Toughening Brittle Bio‐P3HB with Synthetic P3HB of Engineered Stereomicrostructures

Abstract Poly(3‐hydroxybutyrate) (P3HB), a biologically produced, biodegradable natural polyester, exhibits excellent thermal and barrier properties but suffers from mechanical brittleness, largely limiting its applications. Here we report a mono‐material product design strategy to toughen stereoperfect, brittle bio or synthetic P3HB by blending it with stereomicrostructurally engineered P3HB. Through tacticity ([ mm ] from 0 to 100 %) and molecular weight ( M n to 788 kDa) tuning, high‐performance synthetic P3HB materials with tensile strength to ≈30 MPa, fracture strain to ≈800 %, and toughness to 126 MJ m −3 (>110× tougher than bio‐P3HB) have been produced. Physical blending of the brittle P3HB with such P3HB in 10 to 90 wt % dramatically enhances its ductility from ≈5 % to 95–450 % and optical clarity from 19 % to 85 % visible light transmittance while maintaining desirably high elastic modulus (>1 GPa), tensile strength (>35 MPa), and melting temperature (160–170 °C). This P3HB‐toughening‐P3HB methodology departs from the traditional approach of incorporating chemically distinct components to toughen P3HB, which hinders chemical or mechanical recycling, highlighting the potential of the mono‐material product design solely based on biodegradable P3HB to deliver P3HB materials with diverse performance properties.

Zhang, Zhen↗

DOE OSTI2023

Toughening Brittle Bio‐P3HB with Synthetic P3HB of Engineered Stereomicrostructures

Abstract Poly(3‐hydroxybutyrate) (P3HB), a biologically produced, biodegradable natural polyester, exhibits excellent thermal and barrier properties but suffers from mechanical brittleness, largely limiting its applications. Here we report a mono‐material product design strategy to toughen stereoperfect, brittle bio or synthetic P3HB by blending it with stereomicrostructurally engineered P3HB. Through tacticity ([ mm ] from 0 to 100 %) and molecular weight ( M n to 788 kDa) tuning, high‐performance synthetic P3HB materials with tensile strength to ≈30 MPa, fracture strain to ≈800 %, and toughness to 126 MJ m −3 (>110× tougher than bio‐P3HB) have been produced. Physical blending of the brittle P3HB with such P3HB in 10 to 90 wt % dramatically enhances its ductility from ≈5 % to 95–450 % and optical clarity from 19 % to 85 % visible light transmittance while maintaining desirably high elastic modulus (>1 GPa), tensile strength (>35 MPa), and melting temperature (160–170 °C). This P3HB‐toughening‐P3HB methodology departs from the traditional approach of incorporating chemically distinct components to toughen P3HB, which hinders chemical or mechanical recycling, highlighting the potential of the mono‐material product design solely based on biodegradable P3HB to deliver P3HB materials with diverse performance properties.

Chemistry↗

DOE OSTI2023

Nanoparticle Diffusion in Miscible Polymer Nanocomposite Melts

X-ray photon correlation spectroscopy measurements were used to quantify the dynamics of bare and bimodal grafted silica nanoparticles mixed with PEO melts of different molecular weights. In dilute polymer nanocomposite (PNC) samples, we find diffusive NP behavior as described by the Stokes–Einstein relationship so long as the adsorbed PEO polymer layer is taken into account in determining both the effective NP size and its role on composite viscosity. The size of this bound layer was found to be approximately 2R g , where R g is the chain radius of gyration. We also expanded our system to investigate how the dynamics of grafted NPs differ from bare NPs with an adsorbed layer. We showed that the dynamics again can be determined by an effective NP radius at a scale smaller than the effective interparticle spacing; however, at larger length scales, the morphology and grafting parameters play a major role in the system dynamics. These results allow us to quantify NP ordering driven by polymer crystallization. It has previously been speculated that behavior is controlled by the relative ratio of time scale of crystal growth and the diffusive time scale of the NPs, a Peclet number. When the former time scale is longer, then the NPs are expected to be segregated into the interlamellar amorphous zones, while the NPs are too slow to be reorganized in the opposite case. We show here that this conjecture is quantitatively correct and the demarcation in behavior occurs for Pe = 1. Thus, we provide a way to estimate a critical spherulite growth rate for any semicrystalline PNC, at which a given NP can be ordered. Together, the results of this study permit us to tunably design PNCs through directed dispersion of NPs in a polymer matrix.

77 NANOSCIENCE AND NANOTECHNOLOGY↗

DOE OSTI2023

Installing Controlled Stereo-Defects Yields Semicrystalline and Biodegradable Poly(3-Hydroxybutyrate) with High Toughness and Optical Clarity

Stereo-defects present in stereo-regular polymers often diminish thermal and mechanical properties, and hence suppressing or eliminating them is a major aspirational goal for achieving polymers with optimal or enhanced properties. Here, we accomplish the opposite by introducing controlled stereo-defects to semicrystalline biodegradable poly(3-hydroxybutyrate) (P3HB), which offers an attractive biodegradable alternative to semicrystalline isotactic polypropylene but is brittle and opaque. We enhance the specific properties and mechanical performance of P3HB by drastically toughening it and also rendering it with the desired optical clarity while maintaining its biodegradability and crystallinity. This toughening strategy of stereo-microstructural engineering without changing the chemical compositions also departs from the conventional approach of toughening P3HB through copolymerization that increases chemical complexity, suppresses crystal-lization in the resulting copolymers, and is thus undesirable in the context of polymer recycling and performance. More specifically, syndio-rich P3HB (sr-P3HB), readily synthesized from the eight-membered meso-dimethyl diolide, has a unique set of stereo-microstructures comprising enriched syndiotactic [rr] and no isotactic [mm] triads but abundant stereo-defects randomly distributed along the chain. This sr-P3HB material is characterized by high toughness (UT = 96 MJ/m 3 ) as a result of its high elongation at break (>400%) and tensile strength (34 MPa), crystallinity (T m = 114 degrees C), optical clarity (due to its submicron spherulites), and good barrier properties, while it still biodegrades in freshwater and soil.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗