DOE OSTI2023

Improving Cycling Performance of Anode-Free Lithium Batteries by Pressure and Voltage Control

The anode-free lithium (Li) batteries (AFLBs) have great potential to provide higher energy density than most other batteries. However, the performance of AFLBs is very sensitive to pressure and other operating parameters, especially for coin cells widely used in AFLB investigations. Therefore, optimizing cell assembly parameters and test protocol is critical to get reliable and comparable results in this field. In this work, the operating voltage range of AFLBs using a localized high concentration electrolyte has been optimized. The morphology of the deposited Li in AFLBs is much more indicting to the pressure than other type of batteries due to the absence of anode active material (i.e. Li) as a pressure cushion layer in the as prepared cells. With an optimized cycling protocol, a thin layer of uniform nucleation sites can be formed in the initial cycle which will facilitate smooth Li desposition/stripping in the subsequent cycles of AFLBs. The solid electrolyte interphase layer formed under optimized pressure and uniform pressure distribution exhibits a good mechanical stability even after long-term cycling. In conclusion, with an optimized cell configuration, the internal pressure in the coin cells has been optimized to improve the cycling performance of AFLBs (Cu||NMC811) with 72% of capacity retention in 100 cycles.

25 ENERGY STORAGE↗
DOE OSTI2023

Room Temperature Electrorefining of Rare Earth Metals from End-of-use Nd-Fe-B Magnets

Recovering rare earth elements (REE) from used permanent magnets, which contains about 30 wt.% of rare earth elements, has been persistent technological challenge. Current recycling methods relies on pyrometallurgical or hydrometallurgical processes which are energy- and chemical- intensive and not economically and environmentally viable for rare earth containing magnets. Enabling efficient and simplistic recovery and refining of REEs contained in End-of-Use (EoU) products, such as Neodymium-Iron-Boron (Nd-Fe-B) based magnets will play an important and complementary role in the total supply of REEs in the future. We designed a new electrochemical method and demonstrated a room temperature one-pot process that concurrently separates and electroplates REE from commercial Nd-Fe-B magnets. By establishing selective oxidation and reductive potential as electrochemical control parameter along with electrochemically compatible non-aqueous electrolyte system, we demonstrated selective electroleaching of lanthanides (Nd and Preseodymium (Pr)) from anode and concurrent plating as alloy at Pt cathode. The morphological and chemical evolution of the Nd-Fe-B magnets during electroleaching reveals the electrochemical stimuli and rate of dissolution depends on microstructural complexities of the Nd-Fe-B magnet. The concomitant electroplating process leads to Nd-Pr based alloy which can be used as raw metallic alloy for manufacturing new permanent magnet and other devices. Our study demonstrates a scalable separation and refining methodology, based on widely available organic electrolyte system and without any consumptive chemical use, for selective lanthanide recovery from waste magnets.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Porous Liquids as Electrolyte: A Case Study of Li + and Mg 2+ Ion Transport in Crown Ether-Based Type-II Porous Liquids

Here, we demonstrate crown ether (CE)-based type II porous liquid (PL) electrolytes in which CEs provide internal porosity and are capable of coordinating with Li + and Mg 2+ ions. We investigated the physicochemical properties of the PL electro-lytes with different functional groups and cavity sizes. Among the electrolytes studied, the 12-crown-4 (12C4)-based PL electrolyte exhibited the most enhanced ionic conductivity due to size match between the CE cavity and the Li + ion. Nu-clear magnetic resonance and Fourier transform infrared analyses revealed that addition of CEs reduces the Li + ion–solvent interaction, resulting in the formation of Li-CE complexes. The simulation study clearly showed that the solvated Li + and Mg 2+ ions form complexes with 12C4. The strategy described here using CE-based PLs should be applicable to the design versatile electrolytes for various metal-ion batteries.

Shin, Sun Hae Ra↗
DOE OSTI2022

Facile Dual-Protection Layer and Advanced Electrolyte Enhancing Performances of Cobalt-free/Nickel-rich Cathodes in Lithium-Ion Batteries

Despite cobalt (Co)-free/nickel (Ni)-rich layered oxides being considered as one of the promising cathode materials due to their high specific capacity, their highly reactive surface is one of the shortcomings that still hinder their practical usages in high-energy-density batteries. Herein, a polyimide/polyvinylpyrrolidone (PI/PVP, denoted as PP) coating layer is demonstrated as dual-protection for LiNi 0.96 Mg 0.02 Ti 0.02 O 2 (NMT) cathode material to suppress surface contamination against moisty air and to prevent unwanted side reactions between cathode and electrolyte during electrochemical cycling. The optimal PP-coated NMT (PP@NMT) preserves a clean surface without generation of lithium (Li) residues, structural degradation, and gas evolution after exposure to air with ~30% humidity for 2 weeks. Contrarily, the exposed bare NMT shows severe contamination, structural shrinkage due to Li loss, and increased gas release during charging. In addition, the exposed PP@NMT significantly enhances the electrochemical performance of graphite (Gr)||NMT cells by decreasing byproducts and maintaining structural stability. Moreover, the exposed PP@NMT achieves a high capacity retention of 86.7% after 500 cycles in Gr||NMT cells using an advanced localized high-concentration electrolyte. Furthermore, this work demonstrates a promising facile approach to the protection of Co-free/Ni-rich layered cathodes for their practical applications even after exposure to moisty air.

25 ENERGY STORAGE↗
DOE OSTI2022

Crosslinked Polyethyleneimine Gel Polymer Interface to Improve Cycling Stability of RFBs

Redox flow batteries are considered a promising technology for grid energy storage. However, capacity decay caused by crossover of active materials is a universal challenge for many flow battery systems, which are based on various chemistries. In this paper, using the vanadium redox flow battery as an example, we demonstrate a new gel polymer interface (GPI) consisting of crosslinked polyethyleneimine with a large amount of amino and carboxylic acid groups introduced between the positive electrode and the membrane. The GPI functions as a key component to prevent vanadium ions from crossing the membrane, thus supporting stable long-term cycling. Cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) measurements were conducted to investigate the effect of GPI on the electrochemical properties of graphitic carbon electrodes (GCFs) and redox reaction of catholyte. X-ray photoelectron spectroscopy (XPS) and 1 H nuclear magnetic resonance (NMR) spectra demonstrated that the crosslinked GPI is chemically stable for 100 cycles without dissolution of polymers and swelling in the strong acidic electrolytes. Results from inductively coupled plasma mass spectrometry (ICP-MS), Fourier-transform infrared (FTIR) spectroscopy, and energy-dispersive X-ray (EDX) spectroscopy proved that the GPI is effective in maintaining the concentration of vanadium species in their respective half-cells, resulting in improved cycling stability because of it prevents active species from crossing the membrane and stabilizes the oxidation states of active species.

Lim, Hyung-Seok↗
DOE OSTI2021

Stable Solid Electrolyte Interphase Layer Formed by Electrochemical Pretreatment of Gel Polymer Coating on Li Metal Anode for Lithium–Oxygen Batteries

Lithium (Li)-oxygen (O2) batteries (LOBs) exhibit the highest theoretical specific energy density among candidates of the next-generation energy storage systems, but the instability of Li metal anode (LMA), air electrode, and electrolyte largely limit the practical energy density of these batteries. Herein, we report an effective method to protect LMA against side reactions between LMA and crossover contaminants such as highly reactive oxygen moieties. A solid electrolyte interphase (SEI) layer rich in inorganic components was formed on a LMA coated with polyethylene oxide thin-film through an in-situ electrochemical pre-charging step under oxygen atmosphere. This uniformly distributed stiff SEI layer interacted with flexible polymer matrix and formed a submicron-sized gel-like polymer layer. This polymer supported SEI layer leads to much longer cycle life (130 vs. 65 cycles) as compared to those of pristine cell under the same testing conditions (1.0 mAh cm-2 at 0.2 mA cm-2 in the voltage range of 2 to 5 V without any catalysts). It is also very effective during low voltage (2 to 4.5 V) cycling with a redox mediator (0.1 and 0.15M (2,2,6,6-tetramethylpiperidin-1-yl) oxidanyl). Therefore, this approach can be used to stabilize LMA/electrolytes interphase and improve the cycle life of rechargeable LOBs.

lithium-oxygen batteries, lithium metal anodes, ar↗
DOE OSTI2021

Optimization of Localized High Concentration Electrolytes (LHCE) for Li||LiCoO 2 and Si|| LiCoO 2 Batteries used in Consumer Electronics Applications (Final Report for I3T Project 75934)

This project will optimize localized high concentration electrolyte (LHCE) for Li/LCO and Si/LCO batteries for consumer electronics applications, including select the best solvent and diluent, optimize the ratios of the solvents and the salt concentration. Results will be demonstrated not only in both coin cells, but also in pouch cells, which is required for large-scale commercial applications. This work can provide better understanding that would also benefit other LMB projects, including Li/NMC and Li/S batteries for electric vehicle applications. In the history of rechargeable batteries, all batteries have been first used in small scale consumer electronics, then eventually penetrate to large scale applications such as electrical vehicle or grid. We believe this development route will also be true for LMBs. By developing the best electrolyte for Li/LCO and Si/LCO chemistry, we will not only get the early market entry in consumer electronics, but we can also accumulate experience on the practical application of LMBs which can be used to further develop other types of LMBs for EV and other large-scale applications pursued by DOE.

25 ENERGY STORAGE↗