DOE OSTI2023

Enhanced through-thickness electrical conductivity and lightning strike damage response of interleaved vertically aligned short carbon fiber composites

Through-thickness electrical conductivity of carbon fiber reinforced polymers (CFRPs) is a key characteristic that determines the severity of lighting strike-induced damage. Carbon Fibers (CFs) are inherently electrically conductive and therefore provide high conductivity in the direction of the fiber orientation. However, electrical conductivities through the thickness and orthogonal to the CF orientation in CFRPs are governed by the insulating polymer matrix present between CFs. Here, in this work, through the thickness alignment of short CFs in between layers of CFRP laminates is demonstrated to improve the through-thickness electrical conductivity. Composites with interleaved vertically aligned short CF fibers (<150 μm) will be referred as V-fiber composites hereafter. The effect of the V-fiber on the lightning strike damage is evaluated against an artificial lightning strike of 100 kA (modified waveform A of SAE ARP-5412B standard). The improved through-thickness electrical conductivity of CFRP laminates (1.15 S/cm) through vertical alignment of short CFs was compared to reference CFRP laminates (0.13 S/cm) and was found to dissipate the artificial lightning strike current more efficiently. The surface damage after the artificial lightning strike in the V-fiber composites was reduced to 12.69 cm 2 compared to the reference CFRP surface damage of 57.67 cm 2 , a 78% reduction. It was also demonstrated that Joule heat generated due to lightning strike on the composites was significantly less than the reference sample using infrared (IR) thermography. A high retention (up to 78%) of flexural properties (modulus and strength) was observed in V-fiber composites post lightning strike impact as compared to only 47% retention in the reference panel.

42 ENGINEERING↗

DOE OSTI2022

Evaluating the Lightning Strike Damage Tolerance for CFRP Composite Laminates Containing Conductive Nanofillers

Conductive nanofillers, such as carbon nanotube, graphene nanoplatelets, and carbon black particles (with diameters in nanometers) have been shown to enhance the electrical conductivity of fiber reinforced polymer matrix composites in many existing studies. The motivation is primarily for lightning strike protection, electromagnetic interference shielding, de-icing, and the manufacturing of lightweight electronic components. Here, we evaluate the lightning strike damage tolerance of carbon fiber reinforced polymer (CFRP) matrix composite laminates containing conductive nanofillers with varying weight fractions, including carbon black (CB), carbon nanotubes (CNT), and a mix of CB and CNT, through simulated lightning strike tests, followed by both non-destructive ultrasonic inspection and destructive sectioning to characterize the damage inflicted by the simulated lightning strike. Three-point flexural tests are performed to evaluate the residual strength retained by all CFRP specimens. Results show that lightning strike damage experienced varying levels of reduction for CFRP composite specimens containing conductive fillers in comparison to the baseline specimen without fillers. Notably, the delamination only penetrated to the interface between the 1st and 2nd layer for the specimen with 0.25 wt.% CNT in comparison to the baseline CFRP specimen for which the delamination penetrated to the interface between the 5th and 6th layer. Moreover, the retention of the flexural modulus increased from 26.5% to a maximum of 95.0% for the specimen with 0.25 wt.% hybrid CB and CNT. Yet, we show that using our chosen conductive fillers cannot fully eliminate lightning strike damage. Additionally, adding conductive fillers could compromise the flexural properties. We provide discussions on future recommendations on using conductive fillers for the lightning strike protection of CFRP composites.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Low cost carbon fiber as potential lightning strike protection for wind turbine blades

Until recently, glass fiber composites (GFRP) were the preferred choice to prepare wind turbine blades due to their low cost compared to their counterpart carbon fiber composites (CFRP). However, to harvest the maximum wind energy, ever larger wind turbine blades are being manufactured. To support such a large structure carbon fiber composites CFRP have become the integral part of load bearing structures in the blade. In this work, we are proposing to utilize the low cost carbon fiber (LCCF), manufactured at Carbon Fiber Technology Facility (CFTF) of Oak Ridge National Laboratory (ORNL) as not only the cost effective alternative to the currently used carbon fiber (CF) but also as the lightning strike protection of the wind turbine blades. Wind turbines often get hit by lightning strikes due to their operating locations. LCCF can provide structural integrity to these gigantic structures and mitigate the effect of lightning strike on them by effectively dissipating the current. Two composite panels made of LCCF were tested against artificial lightning strikes of 100 kA and 200 kA (component A of lightning waveform SAE ARP 5412-B). The results showed very high resilience of LCCF composite due to their high electrical conductivity both in-plane and in through-thickness directions. There was no significant damage (fiber breakage, resin evaporation or delamination) in both the cases.

Kumar, Vipin↗