Multi-scale stabilization of high-voltage LiCoO 2 enabled by nanoscale solid electrolyte coating
LiCoO 2 (LCO) possess a high theoretical specific capacity of 274 mAh g -1 , and currently LCO charged to 4.48 V with a capacity of ~190–195 mAh g -1 is penetrating the commercial markets. Scalable strategies to further enhance the performance of LCO are highly attractive. Here, we develop a scalable ball-milling and sintering method to tackle this long-standing challenge by modifying LCO surface with only 1.5–3.5% ceramic solid electrolyte nanoparticles, specifically Li 1.5 Al 0.5 Ge 1.5 (PO 4 ) 3 (LAGP) as an example. Consequently, the atomic-to-meso multiscale structural stabilities have been significantly improved, even with a high cut-off voltage of 4.5 V vs. Li/Li + , leading to excellent electrochemical stabilities. The nano-LAGP modified Li|LCO cell exhibits high discharge capacity of 196 mAh g -1 at 0.1 C, capacity retention of 88% over 400 cycles, and remarkably enhanced rate capability (163 mAh g -1 at 6 C). These results show significant improvement compared to the Li|LCO cells. The as-prepared graphite|LAGP-LCO full cells also show steady cycling with 80.4% capacity retention after 200 cycles with a voltage cut-off of 4.45 V. This work provides a simple and scalable approach to achieve stable cycling of LCO at high voltage with high energy density.
Interfacial engineering for stabilizing polymer electrolytes with 4V cathodes in lithium metal batteries at elevated temperature
Poly (ethylene oxide) (PEO) polymer electrolytes are promising candidates for next-generation rechargeable lithium batteries. However, the poor interfacial stability between 4 V cathodes and PEO electrolytes impedes their applications in 4 V lithium batteries with high energy density. Here, we demonstrate a facile and effective strategy to enhance the interfacial stability by the synergy of Li 1.5 Al 0.5 Ge 1.5 (PO 4 ) 3 (LAGP) coating on the cathode surface, and salt combination in the electrolyte, even with a cut-off voltage of 4.25–4.4 V vs. Li + /Li. Nano-LAGP coated Li|PEO|LiCoO 2 cell delivers stable cycling with a capacity retention of 81.9%/400 cycles and 84.7%/200 cycles at 60 °C when charged to 4.25 and 4.3 V in pure polyether electrolyte, respectively. Steady cycling is also demonstrated at room temperature and with LiNi 0.5 Co 0.2 Mn 0.3 O 2 (NCM523) cathode. This work offers a viable and scalable approach to improve the stability between PEO electrolytes and 4 V cathodes and open up new possibilities for practical application of 4 V lithium metal batteries.