Lorenzo-Martin, Cinta

DOE OSTI2023

The effect of current and lambda on white-etch-crack failures

White etching cracks (WECs) have been associated with premature failure of wind turbine roller bearings. Various drivers for the generation of WECs have been identified such as loading conditions, slip, steel quality, lubrication, hydrogen embrittlement, corrosion fatigue cracking, and stray electrical currents passing through the surface. Here, in this work, a benchtop test rig utilizing a three-ring-on-roller test configuration was used to investigate the effect of electrical current and operation in different lubricating regimes, defined by lambda (λ), on high-quality bearing steel samples tested in a commercially available power transmission EP gear lubricant. It was observed that there is an inverse correlation between the magnitude of electric current applied to the ring/ roller system and time-to-failure. Higher current magnitudes lead to shorter time-to-failure than lower current magnitudes, with macropitting as the main failure mode. Sub-surface investigation revealed the presence of WECs in all cases. For the same current magnitude, tests conducted in boundary and mixed lubrication regimes showed that time-to-failure increased as lambda increased, and the tests resulted in WEC related macropits, whereas tests conducted in near-hydrodynamic regime resulted in surface damage with no macropit. It was also noted that a shift toward near-hydrodynamic lubrication resulted in a distinct surface distress on the roller surface. Furthermore, there seems to be a transition in the mixed regime during which the surface distress occurred. The damage on the surface of the test samples resembled non-spatially, periodic, groove-like corrugations and, in some cases, crater-like depressions. Sub-surface imaging, performed by sequential sectioning, revealed the presence of WECs in all cases, and broad, branching cracks that were more prevalent under the more severe boundary conditions.

17 WIND ENERGY↗

DOE OSTI2023

Additive manufacturing process parameter determination for a new Fe-C-Cu alloy

As a potential replacement for stainless steel alloys commonly used to print parts with laser powder bed fusion, a new Cu precipitation strengthened ferrous alloy, with composition Fe-0.2C-6Cu (wt%), was recently developed. This material is Co- and Ni-free, printable, has mechanical properties comparable to that of high strength stainless steels (approximately 1300 MPa UTS), and is cost-advantaged relative to existing low-alloy steels for additive manufacturing of parts with complex shapes. To gain traction for broader application, optimal laser powder bed fusion (LPBF) processing conditions to produce nearly defect-free parts without compromising mechanical strength are needed. Here, an optimal processing window based upon laser speeds that achieve minimal porosity was quantified via comparisons of measured melt pool penetration, scan speeds, printed material density and laser beam energy density on a commercial LPBF unit operating at 350 W, 80 μm hatch spacing, and 50 μm layer thickness based upon optimal parameters for 17-4PH. Furthermore, the window is 300 to 500 mm/s to achieve >99.8 % dense Fe-0.2C-6Cu (wt%) specimens. Other defects such as burning, spatter, and lack of fusion were also avoided in this window. The window was validated with in-situ synchrotron X-ray imaging that enabled visualization of the vapor cavity, melting, and solidification during a single laser track scan on a miniature powder bed sample. In addition, in-situ infrared imaging provided temperature fields, cooling rate and solidification range, and confirmed minimal printing defects and spatter within the processing window.

36 MATERIALS SCIENCE↗