Multiscale Progressive Failure Analysis of 3D Woven Composites

Application of three-dimensional (3D) woven composites is growing as an alternative to the use of ply-based composite materials. However, the design, analysis, modeling, and optimization of these materials is more challenging due to their complex and inherently multiscale geometries. Herein, a multiscale modeling procedure, based on efficient, semi-analytical micromechanical theories rather than the traditional finite element approach, is presented and applied to a 3D woven carbon–epoxy composite. A crack-band progressive damage model was employed for the matrix constituent to capture the globally observed nonlinear response. Realistic microstructural dimensions and tow-fiber volume fractions were determined from detailed X-ray computed tomography (CT) and scanning electron microscopy data. Pre-existing binder-tow disbonds and weft-tow waviness, observed in X-ray CT scans of the composite, were also included in the model. The results were compared with experimental data for the in-plane tensile and shear behavior of the composite. The tensile predictions exhibited good correlations with the test data. While the model was able to capture the less brittle nature of the in-plane shear response, quantitative measures were underpredicted to some degree.

3D woven composites↗

NASA NTRS2021

Effect of Urea Links in the Backbone of Polyimide Aerogels

Flexible, conformal polyimide aerogels with low density, good mechanical properties and high surface areas have attracted much attention for many potential applications such as lightweight antenna substrates, insulating materials for launch vehicles, inflatable structures, aircraft or space suits. Development and improvements to fabrication of polyimide aerogel thin films have been reported over the last decade to meet the needs of many of these applications. However, most starting materials are expensive. In this research, we utilized commercially available, low cost monomers including 4,4’-bis(4-aminophenoxy)propane (BAPP) and 3,3’,4,4’-benzophenone tetracarboxylic dianhydride (BTDA), and 4,4-methylene diphenyl di-isocyanate (MDI) in fabricating polyimide (PI) and polyimide-urea (PIU), which were then cross-linked with 1,3,5-tris(4-aminophenoxy)benzene (TAB). It was found that the addition of MDI into the PI chains not only maintained the flexibility of the aerogel films, but also enhanced the film casting, allowing the production on pilot scale. With the capability in producing robust films at affordable cost, application of the PIU aerogel films can be expanded to terrestrial goods such as winter clothing, or pipe wrapping, etc. In addition, the presence of only a small addition of the urea links in the polyimide chains in PIU aerogels led to lower shrinkage when compared to the corresponding PI aerogels, leading to lower density

Baochau N. Nguyen↗