Liu, Yingtao | Search NASA

DOE OSTI2021

Investigation of porous polydimethylsiloxane structures with tunable properties induced by the phase separation technique

This article reports the fabrication and characterization of porous polydimethylsiloxane (PDMS) structures developed by the solvent evaporationinduced phase separation technique. Here, ternary systems containing water/ tetrahydrofuran (THF)/PDMS with various concentrations are produced to form a stable solution. The porous PDMS structures are formed by removing the solvent (THF) and nonsolvent (water) phases during the stepping heat treatment procedure. The analytical ternary phase diagram is constructed based on the thermodynamic equilibrium state in the polymer solution to explain the stable/unstable formulations and the possible composition change path. The results show that the isolated pores with the adjustable pore size ranging from 330 to 1900 μm are obtained by tuning the water to the THF ratio. The mechanical properties of the porous PDMS structures are determined by conducting the tensile tests on the prepared dog bone-shaped specimens. A wide range of elastic modulus ranging between 0.49 and 1.05 MPa was achieved without affecting the density of the porous sample by adjusting the solvent and non-solvent content in the solution. It is shown that the flexibility of the porous structures can be improved by reducing the ratio of water to THF and decreasing the PDMS content. The porosity measurements reveal that the PDMS concentration is the major phase controlling the porosity of the structure, while the effect of water/THF is negligible.

42 ENGINEERING↗

DOE OSTI2020

Additive Manufacturing of Controlled Porous Elastomeric Nanocomposites for Enhanced Sensing Function

Sensors manufactured using piezoresistive elastomeric nanocomposites have a wide range of applications in many fields such as structural health monitoring, robotics, and biomedical industries. Additive manufacturing of these sensors, achieved using Direct Ink Writing (DIW), has provided numerous advantages including increased sensitivity and the fabrication of complex geometry. However, solid sensors manufactured either additively or using conventional methods, display a greater level of hysteresis, especially at strains higher than 10%, which limits their sensitivity. The solid sensors also display a greater level of piezoresistive relaxation where the resistance change with time either in a static or dynamic loading environment. Porosity can be introduced in the form of varying infill patterns and densities to reduce bulk material effects. In this paper, a lattice structure with four infill densities are investigated, and the samples are printed using a grid infill pattern. The fabricated samples are characterized using a scanning electron microscope (SEM) to validate the microstructural features and layer bonding. The pressure-sensing capability of each sensor is investigated using cyclic compression loading at various strain levels. Sensing results show that an increase in sensitivity, as well as a decrease in hysteresis with an increase in porosity, compared to solid samples (100% in-fill). The highest porosity was measured to be 62.3% with a corresponding 112% increase in the gauge factor compared to the solid bulk. These results indicate that introducing porosity using DIW is a sensible strategy to improve the piezoresistive performance of nanocomposites and to allow for the tunability of sensing capacity in pressure sensors

Sukati, Musa↗