NASA NTRS2019

TUFROC Thermal Protection System

Toughened Unipiece Fibrous Reinforced Oxidation-resistant Composite (TUFROC) is a tiled Thermal Protection System (TPS) suitable for reusable entry heating at 2900+ °F and with single use potential up to at least 3600 °F. TUFROC was initially developed for NASA's X-37 project and ultimately resulted in use on the Air Force X-37B as the wing leading edge (WLE) of the vehicle. TUFROC has similar high temperature capability compared with carbon/carbon, but is manufactured at an order of magnitude lower cost & faster schedule.

thermal protection system↗

NASA NTRS2007

Lightweight Thermal Protection System for Atmospheric Entry

TUFROC (Toughened Uni-piece Fibrous Reinforced Oxidation-resistant Composite) has been developed as a new thermal protection system (TPS) material for wing leading edge and nose cap applications. The composite withstands temperatures up to 1,970 K, and consists of a toughened, high-temperature surface cap and a low-thermal-conductivity base, and is applicable to both sharp and blunt leading edge vehicles. This extends the possible application of fibrous insulation to the wing leading edge and/or nose cap on a hypersonic vehicle. The lightweight system comprises a treated carbonaceous cap composed of ROCCI (Refractory Oxidation-resistant Ceramic Carbon Insulation), which provides dimensional stability to the outer mold line, while the fibrous base material provides maximum thermal insulation for the vehicle structure.

Stewart, David↗

NASA NTRS2006

Tantalum-Based Ceramics for Refractory Composites

A family of tantalum-based ceramics has been invented as ingredients of high-temperature composite insulating tiles. These materials are suitable for coating and/or permeating the outer layers of rigid porous (foam-like or fibrous) ceramic substrates to (1) render the resulting composite ceramic tiles impervious to hot gases and (2) enable the tiles to survive high heat fluxes at temperatures that can exceed 3,000 F ( 1,600 C).

Stewart, David A.↗

NASA NTRS2003

Hot Films on Ceramic Substrates for Measuring Skin Friction

Hot-film sensors, consisting of a metallic film on an electrically nonconductive substrate, have been used to measure skin friction as far back as 1931. A hot film is maintained at an elevated temperature relative to the local flow by passing an electrical current through it. The power required to maintain the specified temperature depends on the rate at which heat is transferred to the flow. The heat transfer rate correlates to the velocity gradient at the surface, and hence, with skin friction. The hot-film skin friction measurement method is most thoroughly developed for steady-state conditions, but additional issues arise under transient conditions. Fabricating hot-film substrates using low-thermal-conductivity ceramics can offer advantages over traditional quartz or polyester-film substrates. First, a low conductivity substrate increases the fraction of heat convected away by the fluid, thus increasing sensitivity to changes in flow conditions. Furthermore, the two-part, composite nature of the substrate allows the installation of thermocouple junctions just below the hot film, which can provide an estimate of the conduction heat loss.

Noffz, Greg↗

NASA NTRS1992

Sol-gel synthesis and densification of aluminoborosilicate powders. Part 1: Synthesis

Aluminoborosilicate powders high in alumina content were synthesized by the sol-gel process utilizing various methods of preparation. Properties and microstructural effects related to these syntheses were examined. After heating to 600 C for 2 h in flowing air, the powders were amorphous with the metal oxides comprising 87 percent of the weight and uncombusted organics the remainder. DTA of dried powders revealed a T(sub g) at approximately 835 C and an exotherm near 900 C due to crystallization. Powders derived from aluminum secbutoxide consisted of particles with a mean diameter 5 microns less than those from aluminum isopropoxide. Powders synthesized with aluminum isopropoxide produced agglomerates comprised of rod shaped particulates while powders made with the secbutoxide precursor produced irregular glassy shards. Compacts formed from these powders required different loadings for equivalent densities according to the method of synthesis.

Bull, Jeffrey↗

NASA NTRS1992

Sol-gel synthesis and densification of aluminoborosilicate powders. Part 2: Densification

Aluminoborosilicate (ABS) powders, high in alumina content, were synthesized by the sol-gel process utilizing four different methods of synthesis. The effect of these methods on the densification behavior of ABS powder compacts was studied. Five regions of shrinkage in the temperature range 25-1184 C were identified. In these regions, the greatest shrinkage occurred between the gel-to-glass transition temperature (T sub g approximately equal to 835 C) and the crystallization transformation temperature (T sub t approximately equal 900 C). The dominant mechanism of densification in this range was found to be viscous sintering. ABS powders were amorphous to x-rays up to T sub t at which a multiphasic structure crystallized. No 2Al2O3.B2O3 was found in these powders as predicted in the phase diagram. Above T sub t, densification was the result of competing mechanisms including grain growth and boria fluxed viscous sintering. Apparent activation energies for densification in each region varied according to the method of synthesis.

Bull, Jeffrey↗

NASA NTRS1992

Sol-Gel Synthesis Of Aluminoborosilicate Powders

Application of sol-gel process to synthesis of aluminoborosilicate powders shows potential for control of microstructures of materials. Development of materials having enhanced processing characteristics prove advantageous in extending high-temperature endurance of fibrous refractory composite insulation made from ceramic fibers.

Bull, Jeffrey↗

NASA NTRS1992

Ceramic-Fibrous-Insulation Thermal-Protection System

New composite thermal-protection system developed in which glass-ceramic impregnated into surface of fibrous insulation. Called TUFI for toughened unipiece fibrous insulation developed as replacement for tiles with reaction-cured-glass (RCG) coating. Impregnation of glass-ceramic results in thermal protection system with insulating properties comparable to existing system but with 20 to 100 times more resistance to impact.

Leiser, Daniel↗

NASA NTRS1991

Improving the temperature performance of low-density ceramic heatshields through sol-gel processing

The performance of rigid insulations for use as thermal protection materials on reentry vehicles can be characterized by their resistance to dimensional and morphological change when exposed to an isothermal environment equivalent to that generated in entry. Improvements in these material characteristics for alumina-enhanced thermal barrier insulation by compositional modification through sol-gel processing are reported.

Bull, Jeffrey↗