DOE OSTI2021

Developing a Low Cost, High Volume and Scalable Manufacturing Technology for Undoped and Heavily P-Type Doped CdTe Feedstock Materials (Final Report)

The goal of this project was to establish a cost-effective and scalable production approach of feedstock (CdTe and Cd-Se-Te) for the solar industry, with the material properties necessary to improve performance and reduce costs. The primary focus was to develop a CdTe synthesis and growth process that pushed the p-type doping of CdTe to previously unattainable levels, while creating a path to scalable production. In our approach, the first step was bulk CdTe growth doped with Group V dopants (P, As, and Sb) using the Modified Vertical Bridgman (MVB) and high Pressure Bridgman (HPB) techniques, and the second step was examination of films deposited by Close-Spaced Sublimation (CSS) and Vapor Transport Deposition (VTD) using this specialized feedstock.

14 SOLAR ENERGY↗
DOE OSTI2020

Arsenic Doping of Polycrystalline CdSeTe Devices for Microsecond Life-times with High Carrier Concentrations

We report seminal advances in fabrication and understanding of group V (As) doped thin-film polycrystalline CdTe-based solar cells. The devices are fabricated using a novel approach, by sublimating layers of CdSeTe and CdSeTe:As. This new method allowed us to achieve minority carrier lifetime of over 1 μs, carrier concentration of more than 5x1015 cc-1 and external radiative efficiency of over 2% in a device configuration. We find an increase in open-circuit voltage when comparing As-doped, Cu-doped and undoped devices. The choice of CdSeTe instead of a CdTe-only absorber has been explained using first-principle density functional theory model. A SCAPS device model is used to analyze the potential causes for lower open-circuit voltage.

14 SOLAR ENERGY↗
DOE OSTI2020

Degenerate doping in B-Ga 2 O 3 Single Crystals through Hf-doping

n-type conductivity of β-Ga 2 O 3 grown from the melt is typically achieved using Sn and Si. In this paper, we experimentally and computationally investigate Hf doping of β-Ga 2 O 3 single crystals using UV–vis-NIR absorption and Hall effect measurements and hybrid functional calculations. Unintentionally-doped and Hf-doped samples with a nominal concentration of 0.5at% were grown from the melt using vertical gradient freeze and Czochralski method in mixed Ar + O 2 atmosphere. We demonstrate Hf dopants, predicted to incorporate on the octahedral GaII site as a shallow donor, achieve degenerate doping in β-Ga 2 O 3 with a measured electron concentration ~2 × 10 19 cm -3 , mobility 80–65 cm 2 V -1 s -1 , and resistivity down to 5 mΩ cm in our samples. The concentration of Hf was measured to be 1.3 × 10 19 atoms cm -3 using glow discharge mass spectroscopy on doped samples, confirming Hf to be the cause of n-type conductivity (electron concentration ~2 × 10 19 cm -3 ).

36 MATERIALS SCIENCE↗