NASA NTRS1981

Enhanced annealing of GaAs solar cell radiation damage

Solar cells are degraded by radiation damage in space. Investigations have been conducted concerning possibilities for annealing this radiation damage in GaAs solar cells, taking into account the conditions favoring such annealing. It has been found that continuous annealing as well as the combination of injection annealing with thermal annealing can lead to recovery from radiation damage under particularly favorable conditions in GaAs solar cells. The damage caused by both electrons and protons in GaAs solar cells can be substantially reduced by annealing at temperatures as low as 150 C, under appropriate conditions. This possibility makes the GaAs solar cells especially attractive for long space missions, or for missions in severe radiation environments. Attention is given to results concerning periodic thermal annealing, continuous annealing, and injection annealing combined with thermal annealing.

Loo, R.↗
NASA NTRS1979

Electron Radiation Damage of (alga) As-gaas Solar Cells

Solar cells (2 cm by 2 cm (AlGa) As-GaAs cells) were fabricated and then subjected to irradiation at normal incidence by electrons. The influence of junction depth and n-type buffer layer doping level on the cell's resistance to radiation damage was investigated. The study shows that (1) a 0.3 micrometer deep junction results in lower damage to the cells than does a 0.5 micrometer junction, and (2) lowering the n buffer layer doping density does not improve the radiation resistance of the cell. Rather, lowering the doping density decreases the solar cell's open circuit voltage. Some preliminary thermal annealing experiments in vacuum were performed on the (AlGa)As-GaAs solar cells damaged by 1-MeV electron irradiation. The results show that cell performance can be expected to partially recover at 200 C with more rapid and complete recovery occurring at higher temperature. For a 0.5hr anneal at 400 C, 90% of the initial power is recovered. The characteristics of the (AlGa)As-GaAs cells both before and after irradiation are described.

Loo, R.↗
NASA NTRS1979

Fabrication of high efficiency and radiation resistant GaAs solar cells

Systematic improvements in fabrication yield were obtained by appropriate control of the liquid phase epitaxial growth process, contact fabrication and surface preparation. To improve radiation hardness, the junction depth was decreased while overcoming the penalty in decreased solar cell efficiency which tends to go hand-in-hand with the reduction of junction depth in (AlGa) As-GaAs solar cells. Cells were made with an AMO efficiency of 18% and a junction depth of 0.5 micrometers, as compared to junction depths on the order of 1.0 micrometers. With respect to the damage caused by proton irradiation, the nature of the observed damage was correlated to the energy and penetration depth of the damaging protons.

Kamath, S.↗
NASA NTRS1979

High energy proton radiation damage to (AlGa)As-G aAs solar cells

Twelve 2 + 2 sq cm (AlGa)As-GaAs solar cells were fabricated and were subjected to 15.4 and 40 MeV of proton irradiation. The results showed that the GaAs cells degrade considerably less than do conventional and developmental K7 silicon cells. The detailed characteristics of the GaAs and silicon cells, both before and after irradiation, are described. Further optimization of the GaAs cells seems feasible, and areas for future work are suggested.

Loo, R.↗
NASA NTRS1979

Low energy proton radiation damage to (AlGa)As-GaAs solar cells

Twenty-seven 2 times 2 sq cm (AlGa)As-GaAs solar cells were fabricated and subjected to 50 keV, 100 keV, and 290 keV of proton irradiation along with eighteen high efficiency silicon solar cells. The results of the study further corroborate the advantages for space missions offered by GaAs cells over state of the art silicon cells. Thus, even though the GaAs cells showed greater degradation when irradiated by protons with energy less than 5 MeV, the solar cells were normally protected from these protons by the glass covers used in space arrays. The GaAs cells also offered superior end of life power capability compared with silicon. The change in the open circuit voltage, short circuit current, spectral response, and dark 1-5 characteristics after irradiation at each proton energy and fluence were found to be consistent with the explanation of the effect of the protons. Also dark 1-5 characteristics showed that a new recombination center dominates the current transport mechanism after irradiation.

Loo, R.↗
NASA NTRS1978

Electron and proton degradation in /AlGa/As-GaAs solar cells

Results on radiation damage in (AlGa)As-GaAs solar cells by 1 MeV electron fluences up to 10 to the 16th electrons/sq cm and by 15, 20, 30 and 40 MeV proton fluences up to 5 times 10 to the 11th protons/sq cm are presented. The damage is compared with data on state-of-the-art silicon cells which were irradiated along with the gallium arsenide cells. The theoretical expectation that the junction depth has to be kept relatively shallow, to minimize radiation damage has been verified experimentally. The damage to the GaAs cells as a function of irradiation, is correlated with the change in their spectral response and dark I-V characteristics. The effect of thermal annealing on the (AlGa)As-GaAs solar cells was also investigated. This data is used to predict further avenues of optimization of the GaAs cells.

Loo, R.↗
NASA NTRS1977

GaAs solar cell development

The motivation for developing GaAs solar cells is based on their superior efficiency when compared to silicon cells, their lower degradation with increasing temperature, and the expectation for better resistance to space radiation damage. The AMO efficiency of GaAs solar cells was calculated. A key consideration in the HRL technology is the production of GaAs cells of large area (greater than 4 sg cm) at a reasonable cost without sacrificing efficiency. An essential requirement for the successful fabrication of such cells is the ability to grow epitaxially a uniform layer of high quality GaAs (buffer layer) on state-of-the-art GaAs substrates, and to grow on this buffer layer the required than layer of (AlGa)As. A modified infinite melt liquid phase epitaxy (LPE) growth technique is detailed.

Knechtli, R. C.↗