Characterization of an Ultra-High Temperature Ceramic Composite

Levine, Stanley R.↗

NASA NTRS2004

Ultra-high Temperature Ceramic Composites for Leading Edges, 2004

Ultrahigh temperature ceramics (UHTC) have performed unreliably due to material flaws and attachment design. These deficiencies are brought to the fore by the low fracture toughness and thermal shock resistance of the UHTC. If these deficiencies are overcome, we are still faced with poor oxidation resistance as a limitation on UHTC applicability to reusable launch vehicles. We have been addressing the deficiencies of UHTC for the past two years via a small task at GRC that is in the Airframe part of the Next Generation Launch Technology Program. Our focus is on composite constructions and functional grading to address the mechanical issues and on composition modification to address the oxidation issue. The progress on approaches to improving oxidation resistance by alloying and functional grading will be reported.

Levine, Stanley R.↗

NASA NTRS2004

Oxidation of High-temperature Alloy Wires in Dry Oxygen and Water Vapor

Small diameter wires (150 to 250 microns) of the high temperature alloys Haynes 188, Haynes 230, Haynes 230, Haynes 214, Kanthal Al and PM2000 were oxidized at 1204 C in dry oxygen or 50% H2O /50% O2 for 70 Hours. The oxidation kinetics were monitored using a thermogravimetric technique. Oxide phase composition and morphology of the oxidized wires were determined by X-ray diffraction,field emission scanning electron microscopy, and energy dispersive spectroscopy. The alumina-forming alloys, Kanthal Al and PM2000, out-performed the chromia-forming alloys under this conditions. PM2000 was recommended as the most promising candidate for advanced hybrid seal applications for space reentry control surface seals or hypersonic propulsion system seals. This study also demonstrated that thermogravimetric analysis of small diameter wires is a powerful technique for the study of oxide volatility, oxide adherence, and breakaway oxidation.

Opila, Elizabeth J.↗

NASA NTRS2003

Ultra-high Temperature Ceramic Composites for Leading Edges

Ultra-high temperature ceramics (UHTC) have performed unreliably due to material flaws and attachment design. These deficiencies are brought to the fore by the low fracture toughness and thermal shock resistance of UHTC. If these deficiencies are overcome, we are still faced with poor oxidation resistance as a limitation on UHT applicability to reusable launch vehicles. We have been addressing the deficiencies of UHTC for the past two years via a small task at GRC that is in the Airframe part of the Next Generation Launch Technology Program. Our focus is on composite constructions and functional grading to address the mechanical issues and on composition modification to address the oxidation issue. The progress on approaches to improving oxidation resistance by alloying and functional grading will be reported. In particular, initial tests of tantalum additions have shown potential for major improvement. Less promising results of additional tests at higher temperatures will be presented. Two fabrication approaches are being pursued to produce carbon fiber reinforced UHTC composites: prepregging and rigid perform infiltration. Fabrication procedures and microstructures for composites will be reported.

Levine, Stanley R.↗

NASA NTRS2003

Ultra-High Temperature Ceramic Composites for Leading Edges

Ultra-high temperature ceramics (UHTC) have performed unreliably due to material flaws and attachment design. These deficiencies are brought to the fore by the low fracture toughness and thermal shock resistance of UHTC. If these deficiencies are overcome, we are still faced with poor oxidation resistance as a limitation on UHTC applicability to reusable launch vehicles. We have been addressing the deficiencies of UHTC for the past two years via a small task at GRC that is in the Airframe part of the Next Generation Launch Technology Program. Our focus is on composite constructions and functional grading to address the mechanical issues and on composition modification to address the oxidation issue. The progress on approaches to improving oxidation resistance by alloying and functional grading will be reported. In particular, initial tests of tantalum additions have shown potential for major improvement. Results for additional tests at higher temperatures will be presented. These oxidation improvements are being incorporated in the composites approaches. Two fabrication approaches are being persued to produce carbon fiber reinforced UHTC composites: prepregging and rigid perform infiltration. Fabrication procedures, microstructures, and initial mechanical property and oxidation results for composites will be reported.

Levine, Stanley R.↗

NASA NTRS2003

Characterization of a Ultra-high Temperature Ceramic Composite

Ultra-high temperature ceramics (UHTC) are of interest for hypersonic vehicle leading edge applications. Monolithic UHTCs are of concern because of their low fracture toughness and brittle behavior. UHTC composites (UHTCC) are being investigated as a possible approach to overcome these deficiencies. In this study a small sample of a UHTCC was evaluated by limited mechanical property tests, furnace oxidation exposures, and oxidation exposures in a flowing environment. The composite was prepared from a carbon fiber perform using ceramic particulates and a preceramic polymer. The as-received composite plate was non-uniform from front to back surface. Plate dimensions were 150 x 150 x 6 mm. The back surface had a fibrous, uniform appearance; XRD analysis revealed the presence of Sic and C. The front surface was smooth and non-uniform in appearance with evidence of a coarse grain structure produced by a liquid phase; XRD analysis revealed the presence of HfB2. Microcracks were present throughout the thickness as one might expect from a carbon fiber reinforced composite with attendant large thermal expansion mismatch between the matrix phases and the fibers. The HfB2 phase on the front surface was comparable in thickness to a fiber ply or about 0.6 mm, and surface microcracks were evident. Limited four point flexural tests were carried out at span to depth ratios of approximately 14 and 16 with markedly different results. Tests were run with the front or the back surface in tension. At the shorter span to depth failures occurred under a loading pin for both orientations. At a span to depth of 16 failures occurred in the center of the span with fracture clearly initiating from a tensile failure. Ultimate flexural strength, strain at ultimate stress, stress and strain at deviation from linear elastic behavior are reported. Strains at ultimate stress ranged from about 0.6 to 0.7 % for the back surface in tension, and 0.4 to 0.6 for the front surface in tension. At constant span to depth the strain at ultimate stress was about 0.2% greater for the back surface in tension and the ultimate strength was also higher. Strengths were in line with predictions from theory. Furnace oxidation studies were carried out at 1627 and 1927OC in a static furnace environment using ten minute cycles and one, five, and ten cycles. Limited oxidation studies were also carried out in a flowing oxyacetylene torch environment. Specimens were photographed, and weight and dimensional changes were determined. XRD and SEM characterizations were performed. Weight losses were attributed primarily to carbon fiber oxidation. The composite survived the torch test with little visible distress. Further details will be determined once metallographic studies are completed.

Levine, Stanley R.↗