Depth-Resolved Lithiated Gradients in Pristine and Laser-Ablated Anodes During Fast Charging
Laser ablating 3D electrode microstructures is a technique to improve Li-ion battery fast-charge performance. This technique has been theoretically proposed and electrochemically validated previously in the literature. The fundamental principle underlying laser ablation is that the ablated features reduce Li-ion transport pathways, improving access to the electrode active material near the current collector. This, in turn, promotes more homogeneous electrode utilization. The present study seeks to directly affirm the physics attributed to laser ablation using operando high-speed synchrotron X-ray diffraction. In this study, depth-resolved graphite lithiation gradients are measured operando during high-rate (15 min) charging. The depth-resolved lithiation dynamics of both ablated and non-ablated anodes are compared. The results highlight that the laser-ablated graphite electrode has notably more homogeneous utilization as compared to the non-ablated electrode. Additionally, the ablated electrode has a significant delay in reaching the maximum graphite lithiation at the separator, indicating less propensity for lithium plating. During low rate delithiation/discharge (2 hr), the two cells' lithiation gradients converge. Notably, a calibrated physics-based electrochemical model accurately reflects experimental findings, suggesting the potential to use pseudo-4D models not only to optimize laser ablation parameters in fast-charge capable electrodes but also to guide fast charging protocols that avoid lithium plating.