DOE OSTI2021

Czochralski growth and characterization of the multicomponent garnet (Lu 1/4 Yb 1/4 Y 1/4 Gd 1/4 ) 3 Al 5 O 12

This work demonstrates the potential for practical scalable growth of complex garnets and evaluates the implications of a multicomponent composition in the optical quality and elemental distribution of a Czochralski-grown crystal. Furthermore, our experimental approach was designed to elucidate the relation between a complex garnet composition ( Lu 1 / 4 Yb 1 / 4 Y 1 / 4 Gd 1 / 4 ) 3 Al 5 O 12 , crystal growth parameters, crystal structural, and elemental homogeneity. Our hypothesis is that combining multiple rare earths (REs) that will fractionally occupy the dodecahedral site in the aluminum garnet structure will result in a stable, single garnet compound that can be grown by the Czochralski method. Single-crystal and powder x-ray diffraction indicated a single garnet phase with an increasing unit cell volume from seed to tail. In addition, we propose that the pattern of elemental segregation will be based on the deviation of the ionic radius of each constituent RE from the average RE ionic radius of the multicomponent garnet. Electron probe microanalysis revealed that ions that are smaller than that average ( Lu 3 + and Yb 3 + ) are preferentially incorporated in the crystal, while elements that are larger than that average ( Gd 3 + ) are rejected. The ionic radius of Y 3 + is close to that average and yttrium segregation was minimal. The concentrations of the four REs are closer to stoichiometric on the tail end of the boule. Scanning electron microscopy and energy-dispersive x-ray spectroscopy analysis reveal Gd-rich inclusions with eutectic microstructures in the tail end of the boule.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Crystal Growth and Elemental Homogeneity of the Multicomponent Rare-Earth Garnet (Lu 1/6 Y 1/6 Ho 1/6 Dy 1/6 Tb 1/6 Gd 1/6 ) 3 Al 5 O 12

We report high-entropy aluminum garnets were grown as bulk single crystals using the micro-pulling-down method, taking the synthesis of complex ceramics a step further from the conventional preparation of polycrystalline materials. We studied the effects of growth parameters on the elemental distribution in high optical quality crystals of (Lu 1/6 Y 1/6 Ho 1/6 Dy 1/6 Tb 1/6 Gd 1/6 ) 3 Al 5 O 12 containing six cations (yttrium and rare-earths) taken in equimolar amounts. A single garnet structure was confirmed by powder X-ray diffraction. Electron microprobe measurements were obtained to correlate the radial distribution of rare-earth elements with pulling rates and molten zone height. The nature of the elemental distribution in the radial direction was associated with ionic radius: smaller rare-earths concentrated in the center of the crystal, while larger rare-earths segregated toward the outer edge of the cylindrical crystal. Faster pulling rates led to a flattening of the concentration profiles toward the nominal concentration, promoting a more homogeneous radial elemental distribution, while varying the molten zone height did not have a significant effect. The demonstrated success with crystal growth enables the practical availability of single crystals of multicomponent aluminum garnets for further discovery of new phenomena and applications.

36 MATERIALS SCIENCE↗

DOE OSTI2019

Solid–state synthesis of multicomponent equiatomic rare–earth oxides

Phase formation in multicomponent rare–earth oxides is determined by a combination of composition, sintering atmosphere, and cooling rate. Polycrystalline ceramics comprising various combinations of Ce, Gd, La, Nd, Pr, Sm, and Y oxides in equiatomic proportions were synthesized using solid–state sintering. The effects of composition, sintering atmosphere, and cooling rate on phase formation were investigated. Single cubic or monoclinic structures were obtained with a slow cooling of 3.3°C/min, confirming that rare–earth oxides follow a different structure stabilization process than transition metal high–entropy oxides. In an oxidizing atmosphere, both Ce and Pr induce a cubic structure, while only Ce plays that role in an inert or reducing atmosphere. Samples without Ce or Pr develop a single monoclinic structure. The structures formed at initial synthesis may be converted to a different one, when the ceramics are annealed in an additional atmosphere. Phase evolution of a five–cation composition was also studied as a function of sintering temperature. In conclusion, the binary oxides used as raw materials completely dissolve into a single cubic structure at 1450°C in air.

36 MATERIALS SCIENCE↗