DOE OSTI2023

Phase patterning of metallic glasses through superfast quenching of ion irradiation-induced thermal spikes

Amorphous metallic glasses (MGs) convert to crystalline solids upon annealing at a high temperature. Such a phase change, however, does not occur with the local melting caused by damage cascades introduced by ion irradiation, although the resulting thermal spikes can reach temperatures > 1000 K. This is because the quenching rate of the local melting zone is several orders of magnitude higher than the critical cooling rate for MG formation. Thus the amorphous structure is sustained. This mechanism increases the highest temperature at which irradiated MG sustains amorphous phase. More interestingly, if an irradiated MG is pre-annealed to form a polycrystalline structure, ion irradiation can locally convert this crystalline phase to an amorphous phase if the grains are nanometers in size and comparable to the damage cascade volume size. Combining pre-annealing and site selective ion irradiation, patterned crystalline-amorphous heterogeneous structures have been fabricated. This finding opens new doors for various applications.

36 MATERIALS SCIENCE↗

DOE OSTI2023

A quantitative method to determine the region not influenced by injected interstitial and surface effects during void swelling in ion-irradiated metals

We propose and demonstrate a microstructurally-based experimental method to quantitively determine the depth regions in self-ion-irradiated metals that are affected by the injected interstitial effect and various surface effects, focusing on the choice of safe analysis zones to minimize the impact of these phenomena. The goal is to define the depth ranges where extracted data can be confidently applied to ion-neutron correlations for reactor application. Since ion energies in the range of 1–5 MeV are most frequently employed by the radiation effects community, irradiations were conducted at four energies in this range, all proceeding at 475 °C. The experiment was conducted on relatively pure single crystal iron to focus only on physical phenomena, avoiding the influence of possibly confounding chemical or segregation processes. Care was also taken to minimize the influence of other physical factors such as crystalline orientation. It was shown that, at 475 °C, ion energies of ≤1 MeV were too shallow in penetration and did not yield a safe depth range, but irradiations at 2.5 MeV and above yielded useful safe zones with predicted swelling behavior becoming independent of ion energy. The surface-affected zone width was found to be roughly twice that of the void-denuded zone width and to be independent of accumulated displacement dose. The largest injected-interstitial effect arises from the injected interstitial depression of void nucleation and growth. The interstitial-affected region starts at about one half of the projected range and does not show any “spreading” of its influence in depth as the peak damage level increases from 50 to 100 dpa. This study provides some confidence that enhances the credibility of ion simulation when applied to prediction of void swelling in neutron environments.

36 MATERIALS SCIENCE↗

DOE OSTI2022

A method to predict texture effect on ion beam channeling analysis of polycrystals and the application to study the mosaic spreading effect in highly oriented pyrolytic graphite

We propose a method to convert the channeling Rutherford backscattering spectrum yield map of a single crystal to a polycrystal through a matrix rotation technique. The rotation matrix is determined by the deviation of the crystal axial direction from the original z axis. The final yield map is created after averaging the rotated yields using the texture function as the weight factor. For highly oriented pyrolytic graphite (HOPG) exhibiting mosaic spread, the method leads to a Gaussian kernel averaging of the map obtained from a single crystal. The yield map of a single crystal is obtained by a simulation of ion trajectories in a potential field described by Moliere screened Coulomb potentials. Yield maps are calculated under various σ values (standard deviations of mosaic spread). The simulated results are compared with experimental results obtained using 1.2 MeV alpha particle. σ is extracted through the best fitting, demonstrating that the method can be used to obtain texture details. The effects of mosaic spread on minimum yield χ min and the half-width at half maximum of angular scans ψ ½ are systematically modeled and compared with previous theoretical equations. The study also shows that previous theoretical equations are valid only at small σ values. The proposed method can be applied to any type of polycrystal and is not limited to HOPG. It provides near-surface mosaic spread and crystallography information with a longitudinal depth resolution of tens of nanometers and is not influenced by grain shapes.

73 NUCLEAR PHYSICS AND RADIATION PHYSICS↗