DOE OSTI2024

A redox-reversible A/B-site co-doped BaFeO 3 electrode for direct hydrocarbon solid oxide fuel cells

Solid oxide fuel cells (SOFCs) can directly convert the chemical energy in fuel to electrical energy with fuel flexibility; however, the conventional nickel-based anodes face great challenges due to coking upon direct oxidation of hydrocarbon fuels and redox instability. Thus, developing new anode materials which can provide high coking resistance as well as redox stability is crucial. In this work, Ba 0.6 La 0.4 Fe 0.8 Mo 0.1 Ni 0.1 O 3-δ (BLFMN) has been synthesized in air using a sol–gel combustion method, resulting in a dual phase consisting of a cubic BLFMN main phase and scheelite BaMoO 4 (BMO 4 ) secondary phase. By heat-treating the BLFMN dual phase in H 2 at 800 °C for 5 h, a metallic nanoparticle-decorated BLFMN triple phase compound comprising cubic BLFMN, cubic BaMoO 3 (BMO 3 ) and in situ exsolved FeNi 3 alloy was obtained. BLFMN was subsequently investigated as an electrode material for La 0.8 Sr 0.2 Ga 0.83 Mg 0.17 O 3-δ (LSGM) electrolyte (300 μm) supported SOFCs. Symmetrical cells using BLFMN as electrodes with the cell configuration of BLFMN//LSGM//BLFMN showed excellent redox reversibility and a peak power density (PPD) of 1.32 W cm -2 at 850 °C when using H 2 as fuel. Single cell with the cell configuration of BLFMN//LSGM//LSCF (La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3-δ ) reached PPD of 1.61 and 0.41 W cm -2 at 850 °C when operating with H 2 and CH 4 fuel, respectively. Moreover, the single cell exhibit excellent stability (over 300 h) upon direct oxidation of hydrocarbon fuels of CH 4 and C 3 H 8 . This study indicates that BLFMN is a promising redox reversible and coking resistant anode for SOFCs.

08 HYDROGEN↗

DOE OSTI2024

Enhancing Direct Electrochemical CO 2 Electrolysis by Introducing A-Site Deficiency for the Dual-Phase Pr(Ca)Fe(Ni)O 3-δ Cathode

High-temperature CO 2 electrolysis via solid oxide electrolysis cells (CO 2 –SOECs) has drawn special attention due to the high energy convention efficiency, fast electrode kinetics, and great potential in carbon cycling. However, the development of cathode materials with high catalytic activity and chemical stability for pure CO 2 electrolysis is still a great challenge. In this work, A-site cation deficient dual-phase material, namely (Pr 0.4 Ca 0.6 ) x Fe 0.8 Ni 0.2 O 3-δ (PCFN, x = 1, 0.95, and 0.9), has been designed as the fuel electrode for a pure CO 2 –SOEC, which presents superior electrochemical performance. Among all these compositions, (Pr 0.4 Ca 0.6 ) 0.95 Fe 0.8 Ni 0.2 O 3-δ (PCFN95) exhibited the lowest polarization resistance of 0.458 Ω cm 2 at open-circuit voltage and 800 °C. The application of PCFN95 as the cathode in a single cell yields an impressive electrolysis current density of 1.76 A cm -2 at 1.5 V and 800 °C, which is 76% higher than that of single cells with stoichiometric Pr 0.4 Ca 0.6 Fe 0.8 Ni 0.2 O 3-δ (PCFN100) cathode. The effects of A-site deficiency on materials' phase structure and physicochemical properties are also systematically investigated. Such an enhancement in electrochemical performance is attributed to the promotion of effective CO 2 adsorption, as well as the improved electrode kinetics resulting from the A-site deficiency.

30 DIRECT ENERGY CONVERSION↗

DOE OSTI2023

Unlocking the Potential of A-Site Ca-Doped LaCo 0.2 Fe 0.8 O 3-δ : A Redox-Stable Cathode Material Enabling High Current Density in Direct CO 2 Electrolysis

Massive carbon dioxide (CO 2 ) emission from recent human industrialization has affected the global ecosystem and raised great concern for environmental sustainability. The solid oxide electrolysis cell (SOEC) is a promising energy conversion device capable of efficiently converting CO 2 into valuable chemicals using renewable energy sources. However, Sr-containing cathode materials face the challenge of Sr carbonation during CO 2 electrolysis, which greatly affects the energy conversion efficiency and long-term stability. Thus, A-site Ca-doped La1– x CaxCo 0.2 Fe 0.8 O 3-δ (0.2 ≤ x ≤ 0.6) oxides are developed for direct CO 2 conversion to carbon monoxide (CO) in an intermediate-temperature SOEC (IT-SOEC). With a polarization resistance as low as 0.18 O cm 2 in pure CO 2 atmosphere, a remarkable current density of 2.24 A cm –2 was achieved at 1.5 V with La 0.6 Ca 0.4 Co 0.2 Fe 0.8 O 3-δ (LCCF64) as the cathode in La 0.8 Sr 0.2 Ga 0.83 Mg 0.17 O 3-δ (LSGM) electrolyte (300 µm) supported electrolysis cells using La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3-δ (LSCF) as the air electrode at 800 °C. Furthermore, symmetrical cells with LCCF64 as the electrodes also show promising electrolysis performance of 1.78 A cm –2 at 1.5 V at 800 °C. In addition, stable cell performance has been achieved on direct CO 2 electrolysis at an applied constant current of 0.5 A cm –2 at 800 °C. The easily removable carbonate intermediate produced during direct CO 2 electrolysis makes LCCF64 a promising regenerable cathode. The outstanding electrocatalytic performance of the LCCF64 cathode is ascribed to the highly active and stable metal/perovskite interfaces that resulted from the in situ exsolved Co/CoFe nanoparticles and the additional oxygen vacancies originated from the Ca 2 Fe 2 O 5 phase synergistically providing active sites for CO 2 adsorption and electrolysis. Here this study offers a novel approach to design catalysts with high performance for direct CO 2 electrolysis.

30 DIRECT ENERGY CONVERSION↗

DOE OSTI2023

High-performance Ruddlesden–Popper perovskite oxide with in situ exsolved nanoparticles for direct CO 2 electrolysis

Carbon dioxide (CO 2 ) is one of the principal greenhouse gases accountable for global warming and extreme climate changes. Electrochemically converting CO 2 into carbon monoxide (CO) is a promising approach for CO 2 utilization in achieving industrial decarbonization. High-temperature CO 2 electrolysis via solid oxide electrolysis cells (SOECs) has great potential, including high-energy efficiency, fast electrode kinetics, and competitive cost; however, this technology still has challenges associated with developing highly active, robust CO 2 electrodes for SOECs. We report novel Ruddlesden–Popper structured Pr 1.2 Sr 0.8 Mn 0.4 Fe 0.6 O 4–δ (RP-PSMF) with in situ exsolved Fe nanoparticles as the CO 2 electrode in SOECs for direct CO 2 conversion to CO. The mechanism of CO 2 electrolysis is studied by using the distribution of relaxation times method from electrochemical impedance spectroscopy. La 0.8 Sr 0.2 Ga 0.8 Mg 0.2 O 3–δ (LSGM)-electrolyte supported SOECs with the RP-PSMF cathode have achieved exceptionally high current densities of 2.90, 1.61, 0.91, and 0.48 A·cm –2 at an applied voltage of 1.5 V at 800, 750, 700, and 650 °C, respectively. Moreover, SOECs with the RP-PSMF cathode have exhibited a stable electrolysis performance for 100 h under a current cycling operation. Here, these results suggest that RP-PSMF with exsolved Fe nanoparticles is a highly promising cathode for high-temperature direct CO 2 electrolysis cells.

03 NATURAL GAS↗

DOE OSTI2023

Improved Solid-State Reaction Method for Scaled-Up Synthesis of Ceramic Proton-Conducting Electrolyte Materials

Protonic ceramic electrochemical cells (PCECs) represent promising technologies in the production of clean electricity, decarbonized hydrogen, chemicals, and fuels at intermediate temperatures. One of the challenges in commercializing PCECs is to produce the electrolyte materials on a large scale. The conventional solid-state reaction (SSR) method suffers from tedious synthesis procedures and low phase purity of the products due to the formation of unwanted secondary phases. Herein, we report an improved SSR (i-SSR) method for kilogram-scale production of high phase-purity electrolyte material BaZr 0.4 Ce 0.4 Y 0.1 Yb 0.1 O 3–δ (BZCYYb4411). In this method, the ball-milled precursor powders are pelletized prior to calcination, which effectively reduces the length of the diffusion paths between the components during perovskite phase formation. In this study, the synthesis procedure and calcination temperature are carefully optimized for efficient and repeatable production based on the powder crystallization behavior. A combined technoeconomic analysis and life cycle assessment modeling suggest that the i-SSR method could reduce the total production cost and greenhouse gas emissions by up to 19% and 39%, respectively, compared to the conventional SSR method. The high quality of the synthesized electrolyte material is corroborated by the excellent electrical conductivity and electrochemical performance of the fabricated PCEC cells.

36 MATERIALS SCIENCE↗

DOE OSTI2023

La- and Mn-doped cobalt spinel oxygen evolution catalyst for proton exchange membrane electrolysis

Discovery of earth-abundant electrocatalysts to replace iridium for the oxygen evolution reaction (OER) in a proton exchange membrane water electrolyzer (PEMWE) represents a critical step in reducing the cost for green hydrogen production. Here we report a nanofibrous cobalt spinel catalyst codoped with lanthanum (La) and manganese (Mn) prepared from a zeolitic imidazolate framework embedded in electrospun polymer fiber. The catalyst demonstrated a low overpotential of 353 millivolts at 10 milliamperes per square centimeter and a low degradation for OER over 360 hours in acidic electrolyte. A PEMWE containing this catalyst at the anode demonstrated a current density of 2000 milliamperes per square centimeter at 2.47 volts (Nafion 115 membrane) or 4000 milliamperes per square centimeter at 3.00 volts (Nafion 212 membrane) and low degradation in an accelerated stress test.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Improving the performance for direct electrolysis of CO 2 in solid oxide electrolysis cells with a Sr 1.9 Fe 1.5 Mo 0.5 O 6– δ electrode via infiltration of Pr 6 O 11 nanoparticles

Direct CO 2 electrolysis using solid oxide electrolysis cells (CO 2 -SOECs) holds promise to efficiently convert carbon dioxide to carbon monoxide and oxygen. Cathodes with desirable catalytic activity and chemical stability play a critical role in the development of direct CO 2 -SOECs. Although Sr 2 Fe 1.5 Mo 0.5 O 6–δ (SFM) has exhibited promise for direct CO 2 -SOECs due to its redox stability, it suffers from insufficient activity for the CO 2 reduction reaction (CO 2 RR). Here we report interface engineering of nanosized Pr 6 O 11 on the SFM cathode obtained through infiltration to promote the CO 2 RR performance for direct CO 2 -SOECs. The effect of Pr 6 O 11 loading on the performance of the CO 2 RR is systematically investigated. At 800 °C, the current density of the Pr 6 O 11 infiltrated SFM cathode with an optimum Pr 6 O 11 loading of 14.8 wt% reaches 1.61 A cm –2 at 1.5 V, more than double that of the SFM cathode (0.76 A cm –2 ) under the same operating conditions. X-ray photoelectron spectroscopy (XPS) characterization and in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) analysis indicate that the adsorption ability of CO 2 on the SFM cathode has been significantly improved by the formation of Pr 6 O 11 . Temperature-programmed desorption (TPD) of CO 2 measurements further manifest that a 14.8 wt% Pr 6 O 11 -SFM cathode has better CO desorption capacity. In addition, polarization resistance of the SFM cathode has significantly decreased with the addition of Pr 6 O 11 . Three-electrode measurement was used to analyze the improved electrode kinetics. Finally, these results demonstrate that the formation of Pr 6 O 11 in the SFM cathode through infiltration is a promising approach for increasing CO 2 RR activity for CO 2 -SOECs.

03 NATURAL GAS↗

DOE OSTI2023

Improved cell performance and sulphur tolerance using A-site substituted Sr2Fe1.4Ni0.1Mo0.5O6–δ anodes for solid-oxide fuel cells

Abstract Solid-oxide fuel cells (SOFCs) offer great promise for producing electricity using a wide variety of fuels such as natural gas, coal gas and gasified carbonaceous solids; however, conventional nickel-based anodes face great challenges due to contaminants in readily available fuels, especially sulphur-containing compounds. Thus, the development of new anode materials that can suppress sulphur poisoning is crucial to the realization of fuel-flexible and cost-effective SOFCs. In this work, La0.1Sr1.9Fe1.4Ni0.1Mo0.5O6–δ (LSFNM) and Pr0.1Sr1.9Fe1.4Ni0.1Mo0.5O6–δ (PSFNM) materials have been synthesized using a sol-gel method in air and investigated as anode materials for SOFCs. Metallic nanoparticle-decorated ceramic anodes were obtained by the reduction of LSFNM and PSFNM in H2 at 850°C, forming a Ruddlesden–Popper oxide with exsolved FeNi3 bimetallic nanoparticles. The electrochemical performance of the Sr2Fe1.4Ni0.1Mo0.5O6–δ ceramic anode was greatly enhanced by La doping of A-sites, resulting in a 44% decrease in the polarization resistance in reducing atmosphere. The maximum power densities of Sr- and Mg-doped LaGaO3 (LSGM) (300 μm) electrolyte-supported single cells with LSFNM as the anode reached 1.371 W cm −2 in H2 and 1.306 W cm–2 in 50 ppm H2S–H2 at 850°C. Meanwhile, PSFNM showed improved sulphur tolerance, which could be fully recovered after six cycles from H2 to 50 ppm H2S–H2 operation. This study indicates that LSFNM and PSFNM are promising high-performance anodes for SOFCs.

Li, Haixia↗

DOE OSTI2022

Nanostructured carbon as highly efficient and stable anodes for ethylene production and power generation in protonic ceramic electrochemical cells

Protonic ceramic electrochemical cells (PCECs) have the potential in reducing the energy input and carbon emissions in ethylene production from ethane dehydrogenation. The performance of conventional perovskite-based anode materials for ethane conversion in PCECs is limited by their low active surface area and proneness to coke deposition. In this work, for the first time, we demonstrate the use of aligned carbon nanotube forests (CNTFs) as a novel anode material for an ethane fueled PCEC to co-produce ethylene and electricity. The CNTF electrode was grown on the electrolyte by the chemical vapor deposition (CVD) method. Highly dispersed iron carbide nanoparticles are formed in situ on the CNTFs during the CVD process, acting as highly active catalysts for ethane dehydrogenation. The novel PCECs show superior catalytic and electrochemical performances to that using conventional perovskite-based anodes. The cell also exhibits excellent durability and anti-coking abilities within 100 h test. This work showcases the promising application of nanostructured carbon, a new class of non-perovskite materials, as the multifunctional electrode materials for PCECs.

03 NATURAL GAS↗

DOE OSTI2022

Atmospheric plasma spraying to fabricate metal‐supported solid oxide fuel cells with open‐channel porous metal support

Abstract Metal‐supported solid oxide fuel cells (MS‐SOFCs) have been fabricated by applying phase‐inversion tape‐casting and atmospheric plasma spraying (APS). The effect of the binder amount of the phase‐inversion slurries on the microstructure development of the 430L stainless steel metal support was investigated. The pore structures, the viscosity of the slurry, porosity and permeability of the as‐prepared metal supports are significantly influenced by the amount of the binder. NiO–scandia‐stabilized zirconia (ScSZ) anode, ScSZ electrolyte and La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3−δ (LSCF) cathode layers were consecutively deposited on the metal support with an ideal microstructure by APS process. The effect of plasma power of the APS on the microstructure of the electrolyte and cathode was investigated. A dense electrolyte layer and a porous cathode layer were successfully obtained at 40 and 6 kW of the APS plasma power, respectively. MS‐SOFCs, with a cell configuration of 430L/Ni‐ScSZ/ScSZ/LSCF, achieved a maximum cell power density of 1079 mW cm −2 at 700°C using humidified H 2 as fuel and ambient air as oxidant. The corresponding ohmic resistance and total resistance of MS‐SOFCs was 0.14 and 0.32 Ω cm 2 , respectively. This work demonstrates the feasibility of fabricating high‐performance MS‐SOFCs with economical and scalable techniques.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Controlling P–C/C–H Bond Cleavage in Nickel Bis(diphosphine) Complexes: Reactivity Scope, Mechanism, and Computations

The synthesis of heteroleptic [Ni(P 2 N 2 )(diphosphine)][BF 4 ] 2 complexes and the cleavage of P–C and C–H bonds of the P 2 N 2 ligand in those complexes are reported here. The products are five-coordinate complexes in which Ni–C and P–H bonds have formed to give a cyclic moiety containing Ni–CH$=$NR 2 . The reactivity of [Ni(P 2 N 2 )(diphosphine)][BF 4 ] 2 complexes is influenced by the rigidity of the diphosphine, the steric effect of the substituents, and length of the carbon linker of the diphosphine ligands. Diphosphine ligands bearing a rigid backbone (e.g., dmpbz, 1,2-bis(dimethylphosphino)benzene) or aromatic substituents (e.g., dppe, 1,2-bis(diphenylphosphino)ethane) react with [Ni(P t Bu 2 N Bn 2 )(CH 3 CN) 2 ][BF 4 ] 2 to give P–C/C–H bond cleavage products. Both [Ni(P t Bu 2 N Bn 2 )(dmpe)(MeCN)][BF 4 ] 2 and [Ni(P t Bu 2 N Bn 2 )(dmpm)(MeCN)][BF 4 ] 2 (dmpm = 1,2-bis(dimethylylphosphino)methane) were prepared by the reaction of [Ni(P t Bu 2 N Bn 2 )(CH 3 CN) 2 ][BF 4 ] 2 with the corresponding diphosphine ligands. [Ni(P t Bu 2 N Bn 2 )(dmpe)(MeCN)][BF 4 ] 2 readily undergoes P–C/C–H bond cleavage in nitromethane. In sharp contrast, [Ni(P t Bu 2 N Bn 2 )(dmpm)][BF 4 ] 2 is stabilized by dmpm, a diphosphine with small bite angle, and does not show P–C/C–H bond cleavage reactivity. Computational results show that for complexes bearing less bulky diphosphine ligands, such as dmpm, the barriers for the rate-determining transition states are in some examples higher than 30 kcal/mol with the M06 functional, higher than those for complexes bearing more rigid or more bulky ligands, consistent with experimental studies. The calculated barriers for the first transition state correlated with increased values of the dihedral angle formed by the two NiP 2 planes.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗