NASA NTRS1996

A Magnetic Bumper-Tether System Using ZFC Y123

We consider the use of magnetic forces in a bumper system, to soften docking procedures. We investigate a system which exhibits no magnetic field except during the docking process, which, if desired, can automatically tether two craft together, and which provides lateral stability during docking. A system composed of zero field cooled Y(1.7)Ba2Cu3O(7-delta) (Y123) tiles and electromagnets is proposed. The Y123 high temperature superconductor (HTS) is mounted on one craft, and the electromagnet on the other. Results of small prototype laboratory experiments are reported. The electromagnet has, for convenience, been replaced by a permanent SmCo ferromagnet in these measurements. When the two craft approach, a mirror image of the ferromagnet is induced in the Y123, and a repulsive bumper force, F(sub B), results. F(sub B) is velocity dependent, and increases with v. For presently available HTS materials, bumper pressure of approx. 3.7 N/cm(exp 2) is achieved using SmCo. This extrapolates to approx. 18 N/cm(exp 2) for an electromagnet, or a force of up to 20 tons for a 1 m(exp 2) system. After reaching a minimum distance of approach, the two colliding craft begin to separate. However, the consequent change of SmCo magnetic field at the Y123 results in a reversal of current in the Y123 so that the Y123 is attractive to the SmCo. The attractive (tether) force, F(sub T), is a function of R = B(sub Fe)/B(sub t, max), where B(sub Fe) is the field at the surface of the ferromagnet, and B(sub t, max) is the maximum trapped field of the Y123, i.e., the trapped field in the so-called critical state. For R greater than or equal to 2, F(sub T) saturates at a value comparable to F(sub B). For a range of initial approach velocities the two craft are tethered following the bumper sequence. Most of the kinetic energy of the collision is first converted to magnetic field energy in the Y123, and then into heat via the creep mechanism. About 15% of the work done against magnetic forces during collision remains stored as magnetic energy after 1 hour. Experiments have also been conducted on the spatial range of the bumper force for arrays of HTS tiles. For a single HTS tile approx. 2 cm in diameter, the range of F(sub B) is approx. l cm. For a l m(exp 2) array the range of F(sub B) will be circa 50 cm.

Weinstein, Roy↗

NASA NTRS1995

Progress in HTS trapped field magnets: J(sub c), area, and applications

Progress in trapped field magnets is reported. Single YBCO grains with diameters of 2 cm are made in production quantities, while 3 cm, 4 1/2 cm and 6 cm diameters are being explored. For single grain tiles: J(sub c) is approximately 10,000 A/cm(exp 2) for melt textured grains; J(sub c) is approximately 40,000 A/cm2 for light ion irradiation; and J(sub c) is approximately 85,000 A/cm(exp 2) for heavy ion irradiation. Using 2 cm diameter tiles bombarded by light ions, we have fabricated a mini-magnet which trapped 2.25 Tesla at 77K, and 5.3 Tesla at 65K. A previous generation of tiles, 1 cm x 1 cm, was used to trap 7.0 Tesla at 55K. Unirradiated 2.0 cm tiles were used to provide 8 magnets for an axial gap generator, in a collaborative experiment with Emerson Electric Co. This generator delivered 100 Watts to a resistive load, at 2265 rpm. In this experiment activation of the TFMs was accomplished by a current pulse of 15 ms duration. Tiles have also been studied for application as a bumper-tether system for the soft docking of spacecraft. A method for optimizing tether forces, and mechanisms of energy dissipation are discussed. A bus bar was constructed by welding three crystals while melt-texturing, such that their a,b planes were parallel and interleaved. The bus bar, an area of approximately 2 cm(exp 2), carried a transport current of 1000 amps, the limit of the testing equipment available.

Weinstein, Roy↗

NASA NTRS1993

Quasipermanent magnets of high temperature superconductor - Temperature dependence

We report on persistent field in quasi-permanent magnets of high temperature superconductors. Magnets composed of irradiated Y(1+)Ba2Cu3O7 trapped field Bt = 1.52 T at 77 K and 1.9 T at lower temperature. However, the activation magnet limited Bt at lower temperature. We present data on Jc(H,T) for unirradiated materials, and calculate Bt at various T. Based upon data at 65 K, we calculate Bt in unirradiated single grains at 20 K and find that 5.2 T will be trapped for grain diameter d about 1.2 cm, and 7.9 T for d = 2.3 cm. Irradiated grains will trap four times these values.

Chen, In-Gann↗

NASA NTRS1992

Characterization of YBa2Cu3O7, including critical current density Jc, by trapped magnetic field

Spatial distributions of persistent magnetic field trapped by sintered and melt-textured ceramic-type high-temperature superconductor (HTS) samples have been studied. The trapped field can be reproduced by a model of the current consisting of two components: (1) a surface current Js and (2) a uniform volume current Jv. This Js + Jv model gives a satisfactory account of the spatial distribution of the magnetic field trapped by different types of HTS samples. The magnetic moment can be calculated, based on the Js + Jv model, and the result agrees well with that measured by standard vibrating sample magnetometer (VSM). As a consequence, Jc predicted by VSM methods agrees with Jc predicted from the Js + Jv model. The field mapping method described is also useful to reveal the granular structure of large HTS samples and regions of weak links.

Chen, In-Gann↗