DOE OSTI2024

Barrier reinforcement for enhanced perovskite solar cell stability under reverse bias

Stability of perovskite solar cells (PSCs) under light, heat, humidity and their combinations have been notably improved recently. However, PSCs have poor reverse-bias stability that limits their real-world application. Here we report a systematic study on the degradation mechanisms of p-i-n structure PSCs under reverse bias. The oxidation of iodide by injected holes at the cathode side initialize the reverse-bias-induced degradation, then the generated neutral iodine oxidizes metal electrode such as copper, followed by drift of Cu+ into perovskites and its reduction by injected electrons, resulting in localized metallic filaments and thus device breakdown. A reinforced barrier with combined lithium fluoride, tin oxide and indium tin oxide at the cathode side reduces device dark current and avoids the corrosion of Cu0. It dramatically increases breakdown voltage to above -20 V and improved the T90 lifetime of PSCs to ~1,000 h under -1.6 V. The modified minimodule also maintained over 90% of its initial performance after 720 h of shadow tests.

degradation mechanisms↗

DOE OSTI2024

Iodide manipulation using zinc additives for efficient perovskite solar minimodules

Abstract Interstitial iodides are the most critical type of defects in perovskite solar cells that limits efficiency and stability. They can be generated during solution, film, and device processing, further accelerating degradation. Herein, we find that introducing a small amount of a zinc salt- zinc trifluoromethane sulfonate (Zn(OOSCF 3 ) 2 ) in the perovskite solution can control the iodide defects in resultant perovskites ink and films. CF 3 SOO ̶ vigorously suppresses molecular iodine formation in the perovskites by reducing it to iodide. At the same time, zinc cations can precipitate excess iodide by forming a Zn-Amine complex so that the iodide interstitials in the resultant perovskite films can be suppressed. The perovskite films using these additives show improved photoluminescence quantum efficiency and reduce deep trap density, despite zinc cations reducing the perovskite grain size and iodide interstitials. The zinc additives facilitate the formation of more uniform perovskite films on large-area substrates (78-108 cm 2 ) in the blade-coating process. Fabricated minimodules show power conversion efficiencies of 19.60% and 19.21% with aperture areas of 84 and 108 cm 2 , respectively, as certified by National Renewable Energy Laboratory (NREL), the highest efficiency certified for minimodules of these sizes.

14 SOLAR ENERGY↗

DOE OSTI2024

Light-enhanced oxygen degradation of MAPbBr 3 single crystal

Organometal halide perovskites are promising materials for optoelectronic applications, whose commercial realization depends critically on their stability under multiple environmental factors. In this study, a methylammonium lead bromide (MAPbBr 3 ) single crystal was cleaved and exposed to simultaneous oxygen and light illumination under ultrahigh vacuum (UHV). The exposure process was monitored using X-ray photoelectron spectroscopy (XPS) with precise control of the exposure time and oxygen pressure. It was found that the combination of oxygen and light accelerated the degradation of MAPbBr 3 , which could not be viewed as a simple addition of that by oxygen-only and light-only exposures. The XPS spectra showed significant loss of carbon, bromine, and nitrogen at an oxygen exposure of 10 10 Langmuir with light illumination, approximately 17 times of the additive effects of oxygen-only and light-only exposures. It was also found that the photoluminescence (PL) emission was much weakened by oxygen and light co-exposure, while previous reports had shown that PL was substantially enhanced by oxygen-only exposure. Measurements using a scanning electron microscope (SEM) and focused ion beam (FIB) demonstrated that the crystal surface was much roughened by the co-exposure. Furthermore, Density functional theory (DFT) calculations revealed the formation of superoxide and oxygen induced gap state, suggesting the creation of oxygen radicals by light illumination as a possible microscopic driving force for enhanced degradation.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2023

Enhancing Photostability of Sn-Pb Perovskite Solar Cells by an Alkylammonium Pseudo-Halogen Additive

High-performance tin-lead perovskite solar cells (PSCs) are needed for all-perovskite-tandem solar cells. However, iodide related fast photodegradation severely limits the operational stability of Sn-Pb perovskites despite the demonstrated high efficiency and thermal stability. Herein, this work employs an alkylammonium pseudo-halogen additive to enhance the power conversion efficiency (PCE) and photostability of methylammonium (MA)-free, Sn-Pb PSCs. Density functional theory (DFT) calculations reveal that the pseudo-halogen tetrafluoroborate (BF 4 - ) has strong binding capacity with metal ions (Sn 2+ /Pb 2+ ) in the Sn-Pb perovskite lattice, which lowers iodine vacancy formation. Upon combining BF 4 - with an octylammonium (OA + ) cation, the PCE of the device with a built-in light-scattering layer is boosted to 23.7%, which represents a new record for Sn-Pb PSCs. The improved efficiency benefits from the suppressed defect density. Under continuous 1 sun illumination, the OABF 4 embodied PSCs show slower generation of interstitial iodides and iodine, which greatly improves the device photostability under open-circuit condition. Moreover, the device based on OABF 4 retains 88% of the initial PCE for 1000 h under the maximum-power-point tracking (MPPT) without cooling.

14 SOLAR ENERGY↗