Engineering topics
Publications and source records attributed to Liang, Yujia.
A process for forming cubic LLZO through the use of atomic mixing of metal salts used in an aerosol process. The cubic LLZO is formed at temperatures below 1000° C.
A dry process for coating Ni-rich cathode powder with cubic LLZO powder prepared by flame spray pyrolysis.
This study proposes constant-voltage charging as a promising fast-charging protocol and reveals the origin of capacity degradation in constant-voltage charging.
Nickel-rich cathode materials (LiNi x Mn y Co 1-x-y O 2 , NMC) are promising to push the limits of lithium-ion batteries to higher energy density. This approach is favored in practical applications including electric vehicles and aviation transportation. However, the instability of the NMC at charged state results in safety concerns and poor cycling stability. Surface coating is a practical and effective strategy to address this. Cubic Li7La3Zr2O12 (LLZO) is an ideal coating material regarding the low electron transfer rate and high Li+ conductivity. Thus, a LLZO coating layer can suppress the parasitic reactions in the electrode/electrolyte interface without deteriorating the lithium migration. However, high-temperature calcination seems to inevitably create the chemical couplings between NMC and LLZO, leading to the interdiffusion and degradation of NMC and LLZO crystal structures. This work presents a simple mechanochemical method to effectively coat LLZO on the NMC particle surface. Furthermore, the coated cathode demonstrates superior electrochemical performance compared with the pristine NMC cathode.
Flame-spray-pyrolysis (FSP) is a robust and scalable process to synthesize particles at the commodity-scale. FSP has been used to produce the precursor powders which were converted to the layered structure $(R\bar{3m} \text { phase})$ by a postannealing step in making nickel-rich cathode materials (NCMs). Theoretically, the high flame temperature (normally >1500 K) in FSP can provide adequate energy for the phase conversion from rock-salt to layered structures and potentially enables one-step synthesis. However, the high flame temperature is a critical issue to cause lithium loss and structural degradation, preventing the formation of the layered phase. Here, guided by the gaseous nucleation theory, we implemented several FSP processes with different solution recipes. The layered phase concentration in the as-burned products can be increased with the solution enthalpies. By adding a rapid quench step to suppress the lithium loss and phase degradation, the layered phase can be further increased. This work contributes new ideas to innovating process regarding the process efficiency and throughput of manufacturing cathode materials at a large scale.
Solid-state lithium batteries (SSLBs) have been regarded as one of the next-generation energy storage systems. With the adoption of solid-state electrolytes (SSEs) and lithium metal anodes, SSLBs enable higher energy density and more reliable safety than the state-of-the-art lithium-ion batteries. Among potential SSEs, the cation-doped Li 7 La 3 Zr 2 O 12 (LLZO) is promising for its high ionic conductivity (~10 –3 S cm –2 ) at room temperature and high stability with Li metal anode. However, the storage of doped LLZO in the ambient condition suffers the aging effect, including the structural transition (i.e. low-temperature cubic form) and the stoichiometric changes (i.e. Li 2 CO 3 ). These changes are detrimental to LLZO ionic conductivity and interfacial stability in SSLBs. To this end, in this study we are motivated to investigate the structural and stoichiometric reversibility of aged LLZO during thermal treatment. With the help of an in-situ synchrotron-based high-energy X-ray diffraction technique, our experiments revealed that the LLZO powders became a low-temperature cubic phase when exposed to the ambient condition for an extended period of time. A high temperature cubic form can be restored after a thermal treatment of the aged LLZO powder, regardless of the type of dopant. However, the restoration of the stoichiometry remained a challenge, and the degree of the restoration showed a clear dependence on the dopant chemistry.