Insights into elevated temperature tensile deformation mechanisms and kink banding in additively manufactured tungsten
Additive manufacturing (AM) potentially enables fabrication and repair of plasma facing components (PFCs) of tungsten. However, deformation mechanisms in AM-fabricated tungsten under service-relevant thermomechanical conditions remain unknown majorly due to challenges in achieving crack-free W. This study reveals the deformation mechanisms operative under tension at 800 °C and 1200 °C in the electron beam melting powder bed fusion (EBM-PBF) fabricated W. Textured columnar grains with mixed <001 >/<111 >|| build-direction were observed. Strong anisotropy in tensile properties persisted across test temperatures, and all specimens exhibited extensive deformation-induced banding phenomena. Grain boundary character analysis of the deformed specimens indicated that these deformation bands were kink bands with tilt grain boundaries prominently present at the band-matrix interface. Interestingly, the material within the kink bands rotated toward higher resolved shear stress, providing insights into the origins of kink band formation in body-centered cubic refractory metals. Intragranular misorientation axis analysis revealed that plasticity was dominated by {110} <111 > slip at 800 °C, whereas additional (213)[11̄1] and (112)[11̄1] slip systems activated at 1200 °C. A dense low-angle boundary networks observed near fractured surface indicated the onset of dynamic recrystallization. Results reveal plasticity governing mechanisms in AM-fabricated W under power plant-relevant conditions, and provide insights into kink band attributes in refractory metals.