Lin, R. Y.

Publications and source records attributed to Lin, R. Y..

8 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1996

Comparison Testings between Two High-temperature Strain Measurement Systems

An experimental evaluation was conducted at NASA Lewis Research Center to compare and contrast the performance of a newly developed resistance strain gage, the PdCr temperature-compensated wire strain gage, to that of a conventional high-temperature extensometry. The evaluation of the two strain measurement systems was conducted through the application of various thermal and mechanical loading spectra using a high-temperature thermomechanical uniaxial testing system equipped with quartz lamp heating. The purpose of the testing was not only to compare and contrast the two strain sensors but also to investigate the applicability of the PdCr strain gage to the testing environment typically employed when characterizing the high-temperature mechanical behavior of structural materials. Strain measurement capabilities to 8OO C were investigated with a nickel base superalloy IN100 substrate material, and application to titanium matrix composite (TMC) materials was examined with the SCS-6/Ti-15-3 08 system. PdCr strain gages installed by three attachment techniques, namely, flame spraying, spot welding and rapid infrared joining were investigated.

Lei, J.-F.↗
NASA NTRS1993

TiC growth in C fiber/Ti alloy composites during liquid infiltration

A cylindrical model is developed for predicting the reaction zone thickness of carbon fiber-reinforced Ti-matrix composites, and good agreement is obtained between its predicted values and experimental results. The reaction-rate constant for TiC formation is estimated to be 1.5 x 10 exp -9 sq cm/sec. The model is extended to evaluate the relationship between C-coating thicknesses on SiC fibers and processing times.

Warrier, S. G.↗
NASA NTRS1993

Interfacial reactions in titanium/SCS fiber composites during fabrication

The objectrive of the study was to determine the effect of titanium concentration and different pyrocarbon fiber coatings on the morphology and the extent of fiber-matrix reactions in Ti/SiC composites fabricated by rapid infrared forming (RIF). It is found that the extent of fiber-matrix reactions in Ti/SiC composites fabricated by the RIF technique is noticeably affected by both an increase in Ti content and by the processing temperature. Uncoated SiC fibers extensively react with the titanium alloy matrix at 1200 C, whereas no reaction occurs when coated SiC fibers are used.

Warrier, S. G.↗
NASA NTRS1993

Control of interfaces in Al-C fibre composites

The interface of Al-C fiber composite was modified by coating a silver layer on the surface of carbon fibres prior to making composites, in an attempt to improve the wettability between molten aluminum and carbon fibers during infiltration. An electroless plating technique was adopted and perfected to provide a homogeneous silver coating on the carbon fiber surface. Al-C fiber composites were prepared using a liquid infiltration technique in a vacuum. It was found that silver coating promoted the wetting between aluminum and carbon fibers, particularly with polyacrylonitrile-base carbon fibers. However, due to rapid dissolution of silver in molten aluminum, it was believed that the improved infiltration was not due to the wetting behavior between molten aluminum and silver. The cleaning of the fiber surface and the preservation of the cleaned carbon surface with silver coating was considered to be the prime reason for the improved wettability. Interfacial reactions between aluminum and carbon fibers were observed. Amorphous carbon was found to react more with aluminum than graphitic carbon. This is believed to be because of the inertness of the graphitic basal planes.

Warrier, S. G.↗
NASA NTRS1992

Effect of heat treatment on the flexural properties of a titanium matrix composite

Titanium matrix composites (TMC) reinforced with carbon fibers are widely used in the aerospace industry due to their light weight, high strength and modulus and the retention of their strength and modulus at elevated temperatures. Liquid infiltration, a low cost technique for making TMCs, has been little used due to the extent of the reaction between titanium and carbon during fabrication. Rapid infrared processing (RIP) has been developed as a technique for reducing interfacial reaction during composite fabrication. The strength and modulus of composites produced using RIP were higher than or comparable to those for other composites. This paper examines the effect of heat treatment on the room temperature flexural strength and modulus of TMC produced using RIP. The experiments carried out are described and results are presented. Results showed increased flexural strength of the composites upon aging at temperatures of 800 and 900 degrees C. This increased strength may be due to increased strength of the matrix.

Warrier, S. G.↗
NASA NTRS1992

Sputter deposition of SiC coating on silicon wafers

A study is conducted of the effect of substrate temperature during coating on the properties of coated SiC films on Si wafers, using a scratch test technique. While specimen temperature during coating has little effect on deposition rate, it significantly affects the durability of the coating. Scratch test damage to both film coating and substrate decreased with increasing deposition temperature, perhaps due to the rapid diffusion of the deposited atoms.

Robson, M. T.↗
NASA NTRS1976

Thermal/acoustical insulation foam

Lightweight low-density substance can be used as fire resistant insulation in aircraft. Material density can be controlled over range from 0.6-1.2 pounds per cubic foot and has good thermal and acoustic properties.

Lin, R. Y.↗