Lolov, George | Search NASA

DOE OSTI2023

Porosity evolution in proton irradiated microfine-grained POCO graphite

This work investigated the porosity evolution of POCO ZXF-5Q graphite that has been irradiated by 340 kW, 120 GeV protons inside NT02 target system in Fermilab's NuMI beamline. This POCO graphite has undergone direct bulk dimensional swelling at low dose irradiation and its local microstructural change is still not well-understood during this process. In this work, the (sub-) micrometre scale porosity from six locations across proton beam fluence and temperature gradients have been studied using focused ion beam-scanning electron microscopy (FIB-SEM) tomography. Here, a deep learning-based tomographic image segmentation technique has been established and implemented for porosity segmentation and quantification. It has been found that there is a decrease in the total volumetric percentage of the porosity at proton beam centre (~ 8 – 8.4 vol.%), by comparing to un-irradiated POCO (~ 12 – 13vol.%) and to beam 2σ and 5σ radii (~ 12vol.%). This decrease in porosity volume percentage was found to be caused by the reduction in pores with volumes > 0.1 μm 3 induced by material bulk dimensional swelling at proton beam centre area. The porosity reduction in relation to dimensional change and irradiation creep was discussed among with other contributing factors, and further investigations through well-controlled irradiation experiment are still needed.

73 NUCLEAR PHYSICS AND RADIATION PHYSICS↗

DOE OSTI2023

A novel method for quantifying irradiation damage in nuclear graphite using Raman spectroscopy

Raman spectroscopy has long been used in studying irradiation damage in carbon/graphite materials. It is however unclear if the measurements from different types of materials are directly comparable. Further, decoupling the contribution from irradiation temperature and fluence to the total damage in nuclear graphite possessing irradiation damage gradient is currently not readily feasible as it requires a complete set of test reactor irradiation experiments over the relevant temperature and fluence range. A novel methodology has therefore been proposed and developed to quantify total irradiation damage evolution at crystal level based on graphite Raman G-band position shift. Specifically, G-band positions derived from a large number of spectra collected from the fractured surface of microfine-grained POCO ZXF-5Q graphite possessing proton irradiation damage gradient were plotted with open literature Raman data on HOPG, BEPO (AXGP graphite), PCEA and IG-110 graphite as a function of dpa. The total damage level within 2σ beam radius in this POCO graphite was estimated to be equivalent to ~2–5 dpa at ~350–370 °C. Derived G-band positions were then mapped to the three-stage amorphization trajectory model indicating beam centre area has entered the second stage, i.e., transitioning from nanocrystalline graphite into amorphous carbon. G-band position relative shift (ΔG) curve with a ‘turn-around’ peak as a function of total damage can be used for in-service lifetime prediction. Importantly, the developed methodology has the potential to ‘unify’ total damage levels across different grades of nuclear graphite caused by ion, neutron and proton irradiation at different temperatures.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗