Li, Siming

Publications and source records attributed to Li, Siming.

18 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2022

Electro-Optical Characterization of Arsenic-Doped CdSeTe and CdTe Solar Cell Absorbers Doped in-situ During Close Space Sublimation

Most contemporary device models predict that an acceptor concentration of at least 10^16 cm^-3 is required to reach an open circuit voltage of 1 V in polycrystalline CdTe-based solar cells. While copper has traditionally been used as the de facto p-type dopant in polycrystalline cadmium telluride (CdTe) and cadmium selenide telluride (CdSeTe), reaching high acceptor concentrations has proved to be challenging in such devices due to significant dopant compensation. The acceptor concentration in copper-doped CdTe and CdSeTe typically ranges from 10^13 to 10^15 cm^-3 and routinely exhibit low external radiative efficiencies below 0.01%, limiting their implied voltage (i.e., quasi-Fermi level splitting) to approximately 900 mV. As an alternative to copper, this work explores the use of arsenic as a p-type dopant for CdTe and CdSeTe. Using a novel technique in which a thin layer of arsenic-containing material is deposited and used as a reservoir for arsenic to diffuse into a front layer of previously undoped material, this contribution demonstrates that high external radiative efficiencies are achievable, a direct result of combined high acceptor concentrations and long minority-carrier lifetimes in the absorber. This leads to improved implied voltages, and indicates that As-doping represents a promising pathway towards improving the external voltage of CdSeTe/CdTe solar cells.

cadmium telluride↗
DOE OSTI2022

Large-Area (Ag,Cu)(In,Ga)Se 2 Thin-Film Solar Cells with Increased Bandgap and Reduced Voltage Losses Realized with Bulk Defect Reduction and Front-Grading of the Absorber Bandgap

The 1.24 eV bandgap, 18.8% power conversion efficiency Ag-alloyed chalcopyrite (Ag,Cu)(In,Ga)Se 2 (ACIGS) solar cells are characterized to relate voltage and efficiency improvements to electro-optical (EO) characteristics. Shockley-Read-Hall recombination center defect density, identified and characterized through deep level transient spectroscopy and time-resolved photoluminescence (TRPL), is reduced through potassium and copper treatment optimization. Concomitantly, longer minority carrier lifetimes are achieved, which increases open-circuit voltage (V OC ). Near-conduction band defects associated in earlier studies with light-induced current instability are also mitigated. Analysis of charge-carrier dynamics after single- and two-photon excitation is used to separate recombination at the front interface and in the absorber bulk. From TRPL decay simulations, the authors estimate ranges of key solar cell material characteristics: bulk carrier lifetime T bulk = 110-210 ns, charge-carrier mobility u = 110-160 cm 2 V -1 s -1 , and front interface recombination velocity S front = 700-1050 cm s -1 . This lowest-reported S front for ACIGS absorbers originates from the notched conduction band grading, which also makes the impact of the back interface recombination negligible. It is suggested in the results that solar cell performance enhancements can be made most readily with two distinct strategies: improving device architecture and reducing semiconductor defect densities. Using these approaches, power conversion efficiency in large-area solar cells is improved by 1.1% absolute.

14 SOLAR ENERGY↗
DOE OSTI2022

Understanding What Limits the Voltage of Polycrystalline CdSeTe Solar Cells

The origin of voltage deficits in polycrystalline cadmium selenide telluride (CdSeTe) solar cells is unclear. Here, we present a comprehensive voltage loss analysis performed on state-of-the-art CdSeTe devices - fabricated at Colorado State University and First Solar - using photoluminescence techniques, including external radiative efficiency (ERE) measurements. More specifically, we report the thermodynamic voltage limit Voc,ideal, internal voltage iVoc and external voltage Voc of partially and fully finished cells fabricated with different dopant species, dopant concentrations and back contacts. Arsenic-doped aluminium-oxide-passivated cells made at Colorado State University present remarkably high ERE (>1%) - translating into iVoc above 970 mV - but suffer from poor back-contact selectivity. On the other hand, arsenic-doped devices from First Solar present almost perfect carrier selectivity (Voc=iVoc), leading to Voc above 840 mV, and are limited by recombination in various parts of the device. Thus, development of contact structures that are both passivating and selective in combination with highly luminescent absorbers is key to reducing voltage losses.

CdSeTe devices↗
DOE OSTI2021

Distinguishing bulk and surface recombination in CdTe thin films and solar cells using time-resolved terahertz and photoluminescence spectroscopies

Understanding the nature of recombination and its dependence on defects and interfaces is essential for engineering materials and contacts for higher open circuit voltage (V oc ) and power conversion efficiency in photovoltaic (PV) devices. Time-resolved photoluminescence (TRPL) has conventionally been used to evaluate recombination, but carrier redistribution often dominates the response at short times. In this work, we report on the quantification of carrier dynamics and recombination mechanisms by complementary use of both time-resolved terahertz spectroscopy (TRTS) and TRPL combined with numerical modeling of the continuity equations and Poisson’s equation. We have demonstrated this approach using CdTe thin films. A thin film stack with CdTe fabricated by vapor transport deposition and treated with CdCl 2 exhibited a bulk lifetime of 1.7 ± 0.1 ns, negligible CdTe/CdS interface recombination velocity, and back surface recombination velocity of 6.3 ± 1.3 x10 4 cm/s. In contrast, a film stack without CdCl 2 treatment had a bulk lifetime of only 68 ± 12 ps and a higher interface recombination velocity of 4 ± 2 x10 8 cm/s. By determining the locus and mechanisms of performance-limiting recombination, we can accelerate the development of thin-film PVs with higher V oc and efficiency. While the method has been demonstrated here using CdTe, it is also applicable to perovskites, Cu(InGa)Se 2 , Cu2ZnSn(S,Se) 4, and emerging technologies.

14 SOLAR ENERGY↗
DOE OSTI2021

Voltage Loss Comparison in CdSe/CdTe Solar Cells and Polycrystalline CdSeTe Heterostructures

Cd(Se)Te solar cells have considerable headroom to increase voltage. Voltage losses occur due to incomplete absorption above bandgap E_g and band tail absorption below E_g; such losses are quantified using radiative voltage. The largest voltage losses are attributed to nonradiative recombination, which is quantified via carrier lifetime and radiative efficiency. We compare radiative voltage, radiative efficiency, and carrier lifetime for Cu-doped CdSe/CdTe solar cells and for undoped polycrystalline CdSeTe heterostructures passivated with Al_2O_3. Using external quantum efficiency spectrum and a CdSeTe absorption spectrum obtained from absolute photoluminescence (PL), we show that the radiative voltage is greater than 1.1 V. Time-resolved PL experiments and modeling show that a major part of voltage losses can be attributed to recombination in the absorber bulk. The front interface recombination makes a larger impact within the first few nanoseconds after pulsed excitation, and the comparison of time-gated and time-integrated PL can be used to assess relative contributions of front interface and bulk recombination rates.

14 SOLAR ENERGY↗
DOE OSTI2021

Sub-Bandgap Features in CdSeTe Solar Cells: Parsing the Roles of Material Properties and Cell Optics

In this contribution, we investigate why different dopant species and back-contact architectures lead to different sub-bandgap behaviors in CdSeTe solar cells. Through extraction of the absorptance from photoluminescence spectra, we parse the contributions from material properties and from cell optics. We show that, as expected, arsenic doping leads to an increase in sub-bandgap features over traditional copper doping, and that this is a material property of arsenic-doped CdSeTe. Conversely, the increase in sub-bandgap absorption and emission using alternative back contact architectures can be attributed to the cell optics, and more specifically to the increased reflectance of the back interface, leading to at least a doubling of the pathlength for sub-bandgap photons.

arsenic doping↗
DOE OSTI2021

Optical Characterization of Defects in High-Efficiency (Ag,Cu)(In,Ga)Se2

We applied time-resolved photoluminescence (TRPL) spectroscopy to study optimized chalcopyrite (Ag,Cu)(In,Ga)Se2 thin films. The device shows power conversion efficiency of 18.7%. The metastable defect VSe-VCu within ACIGS at EV+0.98 eV is detected in sub-bandgap TRPL excitation spectra. TRPL lifetime of 50 ns is limited by the density of mid-gap defects such as CuGa or CuIn. The similarity of TRPL dynamics before and after light soaking indicates the optimized ACIGS thin film is less metastable because the density of VCu-VSe defect is reduced to below 10^15 cm^-3. This study indicates that ACIGS has improved cell efficiency and reliability characteristics.

41 EE - Solar Energy Technologies Office (EE-4S)↗
DOE OSTI2021

CdSexTe1-x/CdTe Devices with Reduced Interface Recombination Through Novel Back Contacts and Group-V Doping

Since excellent carrier lifetimes and front interface electronic quality are now achieved, rear interface recombination can limit V OC in CdSexTe1-x/CdTe solar cells. Several back-contact structures for devices were fabricated using combinations of tellurium, aluminum oxide, amorphous silicon, and indium tin oxide (ITO). Time-resolved photoluminescence was used to characterize such structures. We show increasingly improved interface passivation through the subsequent use of aluminum oxide, amorphous silicon, and ITO. Additionally, we show that arsenic-doped absorbers form a more passive interface with numerous back contact structures.

aluminum oxide↗
DOE OSTI2021

Microsecond Carrier Lifetimes in Polycrystalline CdSeTe Heterostructures and in CdSeTe Thin Film Solar Cells

We report significant advances in understanding and reducing nonradiative Shockley-Read-Hall recombination in polycrystalline CdSe x Te 1-x , leading to microsecond charge carrier lifetimes. In undoped Al 2 O 3 -passivated heterostructures we find external radiative efficiency 0.2%, quasi-Fermi level splitting 950 mV, mobility 100 cm 2 /(Vs), and diffusion length 14 µm. In solar cells measured lifetimes can exceed 1 µs. We interpret this data to indicate MgZnO/CdSeTe interface recombination velocity <; 100 cm/s. Based on our results, it appears CdTe PV technology has potentially overcome longstanding “recombination lifetime” limitation and in the near future will transition to improving other aspects of device design.

41 EE - Solar Energy Technologies Office (EE-4S)↗
DOE OSTI2021

Calculation of the Thermodynamic Voltage Limit of CdSeTe Solar Cells

The first step to understand the origin of losses in any photovoltaic solar cell is to determine the fundamental thermodynamic efficiency and voltage limits of such a device. In this contribution, we detail techniques to calculate the voltage limit in the case of cadmium selenium telluride (CdSeTe) solar cells, and how approaches based on bandgap alone—i.e., the Shockley-Queisser approach with step-function absorptance—can overestimate the thermodynamic open-circuit voltage limit Voc,ideal . This is particularly true for arsenic-doped samples, which tend to exhibit below-bandgap absorptance.

absorptance↗
DOE OSTI2020

Nanosecond carrier lifetimes in solution-processed enargite (Cu 3 AsS 4 ) thin films

Enargite (ENG) Cu 3 AsS 4 is a promising material for photovoltaic applications due to its constituent earth abundant elements of differing ionic radii, ideal predicted optoelectronic properties, and demonstrated use in a working thin-film solar cell. However, little is known about ENG's defect properties; such knowledge is necessary to assess its potential for future use in high-efficiency devices. One indicator of a material's quality is its photogenerated carrier lifetime, which can be related to its bulk defect properties. Here, we use a combination of time-resolved terahertz spectroscopy and time-resolved photoluminescence to assess carrier dynamics in ENG thin films processed from nanoparticle precursors. The Shockley–Read–Hall (SRH) lifetimes are on the multi-nanosecond scale, which exceed those reported in more mature systems and represent promising values for a candidate photovoltaic material. These results suggest that ENG is worthy of further research and development effort with an eye toward future photovoltaic applications.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗
DOE OSTI2020

Impact of K-Optimization on Trap Concentration in (Ag,Cu)(In,Ga)Se 2 Solar Cells

Recent progress has been made in improving efficiency in Cu(In,Ga)Se 2 (CIGS) absorbers with steady increases in peak efficiency. One way this has been achieved is by adding Ag to CIGS (ACIGS) to achieve higher V OC . However, these efficiencies are still well below the Shockley-Queisser efficiency limit, and traps acting as recombination centers and compensating centers are one thing limiting the solar efficiency. Past research in CIGS has shown that alkali treatment can improve the efficiency and metastability problems in CIGS, but less is understood about the role of alkali treatments in ACIGS. Here, we investigate the impact of potassium in ACIGS through its impact on trap incorporation and minority carrier lifetime. The samples in this study were grown in a roll-to-roll coater with Mo, ACIGS, CdS, and ZnO structure. Both cells were grown identically except the second (K-optimized) cell was grown with increased K-doping of the Mo contact and was more Cu-poor near the surface to optimize the K profile. This resulted in an efficiency increase from 16.8% to 18.7% for the K-optimized cell, which was mostly due to a 65 mV V OC increase. The doping profile showed a 2X increase in acceptor concentration of the K-optimized cell (2.5×10 15 cm -3 ) which suggests that the K was better incorporated into the ACIGS after these optimizations. To characterize the traps in these cells, deep level transient and optical spectroscopy were used. The DLOS measurements showed an EV+0.98 eV trap whose concentration was reduced 10X in the K-optimized cell (4×10 14 cm -3 ). This is consistent with previous results from the alkali treatment in CIGS, which also showed a decrease in near-conduction band trap concentration [1], but the reduction was larger than previous studies possibly indicating the combination of K and Cu-poor surface may both have aided in reducing the EV+0.98 eV trap concentration. The other primary trap is the mid-gap trap (EV+0.58 eV), which was quantified using DLTS. Its concentration decreased from 9×10 13 cm -3 to 4×10 13 cm -3 in the K-optimized sample, which is a 2X reduction. Previous studies have shown this trap is likely an efficient recombination center [2], which makes sense because it is near mid-gap. This trap has also been associated with V OC instability and reduction, so reducing this trap concentration is essential to achieve high V OC and cell efficiency. To help confirm this association, time-resolved photoluminescence measurements have shown in this sample set and a previous study that the minority carrier lifetime (19 ns baseline to 56 ns K-optimized) and this EV+0.56 eV trap concentration are inversely proportional, which would be expected for a recombination-limited carrier lifetime. The K optimization of ACIGS results in significantly improved cell efficiency and reduced trap concentrations that correlate with the improved material and electrical properties. We will report on this and the impact of the K optimization on the cell metastability.

14 SOLAR ENERGY↗
DOE OSTI2020

CdSexTe1-x /CdTe Devices With Reduced Interface Recombination Through Novel Back Contacts and Doping Strategies

In order to study rear interface recombination in CdSexTe1-x/CdTe solar cells, several back contact structures were fabricated using combinations of tellurium, alumina, amorphous silicon, and indium tin oxide. Film side Time-Resolved Photoluminescence measurements were taken to measure carrier lifetimes and interface recombination at the back interface. We show increasingly improved interface passivation through the subsequent use of alumina, amorphous silicon, and ITO. Additionally, we provide evidence that an arsenic-doped absorber forms a better interface with numerous back contact structures. Reductions in the back interface recombination velocity are shown to correlate with improvements in device external radiative efficiency.

13 HYDRO ENERGY↗
DOE OSTI2020

Arsenic Doping of Polycrystalline CdSeTe Devices for Microsecond Life-times with High Carrier Concentrations

We report seminal advances in fabrication and understanding of group V (As) doped thin-film polycrystalline CdTe-based solar cells. The devices are fabricated using a novel approach, by sublimating layers of CdSeTe and CdSeTe:As. This new method allowed us to achieve minority carrier lifetime of over 1 μs, carrier concentration of more than 5x1015 cc-1 and external radiative efficiency of over 2% in a device configuration. We find an increase in open-circuit voltage when comparing As-doped, Cu-doped and undoped devices. The choice of CdSeTe instead of a CdTe-only absorber has been explained using first-principle density functional theory model. A SCAPS device model is used to analyze the potential causes for lower open-circuit voltage.

14 SOLAR ENERGY↗
DOE OSTI2020

Arsenic Doping of Polycrystalline CdSeTe Devices for Microsecond Life-times with High Carrier Concentrations

We report seminal advances in fabrication and understanding of group V (As) doped thin-film polycrystalline CdTe-based solar cells. The devices are fabricated using a novel approach, by sublimating layers of CdSeTe and CdSeTe:As. This new method allowed us to achieve minority carrier lifetime of over 1 μs, carrier concentration of more than 5×l0 15 cc -1 and external radiative efficiency of over 2 % in a device configuration. We find an increase in open-circuit voltage when comparing As-doped, Cu-doped and undoped devices. The choice of CdSeTe instead of a CdTe-only absorber has been explained using first-principle density functional theory model. A SCAPS device model is used to analyze the potential causes for lower open-circuit voltage.

Munshi, Amit H.↗
DOE OSTI2020

Optoelectronic Characterization of Emerging Solar Absorber Cu3AsS4

Enargite Cu 3 AsS 4 is a promising absorber for thin-film solar cells but little is known about its optoelectronic properties. Here, we present photoluminescence (PL) spectroscopy, time-resolved terahertz spectroscopy (TRTS), timeresolved photoluminescence (TRPL) spectroscopy, and cyclic voltammetry (CV) measurements of enargite thin films. The results indicate promising defect characteristics with minority carrier lifetimes on the order of ns, and band alignments suggest that buffer layers besides CdS must be developed to achieve high efficiency Cu 3 AsS 4 solar cells.

14 SOLAR ENERGY↗