DOE OSTI2023

Three-dimensional morphology of an ultrafine Al-Si eutectic produced via laser rapid solidification

Al-Si alloys processed by laser rapid solidification yield eutectic microstructures with ultrafine and interconnected fibers. Such fibrous structures have long been thought to bear resemblance to those formed in impurity-doped alloys upon conventional casting. Here, we show that any similarity is purely superficial. By harnessing high-throughput characterization and computer vision techniques, we perform a three-dimensional analysis of the branching behavior of the ultrafine eutectic and compare it against an impurity-modified eutectic as well as a random fractal (as a benchmark). Differences in the branching statistics point to different microstructural origins of the impurity- and quench-modified eutectic. Finally, our quantitative approach is not limited to the data presented here but can be used to extract abstract information from other volumetric datasets, without customization.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Effect of Cooling Rate on Nano-Eutectic Formation in Laser Surface Remelted and Rare Earth Modified Hypereutectic Al-20Si Alloys

Laser Surface Remelting (LSR) was applied to arc-melted Al-20Si-0.2Sr, Al-20Si-0.2Ce, and Al-20Si hypereutectic alloys to refine microstructures. Experiments revealed that microstructures in the melt pool varied from fully eutectic to a mixture of Al dendrites and inter-dendritic eutectic. We calculated cooling rates using the Eagar-Tsai model and correlated cooling rates with characteristic microstructures, revealing that a cooling rate on the order of 104 K/s could lead to maximized fully eutectic microstructure morphology. Due to rapid solidification, the Si composition in the LSR eutectic was measured at 18.2 wt.%, higher than the equilibrium eutectic composition of 12.6 wt.%Si. Compared to Al-20Si, Ce addition had no significant effect on the volume fraction of the fully eutectic structure but refined Si fibers to approximately 30 nm in diameter. Sr addition did not further refine the diameter of eutectic Si fibers compared to Al-20Si but increased the volume fraction of the fully eutectic microstructure morphology. The refinement ratio (φ) of the Si fiber diameter from the bottom of the melt pool to the surface for the three alloys was similar, at around 28%. The established correlation between the cooling rate and the size and morphology of the microstructure within the melt pool will enable tailoring of the microstructure in laser-processed as well as deposited alloys for high strength and plasticity.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Ultrahigh strength and plasticity in laser rapid solidified Al–Si nanoscale eutectics

As-cast Al–20wt.% Si alloys were processed via laser rapid solidification (LRS) techniques to create eutectic microstructures with nanoscale interconnected, nanotwinned Si fibers. LRS morphologies exhibit higher flow stress, exceeding 800 MPa and uniform plastic deformation above 20% compared to as-cast alloy that fractures at strains below 8% at flow strength of approximately 200 MPa. The strengthening mechanisms of LRS morphologies are interpreted in terms of the interfacial constraints: increase in yield strength as well as strain hardening rate due to nanoscale confined slip in fibrous Al–Si eutectic, and load transfer and eventual plasticity in the nanoscale Si fibers.

36 MATERIALS SCIENCE↗