NASA NTRS1987

The effect of V2O5 on the growth and properties of Bi-YIG

The effect of V2O5 additions to PbO-Bi2O3 flux was investigated with respect to the properties of Bi-YIG epitaxial films for magnetic bubble devices. The Bi content of the films (including an estimated 10 percent Pt(2+) were calculated from Faraday rotation measurements. For films grown at constant supercooling, the Bi content increased by 60 percent as the V2O5 content of the flux was increased from 0 to 9 mol pct. Lattice constant data were shown to agree with measured Bi and Ca-Si contents. The growth-induced magnetic anisotropy increased proportionally to the Bi content and could be fairly represented by a model; however, the coefficients of the model vary widely between data sets for different melt compositions.

Luther, L. C.↗

NASA NTRS1987

Rare-earth substitution in (BiYCa)3(FeSiGe)5O12 bubble films

The substitution of Y by Sm, Tb, Gd, and Ho in (BiYCa)3 FeSiGe)5O12 bubble garnet is shown to have large effects on the growth-induced anisotropy (GIA). The presently accepted film composition intended for 6-or 8-micron-period bubble memory devices demands partial substitution of Y by Gd and Ho. However, comparing films grown under the same growth conditions, it is observed that YGdHoBilG films posess less (GIA) than their Gd, Ho-free counterparts. Thus, to satisfy (GIA) requirements, the supercooling during growth must be increased by 20 K to 80 K with undesirable effects on defect densities. A new film composition containing Sm, Tb, and Gd has been formulated to satisfy all known material property specifications for 6- or 8-micron-period memory devices. It can be grown with only 45-50 K supercooling.

Luther, L. C.↗

NASA NTRS1986

Garnet melt viscosity, surface tension and drainage

Good surface morphology and layer uniformity of LPE-grown Bi YIG films are favored by fast melt removal after growth. Three flux modifying oxides: MoO3, V2O3, and WO3 are compared with respect to their effect on viscosity, surface tension and melt drainage. All three oxides increased the viscosities of Bi-garnet melts, but the viscosities and drainage times of V2O3 and MoO3 modified melts were smaller than those of WO3 modified melts. The liquid-gas surface tension was found to be temperature independent. The drainage process was strongly temperature dependent, 40 to 60 kcal/mol, whereas the viscosities of melts had activation energies of 11 to 16 kcal/mol. Contact angles of 16 + or - 2 deg were measured on frozen melt drops.