial growth occurring during solidification and thermally induced plastic deformation occurring post solidification on the overall texture of WA-DED processed SS316L. A spatial variation in solidification pathway is also established and correlated with variation in undercoolings across the build. Tensile tests revealed a strong orientation dependence of deformation mechanisms with over 110% elongation to failure of specimens deformed along <011>. Such anisotropy is rationalized using Schmid's analysis of dislocation slip and deformation twinning. Importantly, overall, the mechanisms outlined in this work will facilitate an enhanced understanding and subsequent control of texture evolution, solidification behavior and mechanical behavior of WA-DED processed steels.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Wire directed energy deposition of steel-aluminum structures using cold metal transfer process

In this study, a sharp transition from 316L stainless steel to 4043 aluminum alloy was fabricated using wire directed energy deposition (DED) via the cold metal transfer (CMT) process. The CMT process with its inherently low heat input, led to a significant reduction in intermetallic thickness at the bi-metallic interface compared to blown powder DED technique reported in the literature resulting in superior properties when compared to those of dissimilar steel-aluminum welds. Thermo-kinetic modeling confirmed that the intermetallic formation is through a classical nucleation and growth mechanism, and the fraction and thickness can be controlled by adjusting CMT process parameters to kinetically arrest or minimize the intermetallic formation. These findings underscore the efficacy of CMT-based wire DED for fabrication of steel-aluminum bi-metallic structures.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Investigating stainless steel/aluminum bimetallic structures fabricated by cold metal transfer (CMT)-based wire-arc directed energy deposition

Here, this study investigated the process of fabricating a bimetallic structure of 316L stainless steel (SS) and 4043 aluminum (Al) using wire-arc directed energy deposition (DED) based on the cold metal transfer (CMT) process. The impact of heat input on the fabricated structure’s geometry, porosity, and microstructures at the interface, with a specific emphasis on the intermetallic compound (IMC) formation, and the subsequent impact on the joint strength of the structure, were studied. The IMC layer at the interface was predominantly comprised of FeAl 2 Si. For the various heat input conditions studied, the IMC layer's thickness varied from 5 µm to 18 µm. The tensile strength reached up to approximately 130 MPa, which is among the highest reported in the literature for steel/Al bimetallic structures. The specimens fabricated with high heat input conditions had a thicker IMC layer at the steel/Al interface, resulting in a more brittle interface and degradation of the mechanical properties.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Review of in situ process monitoring for metal hybrid directed energy deposition

Hybrid manufacturing, or the combination of additive and subtractive manufacturing within a single build volume is transforming the way products are being fabricated. Additive manufacturing confers unprecedented freedom of design and reduced material usage while enabling serial customization. Subtractive manufacturing provides superior surface finish and improved dimensional accuracies. Interwoven, these two digital manufacturing paradigms are enabling the rapid manufacturing of complex, highly accurate, and customized geometries in a diversity of high-performance alloys. In situ monitoring, heavily relied upon in either additive or subtractive, becomes even more crucial with the interplay of the two processes in a single combined build sequence. Moreover, challenges that do not exist in either process alone can now have a dramatic impact on final part quality: (1) a large amount of heat is generated during additive manufacturing deposition, which is primarily dissipated into the machine tooling and impacts accuracy by deforming the material and causing misaligned machining; (2) microstructure, mechanical properties, and residual stresses are the result of the complex thermal histories generated by additive manufacturing and can impact subsequent cutting performance. This comprehensive review considers previous research in monitoring and providing closed-loop control in both additive and subtractive manufacturing separately and then considers the implications of the effectiveness of these monitoring techniques when additive and subtractive processes are integrated together.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Repairing High γ’ Hot Section Gas Turbine Components Using Advanced Manufacturing

This article describes the ability to use laser-blown powder deposition to repair high γ' IN-100 superalloy gas turbine components. The influence of various process conditions on the ability to make crack-free IN-100 deposits over surrogate high γ' alloys was investigated to identify cracking mechanisms in the deposit and heat-affected zones (HAZs). The various crack formation mechanisms, such as solidification cracking and liquation cracking, were evaluated using multiscale characterization and numerical simulation. The cracking in the deposit region was predominantly solidification cracking, while those observed in the HAZ were liquation cracking. The results showed that controlling thermally induced residual stresses is the key to eliminating cracking, and the optimum preheat temperature was determined. In conclusion, the results were then contrasted with those in published literature and an approach to effectively repair hot section parts was presented.

36 MATERIALS SCIENCE↗