Lovejoy, Andrew E.

Publications and source records attributed to Lovejoy, Andrew E..

At least 19 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS2020

Static Loads Testing of a High Aspect Ratio Tow-Steered Wingbox

Static loads testing was performed on a 39-foot, high-aspect-ratio wingbox comprising carbon fiber tow-steered wing skins that were tailored for aircraft fuel efficiency under aeroelastic loads. The test article was designated the Passive Aeroelastic Tailored (PAT) wing. To date, the PAT wing, which has an aspect ratio of 13.5, is the largest wingbox designed and built to employ variably oriented carbon fibers along the span of the wing. During testing, distributed point loads were applied to the wingbox to simulate both -1g and 2.5g maneuver loads. To determine the wingbox’s flexural axis location, individual point loads were applied. The global response of the wing (displacement and rotation measurements) showed similar trends compared to the finite element model predictions, though discrepancies of up to 17% were observed when comparing actual values between model and test. It was concluded that the boundary conditions and nonstructural features of the wingbox were the likely cause of the inconsistencies. The local response of the wingbox (strain measurements), which was much less affected by factors unrelated to tow-steering, exhibited good agreement with the model predictions, validating the modelling techniques employed for tow-steered composites.

Tow-steered composites↗
NASA NTRS2019

Characterization of IM7/8552 Thin-Ply and Hybrid Thin-Ply Composites

Composite materials have increasingly been used for aerospace applications due to improved performance and reduced weight compared to their metallic counterparts. Inclusion of thin-ply material, plies with cured thickness half or less than standard composites, have potential to improve performance and reduce structural weight. Limited characterization of thin-ply IM7/8552 material in 30 and 70 grams per square meter fiber areal weights has been carried out using a series of selected American Society for Testing and Materials (ASTM) tests. Tests included unnotched tension, unnotched compression, v-notched rail shear, open-hole tension, and open-hole compression. Unidirectional, cross-ply, quasiisotropic and hybrid hard laminates were included in the study, and were compared to standard-ply laminates. Properties compared include fiber volume, laminate moduli, and failure strength, with failure modes also being examined. The thin-ply specimens exhibited similar or superior performance to standard ply laminates in many of the cases compared. Improvements in strength for laminates containing thin-ply material were seen for unidirectional laminates under unnotched tension, quasi-isotropic laminates under unnotched tension and compression, and hard laminates under open hole tension. Additional investigation is required to determine appropriate ply stacking rules for hybrids of thin and standard plies to avoid undesirable failure modes such as axial splitting. However, the observed performance improvements demonstrated by the conducted ASTM tests of hybrid thin-ply hard laminates could have benefits for improved structural weight in aircraft.

Lovejoy, Andrew E.↗
NASA NTRS2019

Potential Weight Benefits of IM7/8552 Hybrid Thin-Ply Composites for Aircraft Structures

Composite materials have increasingly been used for aerospace applications due to improved performance and reduced weight compared to their metallic counterparts. Inclusion of thin-ply material, plies with cured thickness half or less than standard-ply composites, have potential to improve performance and reduce structural weight further. The effect of thin-ply material on the weight of aircraft structure was investigated by examining wing cover weight reduction. To minimize the effects on manufacturing due to using thin plies, hybrid laminates were examined that used thin ±45-degree plies to replace their standard-ply counterparts in laminates. Compression after impact (CAI) tests were conducted to examine the possible weight savings that could be gained by increasing the design allowables that were used to size the wing upper cover of a semi-span test article. A large increase in CAI strength was observed for quasi-isotropic hybrid laminates, whereas less improvement was seen for hard hybrid laminates such as found in the wing cover. For laminates design by CAI strength, weight savings of about 13% were found using the hybrid hard laminates compared to the standard-ply laminates. Whether similar weight savings could be expected for structure sized using tension after impact allowables will have to be investigated further. Notched specimens were tested to examine possible weight savings using hybrid laminates in regions that are sized using discrete source damage requirements. As expected, the hybrid laminate had marginal improvements over the standard-ply laminate for compression with a notch present. The hybrid laminate, however, exhibited about 20% lower strength than the standard-ply laminate counterpart for tension with a notch. The failure mode of the hybrid specimens was a brittle, self-similar crack, which differs from the standard-ply specimens that failed by significant amounts of delamination and fiber splitting. In light of the apparent reduction in notched tensile strength, additional investigation is required to assess the use of hybrid laminates for areas containing discrete source damage, and their effect on weight of such regions.

Lovejoy, Andrew E.↗
NASA NTRS2018

Buckling Response of a Large-Scale, Seamless, Orthogrid-Stiffened Metallic Cylinder

Results from the buckling test of a compression-loaded 8-ft-diameter seamless (i.e., without manufacturing joints), orthogrid-stiffened metallic cylinder are presented. This test was used to assess the buckling response and imperfection sensitivity characteristics of a seamless cylinder. In addition, the test article and test served as a technology demonstration to show the application of the flow forming manufacturing process to build more efficient buckling-critical structures by eliminating the welded joints that are traditionally used in the manufacturing of large metallic barrels. Pretest predictions of the cylinder buckling response were obtained using a finite-element model that included measured geometric imperfections. The buckling load predicted using this model was 697,000 lb, and the test article buckled at 743,000 lb (6% higher). After the test, the model was revised to account for measured variations in skin and stiffener geometry, nonuniform loading, and material properties. The revised model predicted a buckling load of 754,000 lb, which is within 1.5% of the tested buckling load. In addition, it was determined that the load carrying capability of the seamless cylinder is approximately 28% greater than a corresponding cylinder with welded joints.

Rudd, Michelle Tillotson↗
NASA NTRS2018

Test and Analysis of Full-Scale 27.5-Foot-Diameter Stiffened Metallic Launch Vehicle Cylinders

The Shell Buckling Knockdown Factor Project (SBKF) was established with the goal of developing improved (i.e., less-conservative, more robust) shell buckling knockdown factors (KDFs) for modern launch-vehicle structures. To this end, SBKF has engaged in several activities to support the development, validation, and implementation of the new design factors, including subscale and full-scale structural testing. Tests on eight different subscale, 8-foot-diameter, integrally stiffened aluminum-lithium 2195 (Al-Li 2195) cylinders were conducted in order to obtain the majority of the required validation data. In addition, two full-scale, 27.5-foot-diameter, Al-Li 2195, integrally stiffened cylinders were tested to provide additional validation data and to determine structural scaling trends. Presented herein are the details of a recent analysis model development and test and analysis correlation effort on the full-scale test articles. The effects of selected modeling assumptions and approaches are discussed, and results from a modeling sensitivity study are presented. It was found that simplified finite element models, that assume nominal test article geometry and material properties, can predict the overall response characteristics well. However, several discrepancies in the test and analysis results were observed. A sensitivity study was performed to determine the effects of several modeling assumptions and address the observed discrepancies. The results from the study indicated that the evolution of local skin pocket buckling and the presence of residual stresses due to the manufacturing process can have a significant influence on the predicted buckling response of the cylinders considered.

Lovejoy, Andrew E.↗
NASA NTRS2016

Design and Use of a Guided Weight Impactor to Impart Barely Visible Impact Damage

Aircraft structure is required to demonstrate satisfaction of the FAR requirements for Category 1, such as barely visible impact damage (BVID). Typical aircraft structure is impacted using a dropped weight impactor, which can impart BVID to the top surface of the structure. A recent test of a multi-bay box (MBB) composite test article, that represents an 80% scale center section of a hybrid wing body aircraft, required impact to be in a direction other than vertical from above, but still in an direction that is normal to the surface. This requirement eliminated the use of the conventional dropped weight impactor. Therefore, a design study was undertaken to determine the most effective way to efficiently and reliably impact the MBB. The chosen design was a guided weight impactor that is gravity driven. This paper describes the design of the guided weight impactor, and presents the results of its use for imparting BVID to the MBB. The guided weight impactor was seen to be a very reliable method to impart BVID, while at the same time having the capability to be highly configurable for use on other aircraft structure that is impacted at a variety of impact energies and from a variety of directions.

Lovejoy, Andrew E.↗
NASA NTRS2016

The Behavior of a Stitched Composite Large-Scale Multi-Bay Pressure Box

NASA has created the Environmentally Responsible Aviation (ERA) Project to develop technologies to reduce impact of aviation on the environment. A critical aspect of this pursuit is the development of a lighter, more robust airframe to enable the introduction of unconventional aircraft configurations. NASA and The Boeing Company have worked together to develop a structural concept that is lightweight and an advancement beyond state-of-the-art composite structures. The Pultruded Rod Stitched Efficient Unitized Structure (PRSEUS) is an integrally stiffened panel design where elements are stitched together and designed to maintain residual load-carrying capabilities under a variety of damage scenarios. With the PRSEUS concept, through-the-thickness stitches are applied through dry fabric prior to resin infusion, and replace fasteners throughout each integral panel. Through-the-thickness reinforcement at discontinuities, such as along flange edges, has been shown to suppress delamination and turn cracks, which expands the design space and leads to lighter designs. The pultruded rod provides stiffening away from the more vulnerable skin surface and improves bending stiffness. A series of building block tests were evaluated to explore the fundamental assumptions related to the capability and advantages of PRSEUS panels. The final step in the building block series of tests is an 80%-scale pressure box representing a portion of the center section of a Hybrid Wing Body (HWB) transport aircraft. The testing of this test article under maneuver and internal pressure loading conditions is the subject of this paper. The experimental evaluation of this article, along with the other building block tests and the accompanying analyses, has demonstrated the viability of a PRSEUS center body for the HWB vehicle. Additionally, much of the development effort is also applicable to traditional tube-and-wing aircraft, advanced aircraft configurations, and other structures where weight and through-the-thickness strength are design considerations.

Jegley, Dawn C.↗
NASA NTRS2016

Finite Element Analysis and Test Results Comparison for the Hybrid Wing Body Center Section Test Article

This report documents the comparison of test measurements and predictive finite element analysis results for a hybrid wing body center section test article. The testing and analysis efforts were part of the Airframe Technology subproject within the NASA Environmentally Responsible Aviation project. Test results include full field displacement measurements obtained from digital image correlation systems and discrete strain measurements obtained using both unidirectional and rosette resistive gauges. Most significant results are presented for the critical five load cases exercised during the test. Final test to failure after inflicting severe damage to the test article is also documented. Overall, good comparison between predicted and actual behavior of the test article is found.

Przekop, Adam↗
NASA NTRS2016

T-Cap Pull-Off and Bending Behavior for Stitched Structure

The Pultruded Rod Stitched Efficient Unitized Structure (PRSEUS) is a structural concept that was developed by The Boeing Company to address the complex structural design aspects associated with a pressurized hybrid wing body aircraft configuration. An important design feature required for assembly is the integrally stitched T-cap, which provides connectivity of the corner (orthogonal) joint between adjacent panels. A series of tests were conducted on T-cap test articles, with and without a rod stiffener penetrating the T-cap web, under tension (pull-off) and bending loads. Three designs were tested, including the baseline design used in largescale test articles. The baseline had only the manufacturing stitch row adjacent to the fillet at the base of the T-cap web. Two new designs added stitching rows to the T-cap web at either 0.5- or 1.0-inch spacing along the height of the web. Testing was conducted at NASA Langley Research Center to determine the behavior of the T-cap region resulting from the applied loading. Results show that stitching arrests the initial delamination failures so that the maximum strength capability exceeds the load at which the initial delaminations develop. However, it was seen that the added web stitching had very little effect on the initial delamination failure load, but actually decreased the initial delamination failure load for tension loading of test articles without a stiffener passing through the web. Additionally, the added web stitching only increased the maximum load capability by between 1% and 12.5%. The presence of the stiffener, however, did increase the initial and maximum loads for both tension and bending loading as compared to the stringerless baseline design. Based on the results of the few samples tested, the additional stitching in the T-cap web showed little advantage over the baseline design in terms of structural failure at the T-cap web/skin junction for the current test articles.

Lovejoy, Andrew E.↗
NASA NTRS2016

Imparting Barely Visible Impact Damage to a Stitched Composite Large-Scale Pressure Box

The Pultruded Rod Stitched Efficient Unitized Structure (PRSEUS) is a concept that was developed by The Boeing Company to address the complex structural design aspects associated with a pressurized hybrid wing body (HWB) aircraft configuration, which has been a focus of the NASA Environmentally Responsible Aviation Project. The NASA-Boeing structural development for the HWB aircraft culminated in testing of the multi-bay box, which is an 80%-scale representation of the pressurized center-body section. This structure was tested in the NASA Langley Research Center Combined Loads Test System facility. As part of this testing, barely visible impact damage was imparted to the interior and exterior of the test article to demonstrate compliance with a condition representative of the requirements for Category 1 damaged composite structure as defined by the Federal Aviation Regulations. Interior impacts were imparted using an existing spring-loaded impactor, while the exterior impacts were imparted using a newly designed, gravity-driven impactor. This paper describes the impacts to the test article, and the design of the gravitydriven guided-weight impactor. The guided-weight impactor proved to be a very reliable method to impart barely visible impact damage in locations which are not easily accessible for a traditional drop-weight impactor, while at the same time having the capability to be highly configurable for use on other aircraft structures.

Lovejoy, Andrew E.↗
NASA NTRS2016

Testing and Analysis of a Composite Non-Cylindrical Aircraft Fuselage Structure : Severe Damage - Part II

The Environmentally Responsible Aviation Project aimed to develop aircraft technologies enabling significant fuel burn and community noise reductions. Small incremental changes to the conventional metallic alloy-based 'tube and wing' configuration were not sufficient to achieve the desired metrics. One airframe concept identified by the project as having the potential to dramatically improve aircraft performance was a composite-based hybrid wing body configuration. Such a concept, however, presented inherent challenges stemming from, among other factors, the necessity to transfer wing loads through the entire center fuselage section which accommodates a pressurized cabin confined by flat or nearly flat panels. This paper discusses a finite element analysis and the testing of a large-scale hybrid wing body center section structure developed and constructed to demonstrate that the Pultruded Rod Stitched Efficient Unitized Structure concept can meet these challenging demands of the next generation airframes. Part II of the paper considers the final test to failure of the test article in the presence of an intentionally inflicted severe discrete source damage under the wing up-bending loading condition. Finite element analysis results are compared with measurements acquired during the test and demonstrate that the hybrid wing body test article was able to redistribute and support the required design loads in a severely damaged condition.

Przekop, Adam↗
NASA NTRS2016

Testing and Analysis of a Composite Non-Cylindrical Aircraft Fuselage Structure: Ultimate Design Loads - Part 1

The Environmentally Responsible Aviation Project aimed to develop aircraft technologies enabling significant fuel burn and community noise reductions. Small incremental changes to the conventional metallic alloy-based 'tube and wing' configuration were not sufficient to achieve the desired metrics. One airframe concept identified by the project as having the potential to dramatically improve aircraft performance was a composite-based hybrid wing body configuration. Such a concept, however, presented inherent challenges stemming from, among other factors, the necessity to transfer wing loads through the entire center fuselage section which accommodates a pressurized cabin confined by flat or nearly flat panels. This paper discusses finite element analysis and testing of a large-scale hybrid wing body center section structure developed and constructed to demonstrate that the Pultruded Rod Stitched Efficient Unitized Structure concept can meet these challenging demands of the next generation airframes. Part I of the paper considers the five most critical load conditions, which are internal pressure only and positive and negative g-loads with and without internal pressure. Analysis results are compared with measurements acquired during testing. Performance of the test article is found to be closely aligned with predictions and, consequently, able to support the hybrid wing body design loads in pristine and barely visible impact damage conditions.

Przekop, Adam↗
NASA NTRS2016

Tension and Bending Testing of an Integral T-Cap for Stitched Composite Airframe Joints

The Pultruded Rod Stitched Efficient Unitized Structure (PRSEUS) is a structural concept that was developed by The Boeing Company to address the complex structural design aspects associated with a pressurized hybrid wing body aircraft configuration. An important design feature required for assembly is the integrally stitched T-cap, which provides connectivity of the corner (orthogonal) joint between adjacent panels. A series of tests were conducted on T-cap test articles, with and without a rod stiffener penetrating the T-cap web, under tension (pull-off) and bending loads. Three designs were tested, including the baseline design used in large-scale test articles. The baseline had only the manufacturing stitch row adjacent to the fillet at the base of the T-cap web. Two new designs added stitching rows to the T-cap web at either 0.5- or 1.0-inch spacing along the height of the web. Testing was conducted at NASA Langley Research Center to determine the behavior of the T-cap region resulting from the applied loading. Results show that stitching arrests the initial delamination failures so that the maximum strength capability exceeds the load at which the initial delaminations develop. However, it was seen that the added web stitching had very little effect on the initial delamination failure load, but actually decreased the initial delamination failure load for tension loading of test articles without a stiffener passing through the web. Additionally, the added web stitching only increased the maximum load capability by between 1% and 12.5%. The presence of the stiffener, however, did increase the initial and maximum loads for both tension and bending loading as compared to the stringerless baseline design. Based on the results of the few samples tested, the additional stitching in the T-cap web showed little advantage over the baseline design in terms of structural failure at the T-cap web/skin junction for the current test articles.

Lovejoy, Andrew E.↗
NASA NTRS2015

Nonlinear Analysis and Preliminary Testing Results of a Hybrid Wing Body Center Section Test Article

A large test article was recently designed, analyzed, fabricated, and successfully tested up to the representative design ultimate loads to demonstrate that stiffened composite panels with through-the-thickness reinforcement are a viable option for the next generation large transport category aircraft, including non-conventional configurations such as the hybrid wing body. This paper focuses on finite element analysis and test data correlation of the hybrid wing body center section test article under mechanical, pressure and combined load conditions. Good agreement between predictive nonlinear finite element analysis and test data is found. Results indicate that a geometrically nonlinear analysis is needed to accurately capture the behavior of the non-circular pressurized and highly-stressed structure when the design approach permits local buckling.

Przekop, Adam↗
NASA NTRS2015

Preliminary Weight Savings Estimate for a Commercial Transport Wing Using Rod-Stiffened Stitched Composite Technology

A structural concept called pultruded rod stitched efficient unitized structure (PRSEUS) was developed by the Boeing Company to address the complex structural design aspects associated with a pressurized hybrid wing body (HWB) aircraft configuration. While PRSEUS was an enabling technology for the pressurized HWB structure, limited investigation of PRSEUS for other aircraft structures, such as circular fuselages and wings, has been done. Therefore, a study was undertaken to investigate the potential weight savings afforded by using the PRSEUS concept for a commercial transport wing. The study applied PRSEUS to the Advanced Subsonic Technology (AST) Program composite semi-span test article, which was sized using three load cases. The initial PRSEUS design was developed by matching cross-sectional stiffnesses for each stringer/skin combination within the wing covers, then the design was modified to ensure that the PRSEUS design satisfied the design criteria. It was found that the PRSEUS wing design exhibited weight savings over the blade-stiffened composite AST Program wing of nearly 9%, and a weight savings of 49% and 29% for the lower and upper covers, respectively, compared to an equivalent metallic wing.

Lovejoy, Andrew E.↗
NASA NTRS2014

Analysis and Testing of a Metallic Repair Applicable to Pressurized Composite Aircraft Structure

Development of repair technology is vital to the long-term application of new structural concepts on aircraft structure. The design, analysis, and testing of a repair concept applicable to a stiffened composite panel based on the Pultruded Rod Stitched Efficient Unitized Structure was recently completed. The damage scenario considered was a mid-bay to mid-bay saw-cut with a severed stiffener, flange, and skin. A bolted metallic repair was selected so that it could be easily applied in the operational environment. The present work describes results obtained from tension and pressure panel tests conducted to validate both the repair concept and finite element analysis techniques used in the design effort. Simulation and experimental strain and displacement results show good correlation, indicating that the finite element modeling techniques applied in the effort are an appropriate compromise between required fidelity and computational effort. Static tests under tension and pressure loadings proved that the proposed repair concept is capable of sustaining load levels that are higher than those resulting from the current working stress allowables. Furthermore, the pressure repair panel was subjected to 55,000 pressure load cycles to verify that the design can withstand a life cycle representative for a transport category aircraft. These findings enable upward revision of the stress allowables that had been kept at an overly-conservative level due to concerns associated with repairability of the panels. This conclusion enables more weight efficient structural designs utilizing the composite concept under investigation.

Przekop, Adam↗
NASA NTRS2014

The Use of the STAGS Finite Element Code in Stitched Structures Development

In the last 30 years NASA has worked in collaboration with industry to develop enabling technologies needed to make aircraft more fuel-efficient and more affordable. The focus on the airframe has been to reduce weight, improve damage tolerance and better understand structural behavior under realistic flight and ground loading conditions. Stitched structure is a technology that can address the weight savings, cost reduction, and damage tolerance goals, but only if it is supported by accurate analytical techniques. Development of stitched technology began in the 1990's as a partnership between NASA and Boeing (McDonnell Douglas at the time) under the Advanced Composites Technology Program and has continued under various titles and programs and into the Environmentally Responsible Aviation Project today. These programs contained development efforts involving manufacturing development, design, detailed analysis, and testing. Each phase of development, from coupons to large aircraft components was supported by detailed analysis to prove that the behavior of these structures was well-understood and predictable. The Structural Analysis of General Shells (STAGS) computer code was a critical tool used in the development of many stitched structures. As a key developer of STAGS, Charles Rankin's contribution to the programs was quite significant. Key features of STAGS used in these analyses and discussed in this paper include its accurate nonlinear and post-buckling capabilities, its ability to predict damage growth, and the use of Lagrange constraints and follower forces.

Jegley, Dawn C.↗