Investigation of the temperature-dependent failure processes in PVD Cr-coated ZIRLO nuclear fuel cladding using in situ X-ray micro-tomography imaging

In this work, an accident tolerant fuel cladding system with Cr coating deposited using physical vapour deposition (PVD) method onto commercial Optimized ZIRLO™ was studied. The cladding tubes were machined into C-rings and loaded to failure under compression with real-time synchrotron micro-X-ray computed tomography (XCT) imaging at room temperature (RT), 345 °C, 650 °C and 950 °C in argon (Ar) atmosphere. The mechanical behaviour and failure processes were found strongly temperature-dependent where the Cr coating showed brittle fracture at RT and 345 °C, ductile fracture at 650 °C and a reversion to brittle fracture at 950 °C. Nanoindentation measurements and scanning electron microscopy (SEM) imaging were conducted on the materials after high temperature testing. It was found that recrystallisation of the Cr coating occurred at elevated temperatures, which significantly affected its local properties hence the failure behaviour at different temperatures. This work represents the first in situ 3D XCT observation of progressive failure processes in PVD Cr-coated ZIRLO claddings up to 950 °C providing critical insights into its brittle-to-ductile transition (BDTT) behaviour and subsequent ductile-to-brittle reversion with the increase in temperature. Moreover, results are compared with other PVD Cr-coated Zircaloy materials from open literature; the influences of the coating microstructure and local properties on the failure stress/strain and fracture processes are discussed.

Yuan, Guanjie↗
DOE OSTI2024

Under the microscope: Reduced activation ferritic martensitic steel Eurofer-97 following ion-Irradiation and high-temperature high-pressure water exposure

Here, this study is designed to characterise the microstructural behaviour of Eurofer-97 steel under ion irradiation and subsequent exposure to high-temperature high-pressure (HTHP) water. Eurofer-97, a ferritic-martensitic steel, has been developed to withstand the conditions of fusion reactors in the locations in contact with coolant with an elevated level of neutron flux, such as the breeder-wall blanket. The material has been studied after self-ion irradiation (using Fe ions) simulating the microstructural effects of neutron irradiation limited to the subsurface layer. The corrosion properties of the Eurofer-97 steel were studied by exposure to HTHP water up to 331 °C. Advanced microstructural characterisation using scanning, transmission electron and focused ion beam microscopy was performed on the as-received microstructure and after ion irradiation. This was then characterised after exposure for 240 h in high-temperature water. Eurofer-97 had a dense, columnar Cr-rich inner oxide, followed by a Fe-rich outer oxide layer. In the irradiated condition the grain structure and oxide itself was less ordered. No appreciable difference in oxide thickness was identified between the irradiated and unirradiated specimens after this short exposure time.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Chemical insights into ethyl acetate flames from experiment and kinetic modeling: Laminar burning velocity, speciation and NO$_x$ emission

Oxygenated fuels, such as alcohols, ethers, and esters, are promising alternatives to conventional fuels. These fuels can help reduce detrimental emissions like carbon monoxide and unburned hydrocarbons and enhance octane ratings. Among these oxygenates, ethyl acetate (EA), a small alkyl ester sourced from biomass, emerges as a clean, promising energy carrier. It serves as a surrogate fuel to facilitate investigations into the combustion behaviours of biodiesel. Despite its importance, the literature knowledge of EA combustion characteristics is limited. Therefore, this study aims to broaden the knowledge of the combustion behaviour of this type of oxygenated fuel compound. In this study, we measured the laminar burning velocities of EA by employing a heat flux burner and a closed combustion vessel over the equivalence ratios of 0.7 – 1.7, pressures of 1 – 10 bar and temperatures ranging from 353 – 423 K. Further, we also measured the NOx emissions in exhaust gas of the premixed flames fueled by EA/air for the first time over the equivalence ratio of 0.8 – 1.2. Additionally, we employed a non-premixed counterflow flame setup for extensive characterisation of species and their concentration under diverse conditions encompassing various strain rates and oxygen concentrations. Finally, we utilized these newly measured data to construct and validate a detailed kinetic model developed as part of this work. The newly developed model will help characterize the combustion properties of EA.

30 DIRECT ENERGY CONVERSION↗
DOE OSTI2024

Sustainable production of extracellular polymeric substances and iron or copper complex from glutinous rice processing wastewater

Essential trace minerals play vital roles in maintaining human and animal health. However, an overdose of the existing inorganic trace minerals is prone to induce detrimental effects that outweigh positive benefits. In this study, an extracellular polymeric substances (EPS)-producing bacterium, identified as Bacillus licheniformis CCTCC M2020298, was isolated from marine using glutinous rice processing wastewater as enrichment medium. The EPS yield of Bacillus licheniformis CCTCC M2020298 could reach 8.62 g/L by using glutinous rice-processing wastewater containing medium. Furthermore, the potential of the EPS as a carrier for synthesizing EPS-iron (Fe) and EPS-copper (Cu) complex was explored. The results showed that the optimum condition for the synthesis EPS-Fe were the reaction temperature 70°C, pH 8.5–9.0 and mass ratio of EPS to trisodium citrate 2:1. The iron content of EPS-Fe reached 77.4 mg/g. Under the same condition, the copper content of EPS-Cu reached 90.7 mg/g. The elemental composition, functional groups and valence state of the mineral elements of EPS-Fe and EPS-Cu were well characterized. The EPS-Fe and EPS-Cu exhibited antioxidant activity in scavenging ·OH, DPPH and ·O 2− free radicals, thereby leading to reduced oxidative stress and apoptosis levels in human colonic epithelial cells in vitro . They also inhibited the proliferation of mouse hepatocellular carcinoma H22 and the growth of intestinal pathogens in vitro . This study provided an effective avenue for EPS production from glutinous rice processing wastewater and proved the potential of EPS-Fe and EPS-Cu complexes as a new-type comprehensive essential trace mineral supplement.

Chen, Zhen↗
DOE OSTI2023

Porosity evolution in proton irradiated microfine-grained POCO graphite

This work investigated the porosity evolution of POCO ZXF-5Q graphite that has been irradiated by 340 kW, 120 GeV protons inside NT02 target system in Fermilab's NuMI beamline. This POCO graphite has undergone direct bulk dimensional swelling at low dose irradiation and its local microstructural change is still not well-understood during this process. In this work, the (sub-) micrometre scale porosity from six locations across proton beam fluence and temperature gradients have been studied using focused ion beam-scanning electron microscopy (FIB-SEM) tomography. Here, a deep learning-based tomographic image segmentation technique has been established and implemented for porosity segmentation and quantification. It has been found that there is a decrease in the total volumetric percentage of the porosity at proton beam centre (~ 8 – 8.4 vol.%), by comparing to un-irradiated POCO (~ 12 – 13vol.%) and to beam 2σ and 5σ radii (~ 12vol.%). This decrease in porosity volume percentage was found to be caused by the reduction in pores with volumes > 0.1 μm 3 induced by material bulk dimensional swelling at proton beam centre area. The porosity reduction in relation to dimensional change and irradiation creep was discussed among with other contributing factors, and further investigations through well-controlled irradiation experiment are still needed.

73 NUCLEAR PHYSICS AND RADIATION PHYSICS↗
DOE OSTI2023

A novel method for quantifying irradiation damage in nuclear graphite using Raman spectroscopy

Raman spectroscopy has long been used in studying irradiation damage in carbon/graphite materials. It is however unclear if the measurements from different types of materials are directly comparable. Further, decoupling the contribution from irradiation temperature and fluence to the total damage in nuclear graphite possessing irradiation damage gradient is currently not readily feasible as it requires a complete set of test reactor irradiation experiments over the relevant temperature and fluence range. A novel methodology has therefore been proposed and developed to quantify total irradiation damage evolution at crystal level based on graphite Raman G-band position shift. Specifically, G-band positions derived from a large number of spectra collected from the fractured surface of microfine-grained POCO ZXF-5Q graphite possessing proton irradiation damage gradient were plotted with open literature Raman data on HOPG, BEPO (AXGP graphite), PCEA and IG-110 graphite as a function of dpa. The total damage level within 2σ beam radius in this POCO graphite was estimated to be equivalent to ~2–5 dpa at ~350–370 °C. Derived G-band positions were then mapped to the three-stage amorphization trajectory model indicating beam centre area has entered the second stage, i.e., transitioning from nanocrystalline graphite into amorphous carbon. G-band position relative shift (ΔG) curve with a ‘turn-around’ peak as a function of total damage can be used for in-service lifetime prediction. Importantly, the developed methodology has the potential to ‘unify’ total damage levels across different grades of nuclear graphite caused by ion, neutron and proton irradiation at different temperatures.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗
NASA NTRS2004

High Speed Networking and Large-scale Simulation in Geodynamics

Large-scale numerical simulation has been one of the most important approaches for understanding global geodynamical processes. In this approach, peta-scale floating point operations (pflops) are often required to carry out a single physically-meaningful numerical experiment. For example, to model convective flow in the Earth's core and generation of the geomagnetic field (geodynamo), simulation for one magnetic free-decay time (approximately 15000 years) with a modest resolution of 150 in three spatial dimensions would require approximately 0.2 pflops. If such a numerical model is used to predict geomagnetic secular variation over decades and longer, with e.g. an ensemble Kalman filter assimilation approach, approximately 30 (and perhaps more) independent simulations of similar scales would be needed for one data assimilation analysis. Obviously, such a simulation would require an enormous computing resource that exceeds the capacity of a single facility currently available at our disposal. One solution is to utilize a very fast network (e.g. 10Gb optical networks) and available middleware (e.g. Globus Toolkit) to allocate available but often heterogeneous resources for such large-scale computing efforts. At NASA GSFC, we are experimenting with such an approach by networking several clusters for geomagnetic data assimilation research. We shall present our initial testing results in the meeting.

Kuang, Weijia↗