3 records

DOE OSTI2023

Improved catalytic activity of Mo x Ni y Al z thin films as electrocatalyst for hydrogen evolution reaction in alkaline media

In this work, we report activities of Mo x Ni y X z (where X is Al, Co, Cr, Cu, Fe, W)-based electrocatalysts for hydrogen evolution reaction (HER) in a 1 M NaOH solution. Mo x Ni y X z thin film electrocatslysts were prepared by magentron sputtering at 25°C and 800°C and characterized by scanning electron microscopy (SEM) with energy dispersive X-ray (EDX) analyzer and X-ray diffraction (XRD) analysis. Here, the catalytic activity of electrocatalyst was studied by cyclic voltammetry and electrochemical impedance spectroscopy. The electrocatalyst based on Mo 80 Ni 5 Al 15 (800°C) shows the best value of the overpotential (-181 mV) for HER from all tested ternary systems. XRD analysis indicates that HER activity only Mo 80 Ni 5 Al 15 thin films prepared at 800°C contained fcc phase. Other less active composition contained only bcc phase. The results obtained from impedance spectroscopy are consistent with the results from cyclic voltammetry. The stability of the prepared catalyst was studied by chronoamperometric analysis. The results from chronoamperometry show that HER activity of Mo 80 Ni 5 Al 15 prepared at 800°C, after very slight initial activity decrease, stays constant, while activity of Ni catalyst decreased almost twice in measured time window. Since Ni is commonly used industrial catalyst, Mo 80 Ni 5 Al 15 based alloy could be more attractive catalyst material for alkaline electrolyzers.

08 HYDROGEN↗

DOE OSTI2022

Structural dependence of hydrogen evolution reaction on transition metal catalysts sputtered at different temperatures in alkaline media

In the present article, we studied the catalytic activity of magnetron sputtered Mo, V, Ni, and Co thin films for hydrogen evolution reaction (HER) in the alkaline electrolyte. Here, we find that the HER potentials (η 10 ) of the Mo and V thin film catalysts sputtered at 800 °C shift positive with respect to those of the film catalysts sputtered at 25°C. For Mo metal the observed shift of η 10 was 280 mV and for V metal observed shift of η 10 was 390 mV. On the other hand, minimal effect of sputtering temperature on both Ni and Co thin film catalyst activity for HER was observed. Structural analysis reveals that Mo and V prepared at 800 °C have uncommon face centered cubic (fcc, 0.74 packing density) structure as opposed to room-temperature sputtered Mo and V thin films which have common body centered cubic (bcc, 0.68 packing density) structure, resulting in significant increases of the packing densities when they are prepared at 800 °C. On the other hand, the high-temperature prepared thin films of Ni and Co retained fcc structures, resulting in no density changes compared to the room-temperature prepared fcc Ni and hexagonal close packed (hcp, 0.74 packing density) Co. Impedance spectroscopy shows that fcc Mo is a better catalyst than fcc Ni, which is considered an industry standard for non-noble pure metal-based catalysts in alkaline media. Stability tests also suggest that fcc Mo thin film catalysts prepared at 800 °C are more durable than fcc Ni thin films. Our study points out that structure phases of catalysts can be a key factor governing the activities of transition metals for HER in alkaline media.

08 HYDROGEN↗

DOE OSTI2022

Study of synergistic effects and compositional dependence of hydrogen evolution reaction on MoxNiy alloy thin films in alkaline media

In this paper hydrogen evolution reaction (HER) on the molybdenum-nickel thin films has been studied. The Mo x Ni y thin films were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). A change in the crystal structure of the samples prepared at different temperatures was observed. The structure of the samples prepared at 25 °C are bcc or amorphous. The structure of alloys sputtered at 800 °C changed to fcc. Tafel plots were constructed for each Mo x Ni y alloy sample. The mechanism of HER was determined from Tafel slope analysis. Values of charge transfer resistance were also determined by impedance spectroscopy. The compositional dependence of activity and the stability of Mo x Ni y thin films in 1 M NaOH were determined by cycling and chronoamperometry. Our results demonstrate that Mo x Ni y thin films prepared at 800 °C show significantly improved activity compared to pure Mo and Ni metals. On the other hand, Mo x Ni y thin films sputtered at 25°C do not show increased activity in comparison to pure Ni metal. Furthermore, this points to a synergistic effect between fcc Mo and fcc Ni in thin films sputtered at elevated temperatures. Mo 63 Ni 67 thin films alloy prepared at 800 °C shows the best values of catalytic activity for HER from all investigated compositions.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗