NASA NTRS2005

Improved Small-Particle Powders for Plasma Spraying

Improved small-particle powders and powder-processing conditions have been developed for use in plasma spray deposition of thermal-barrier and environmental barrier coatings. Heretofore, plasma-sprayed coatings have typically ranged in thickness from 125 to 1,800 micrometers. As explained below, the improved powders make it possible to ensure complete coverage of substrates at unprecedently small thicknesses of the order of 25 micrometers. Plasma spraying involves feeding a powder into a hot, high-velocity plasma jet. The individual powder particles melt in the plasma jet as they are propelled towards a substrate, upon which they splat to build up a coating. In some cases, multiple coating layers are required. The size range of the powder particles necessarily dictates the minimum thickness of a coating layer needed to obtain uniform or complete coverage. Heretofore, powder particle sizes have typically ranged from 40 to 70 micrometers; as a result, the minimum thickness of a coating layer for complete coverage has been about 75 micrometers. In some applications, thinner coatings or thinner coating layers are desirable. In principle, one can reduce the minimum complete-coverage thickness of a layer by using smaller powder particles. However, until now, when powder particle sizes have been reduced, the powders have exhibited a tendency to cake, clogging powder feeder mechanisms and feed lines. Hence, the main problem is one of synthesizing smaller-particle powders having desirable flow properties. The problem is solved by use of a process that begins with a spray-drying subprocess to produce spherical powder particles having diameters of less than 30 micrometers. (Spherical-particle powders have the best flow properties.) The powder is then passed several times through a commercial sifter with a mesh to separate particles having diameters less than 15 micrometers. The resulting fine, flowable powder is passed through a commercial fluidized bed powder feeder into a plasma spray jet.

Nguyen, QuynhGiao, N.↗

NASA NTRS2003

Sintering and Interface Strain Tolerance of Plasma-Sprayed Thermal and Environmental Barrier Coatings

Ceramic thermal and environmental barrier coatings will be more aggressively designed to protect gas turbine engine hot section SiC/SiC Ceramic Matrix Composite (CMC) components in order to meet future engine higher fuel efficiency and lower emission goals. A coating system consisting of a zirconia-based oxide topcoat (thermal barrier) and a mullite/BSAS silicate inner coat (environmental barrier) is often considered a model system for the CMC applications. However, the coating sintering, and thermal expansion mismatch between the zirconia oxide layer and the silicate environmental barrier/CMC substrate will be of major concern at high temperature and under thermal cycling conditions. In this study, the sintering behavior of plasma-sprayed freestanding zirconia-yttria-based thermal barrier coatings and mullite (and/or barium-strontium-aluminosilicate, i.e., BSAS) environmental barrier coatings was determined using a dilatometer in the temperature range of 1200-1500 C. The effects of test temperature on the coating sintering kinetics were systematically investigated. The plasma-sprayed zirconia-8wt.%yttria and mullite (BSAS) two-layer composite coating systems were also prepared to quantitatively evaluate the interface strain tolerance of the coating system under thermal cycling conditions based on the dilatomentry. The cyclic response of the coating strain tolerance behavior and interface degradation as a function of cycle number will also be discussed.

Zhu, Dongming↗

NASA NTRS1995

A simulation technique for predicting thickness of thermal sprayed coatings

The complexity of many of the components being coated today using the thermal spray process makes the trial and error approach traditionally followed in depositing a uniform coating inadequate, thereby necessitating a more analytical approach to developing robotic trajectories. A two dimensional finite difference simulation model has been developed to predict the thickness of coatings deposited using the thermal spray process. The model couples robotic and component trajectories and thermal spraying parameters to predict coating thickness. Simulations and experimental verification were performed on a rotating disk to evaluate the predictive capabilities of the approach.

Goedjen, John G.↗

NASA NTRS1993

Characterization and durability testing of plasma-sprayed zirconia-yttria and hafnia-yttria thermal barrier coatings. Part 2: Effect of spray parameters on the performance of several hafnia-yttria and zirconia-yttria coatings

This is the second of two reports which discuss initial experiments on thermal barrier coatings prepared and tested in newly upgraded plasma spray and burner rig test facilities at LeRC. The first report, part 1, describes experiments designed to establish the spray parameters for the baseline zirconia-yttria coating. Coating quality was judged primarily by the response to burner rig exposure, together with a variety of other characterization approaches including thermal diffusivity measurements. That portion of the study showed that the performance of the baseline NASA coating was not strongly sensitive to processing parameters. In this second part of the study, new hafnia-yttria coatings were evaluated with respect to both baseline and alternate zirconia-yttria coatings. The hafnia-yttria and the alternate zirconia-yttria coatings were very sensitive to plasma-spray parameters in that high-quality coatings were obtained only when specific parameters were used. The reasons for this important observation are not understood.

Miller, Robert A.↗

NASA NTRS1993

Characterization and durability testing of plasma-sprayed zirconia-yttria and hafnia-yttria thermal barrier coatings. Part 1: Effect of spray parameters on the performance of several lots of partially stabilized zirconia-yttria powder

Initial experiments conducted on thermal barrier coatings prepared in the newly upgraded research plasma spray facility and the burner rig test facilities are discussed. Part 1 discusses experiments which establish the spray parameters for three baseline zirconia-yttria coatings. The quality of five similar coating lots was judged primarily by their response to burner rig exposure supplemented by data from other sources such as specimen characterizations and thermal diffusivity measurements. After allowing for burner rig variability, although there appears to be an optimum density (i.e., optimum microstructure) for maximum burner rig life, the distribution tends to be rather broad about the maximum. In Part 2, new hafnia-yttria-based coatings were evaluated against both baseline and alternate zirconia-yttria coatings. The hafnia-yttria coatings and the zirconia-yttria coatings that were prepared by an alternate powder vendor were very sensitive to plasma spray parameters, in that high-quality coatings were only obtained when certain parameters were employed. The reasons for this important observation are not understood. Also not understood is that the first of two replicate specimens sprayed for Part 1 consistently performed better than the second specimen. Subsequent experiments did not display this spray order affect, possibly because a chiller was installed in the torch cooling water circuit. Also, large changes in coating density were observed after switching to a new lot of electrodes. Analyses of these findings were made possible, in part, because of the development of a sensitive density measurement technique described herein in detail. The measured thermal diffusivities did not display the expected strong relationship with porosity. This surprising result was believed to have been caused by increased microcracking of the denser coatings on the stainless steel substrates.

Miller, Robert A.↗

NASA NTRS1991

Plasma Spraying Reclaims Compressor Housings

Plasma-spraying process used to build up material in worn and pitted areas. Newly applied material remachined to specified surface contours. Effective technique for addition of metal to out-of-tolerance magnesium-alloy turbine-engine compressor housings.

Leissler, George W.↗

NASA NTRS1988

T55-L-712 turbine engine compressor housing refurbishment-plasma spray project

A study was conducted to assess the feasibility of reclaiming T55-L-712 turbine engine compressor housings with an 88 wt percent aluminum to 12 wt percent silicon alloy applied by a plasma spray process. Tensile strength testing was conducted on as-sprayed and thermally cycled test specimens which were plasma sprayed with 0.020 to 0.100 in. coating thicknesses. Satisfactory tensile strength values were observed in the as-sprayed tensile specimens. There was essentially no decrease in tensile strength after thermally cycling the tensile specimens. Furthermore, compressor housings were plasma sprayed and thermally cycled in a 150-hr engine test and a 200-hr actual flight test during which the turbine engine was operated at a variety of loads, speeds and torques. The plasma sprayed coating system showed no evidence of degradation or delamination from the compressor housings. As a result of these tests, a procedure was designed and developed for the application of an aluminum-silicon alloy in order to reclaim T55-L-712 turbine engine compressor housings.

Leissler, George W.↗

NASA NTRS1988

Metal/Ceramic Bond Coatings For High Temperatures

Reduced-thermal-expansion bond coatings developed for use at high temperatures in thermal-barrier-coating systems. Bond coatings composed of low-pressure-plasma-sprayed metallic matrices dispersed with low-thermal-expansion high-bulk-modulus ceramic particles. New coatings and application lower thermal-expansion-mismatch strain while maintaining integrity at high temperatures.

Miller, Robert A.↗

NASA NTRS1988

Wear-Resistant, Thermally Conductive Coating

Process makes coating with unusual properties. Coating is copper or copper alloy with controlled dispersion of oxide or carbide particles. Process results in coating that has thermal expansion similar to base material, increased resistance to abrasion when hot, and high thermal conductivity. Coatings resistant to wear used in variety of applications ranging from earth-moving equipment to space vehicles.

Edmonds, Brian J.↗

NASA NTRS1988

Plasma Spraying Of Dense, Rough Bond Coats

Simple modification of plasma torch facilitates spraying of coarse powders. Shape of nozzle changed to obtain decrease in velocity of gas and consequent increase in time particles spend in flame before impact on substrate. Increased residence time allows melting of coarser powders, spraying of which results in rougher bond surfaces.

Miller, Robert A.↗

NASA NTRS1987

The T55-L-712 turbine engine compressor housing refurbishment project

A study was conducted to access the feasibility of reclaiming T55-L-712 turbine engine compressor housings with an 88 wt % aluminum -- 12 wt % silicon alloy applied by the plasma spray processes. Tensile strength testing was conducted on as-sprayed and thermally cycled test specimens which were plasma sprayed from 0.020 to 0.100 in. Satisfactory tensile strength valves were observed in the as-sprayed tensile specimens. There was essentially no decrease in tensile strength after thermally cycling the tensile specimens.

Leissler, George W.↗