NASA NTRS2011

Post STS-135 Evaluation of Main Flame Deflector Witness Materials

NASA and USA design engineers submitted witness materials from the solid rocket booster (SRB) main flame deflector for evaluation after the launch of STS-135. The following items were submitted for analysis: HY-80 steel witnes rods, 304 sta inles steel caps, and tungsten pistons. All of the items were photographed in order to document their condition after the launch of STS-135. The submitted samples were dimensionally measured in order to determine the amount of material lost during launch. Microstructural changes were observed in the HY-80 witness rod metallographic samples due to the heat of the launch.

Long, Victoria↗

NASA NTRS2011

Post STS-134 Evaluation of Main Flame Deflector Witness Materials

NASA and USA design engineers submitted witness materials from the solid rocket booster (SRB) main flame deflector for evaluation after the launch of STS-134. The following items were submitted for analysis: 1018 steel witness rods 304 stainless steel caps, tungsten pistons, and A-286 piston sleeves. All of the items were photographed in order to document their condition after the launch of STS-134. All of the items were dimensionally measured in order to determine the amount of material lost during launch. Microstructural changes were observed in the 1018 witness rod metallographic samples due to the heat of the launch

Long, Victoria↗

NASA NTRS2011

Post STS-133 Evaluation of Main Flame Deflector Witness Materials

NASA and USA Structures engineers submitted main flame deflector witness materials for evaluation after the launch of STS-133. The following items were submitted for analysis: HY-80 steel witness rods, 304 stainless steel caps, tungsten pistons, 17-4 precipitation hardened (PH) stainless steel and A-286 piston sleeves, Medtherm Corporation calorimeters, and Nanmac Corporation thermocouples. All of the items were photographed in order to document their condition after the launch of STS-133, and before they were reinstalled at the launch pad for future launches. The HY -80 witness rods, 304 stainless steel caps, and the piston sleeves were dimensionally measured in order to determine the amount of material lost during launch. Microstructural changes were observed in the HY-80 witness rod and 304 stainless steel cap metallographic samples due to the heat of the launch.

Long, Victoria↗

NASA NTRS2009

Failure Analysis of Main Flame Deflector Nelson Studs

NASA Structures engineers submitted two Nelson refractory studs from the main flame deflector at Launch Complex (LC) 39 A for analysis when they were observed to be missing a significant amount of material after launch. The damaged stud and an unused comparative stud were analyzed by macroscopic and microscopic examination along with metallographic evaluation of the microstructure. The stud lost material due to a combination of erosion and corrosion. Plain carbon steel readily forms an oxide layer in the coastal launch environment at Kennedy Space Center. The blast during a launch removes this brittle oxide layer, which then forms again post-launch, thereby further removing material. No indications of melting were observed.

Long, Victoria↗