Fatigue crack propagation in fine-grained magnesium under low temperature tension-tension cyclic loading
Not Available
Geometrically Necessary Dislocation Analysis of Deformation Mechanism for Magnesium under Fatigue Loading at 0 °C
This study focused on the analysis of geometrically necessary dislocation (GND) densities for five selected fine-grained magnesium samples. Among the samples, three were tested under different fatigue-loading conditions at 0 °C, one experienced quasi-static tensile loading at 0 °C, and one represented the as-rolled state. The fatigue-tested samples were chosen according to the relationship between the maximum loading stress of a test and the material’s yield strength. This study provides new insights on the deformation mechanism of fine-grained magnesium at 0 °C. It is observed that the average GND densities were increased by 95~111% for the tested samples when compared with the as-rolled sample. It is especially interesting that there is a significant increase in the average GND density for the sample that experienced the fatigue loading with a low-maximum applied stress, and the maximum applied stress was lower than the material’s yield strength. This observation implies that the grain boundary mediated the dislocation-emission mechanism.
Microhardness Distribution of Long Magnesium Block Processed through Powder Metallurgy
Powder metallurgy is a popular method of making raw powders into specific shaped samples. However, the pressure distribution and the microhardness difference within the sample are nonnegligible and unclear when the sample is long or exceeds a specific size. In this study, the long magnesium blocks, with a ratio of about 2.8 between the sample height and the sample side length, are successfully synthesized under three uniaxial and two biaxial conditions. Then, the sample hardness values on the outer surface and the center plane are tested to study the microhardness distribution. The modified analytical expression indicates that the normal pressure exponentially decreases along the compression direction, which is consistent with the hardness distribution trend. Because higher pressure leads to a more compact arrangement of the powders, more metal bonds are formed after sintering. During the first pressing, the sidewall pressure makes the surface hardness higher. The secondary reverse compression mainly improves the bottom and core hardness due to the re-orientation and re-location of the powders. The obtained relationship between the applied pressure and the hardness distribution is instructive in predicting and improving the sample quality.
Microstructural analysis of fine-grained magnesium after cyclic tension–tension fatigue testing at 0 °C
Not Available
Study of growth twins produced through heat treatment of fine-grained magnesium
This study investigated the microstructural features of magnesium after the fine-grained magnesium sample was heat treated at 400 °C for 2 h. Both fine-grained and heat-treated magnesium samples were observed using the electron backscatter diffraction technique in scanning electron microscopy. The results show that the grains were substantially coarsened, the local strain and the local misorientation was significantly reduced, and a large number of twins were observed in the heat-treated magnesium sample. The misorientation angle analysis determined that the twins were oriented about 86.3° away from the orientation of their corresponding matrices, and the twins were the variants of $\{1 0 \bar{1} 2\}$ tensile twins. The relative orientation analysis also identified that the fast growth directions of the twins were closely along the $<2 \bar{1} \bar{1} 0>$ or $<1 0 \bar{1} 0>$ directions in the basal plane. The twins can merge or impinge onto each other. Most boundaries between the twins have the misorientation angle of about 7.4°.
Fatigue behavior of fine-grained magnesium under tension-tension loading at 0 °C
Here, this study investigated low-temperature fatigue behavior of fine-grained magnesium through tension–tension fatigue testing at the temperature of 0 °C. The applied stress profiles of fatigue testing were selected to cover a wide range of loading conditions including low, medium, and high loading stresses. Even when the maximum applied stress of fatigue testing was as high as 88% of the ultimate tensile strength of the material, the corresponding fatigue life was long, i.e., 3973 cycles. Deformation accumulation per loading cycle reduced with the progression of fatigue testing for all studied loading conditions. Fatigue life analyses were performed using both Smith-Watson-Topper (SWT) model and Jahed-Varvani energy-based (JV) model. The fatigue life predictions through both models agree well with the experimental data.
Effect of subfreezing testing temperature on tensile mechanical behavior of fine-grained magnesium
Here, the effect of testing temperature on mechanical properties and deformation mechanisms was investigated by tensile testing of fine-grained magnesium samples under a range of temperatures (i.e. room temperature 20°C, subfreezing temperatures 0°C, -30°C, and - 60°C) and microstructural observations of both untested and tested samples using electron backscatter diffraction. The results suggest that mechanical properties and deformation mechanisms were significantly affected by lowering testing temperature. Strength increased linearly and ductility decreased linearly with the decrease of testing temperature. Although twinning is generally known to be athermal, this experimental study shows that tensile twinning is the dominating deformation mechanism at room temperature, and that twinning is negligible and dislocation operation is the primary deformation mechanism at 0°C, -30°C, and -60°C
Effect of pre-compression on microstructural evolution, mechanical property and strengthening mechanism of AZ31 alloy
Not provided.