4 records

DOE OSTI2024

Uniaxial compressive creep tests by spark plasma sintering of 70% theoretical density α -uranium and U-10Zr

Metallic fuels hold numerous advantages over conventional uranium dioxide fuels and are a key component of several liquid metal-cooled advanced reactor concepts including sodium fast reactors. These fuels undergo rapid swelling during early burnup; consequently, they spend most of their reactor lifetime in a porous state. The presence of this porosity alters many of the mechanical properties of the fuel including creep impacting fuel deformation during axial swelling. This work investigates the creep behavior of the porous fuel using a spark plasma sintering technique. Creep tests were performed for the first time on porous α-phase uranium and uranium with 10 wt. % zirconium (U-10Zr) samples. The samples of α-phase uranium and U-10Zr were fabricated from depleted uranium by spark plasma sintering and subjected to uniaxial compressive creep testing. Calculated stress exponents were found to be 2.6±1.6 and 5.7±1.4 for α-U and U-10Zr, respectively, and calculated activation energies were found to be 61.6±1.1kJ/mol for α-U. The creep data were also used to evaluate existing porosity inclusive in creep models.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2024

Manufacturing porous U-10Zr metallic fuels with controllable microstructure by volume control spark plasma sintering

In this paper, the volume control spark plasma sintering tool has been designed and applied to sinter porous U-10Zr metallic fuels, by which the sintered sample volume can be precisely controlled. Ethanol and NH 4 HCO 3 are used to control the powder compact or as pore formers to control the pore size and pore structure. Without pore formers, the fuel pellet displays an inhomogeneous microstructure consisting of highly porous and highly densified areas. Uneven powder stacking in the green body results in a non-uniform microstructure, and in the closed-packed area, Joule heating accelerates the neck formation and densification. The addition of ethanol reduces the friction between the powders, resulting in isolated pores formed by the stacking of powders during the sintering. By adding NH 4 HCO 3 , the pore size, and structure can be well controlled, and an interconnected pore structure can be obtained upon the decomposition of the NH 4 HCO 3 . Further, a uniform microstructure and pore distributions can be achieved through the U-10Zr fuel pellets by controlling current flow during the volume control SPS sintering. The microstructure and phase characterization of the sintered porous U-10Zr pellets show major phases of α-U and α-Zr for the sample with short dwelling. For the sample with long dwelling (30 min), the ω UZr 2 in the Zr-enriched area has been observed. The strategy of volume control SPS sintering with the assistance of pore formers could be used to fabricate porous U-10Zr metallic fuels to mimic the microstructure evolution of irradiated metallic fuels (including porosity) and could enable a possible solution for the design of new sodium-free metallic fuels for high burnup.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

Results of Oklo Diffusion Couple Experiments

Through the Gateway for Accelerated Innovation in Nuclear (GAIN) initiative, the U.S. Department of Energy funded a GAIN Nuclear Energy Voucher to perform out-of-pile experiments related to the fuel design for Oklo Inc., headquartered in Santa Clara, CA. GAIN’s goal is to accelerate the innovation and application of advanced nuclear technologies, and voucher recipients do not receive direct financial awards but are provided access to national laboratory capabilities at no cost. This report documents the results of diffusion couple experiments performed as part of the GAIN-funded project for Oklo. This work addresses the specific problem of filling the gap in understanding of the fuel-cladding chemical interaction (FCCI) that result from the past focus on a particular fuel design. These knowledge and mechanistic modeling gaps make it difficult to extrapolate from prior fuel performance data to advance an economically competitive fuel design. Specifically, the current state-of-the-art fuel performance modeling cannot separate the entangled effects of temperature ranges, burnups, materials, and geometries.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

Mechanical and Thermophysical properties of low enriched uranium-10wt% molybdenum rolled foils

In this study, low-enriched (~19.75% 235 U) U-10Mo(wt%) foils were evaluated for both mechanical and thermophysical properties to establish baseline characteristics prior to irradiation testing. Cast U-10Mo ingots were sequentially hot and cold rolled to two different final foil thicknesses, resulting in different levels of cold work being present in the finished foils. The mechanical response of the U-10Mo foils was evaluated in the temperature range of 293–623 K. Increasing test temperatures resulted in decreases of both yield and ultimate tensile strength. Comparison of results to earlier work performed on depleted U-10Mo rolled foils indicates that the material in this study has lower strength and increased ductility. However, a comparison of the two different foil thicknesses in this study found that they were nearly identical in yield and ultimate tensile strength, differing by only 10–20 MPa (<2%). Thermal conductivity was calculated from the measurements of specific heat, linear thermal expansion, and thermal diffusivity from 323 to 1273 K on both thicknesses of the foils. These data were approximately 5–10% lower than previously published data above 573 K and were similar to data for temperature ranges below 573 K. Differences are likely related to differences in grain size and/or impurity content and variation in fabrication history.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗