Recycled graphite enabled superior performance for lithium ion batteries

Recycling graphite attracts growing attention since cumulative amount of spent Li-ion batteries and the shortage of graphite supply chain. Although various recycling methods have been reported, the recycled graphite cannot reach the strict commercial standards of purity, scalability, efficiency, and capacity, preventing it from battery manufacturing. Herein, the important roles of defects and functional groups on the graphite surface are deeply studied, and a closed-loop graphite recycling process with the surface recovery and modification for the graphite from the end-of-life batteries is demonstrated. The recovered graphite delivers a purity of over 99.9 % and an average initial coulombic efficiency of 91.5 %. Compared with commercial graphite in industrial standard battery testing parameters, full cells with recovered graphite possess enhanced rate reversibility, doubled cycle life, over 10 % higher capacity along with half anode material cost. In conclusion, these impressive results not only underscore the transformative potential of surface reconstruction and modification in graphite recycling, but also present economic feasibility and sustainable pathway for significantly improving battery performance and addressing global resource challenges via integration with the hydrometallurgical recycling process.

25 ENERGY STORAGE↗

DOE OSTI2024

Acid Etching‐Driven Self‐Assembly of Mn‐Shell Inducing Rock‐Salt Phase for Enhanced Single‐Crystal Ni‐Rich Cathodes

With the wide adoption of Li‐ion batteries, Ni‐rich cathode is considered as one of the most promising candidates of cathodes due to its high energy density and low cost. However, stability decreased with increasing Ni content in the Ni‐rich cathode. To solve this bottleneck, many strategies, such as coating, doping, surface modification, and special morphologies, have been developed. Herein, we introduce a groundbreaking approach for enhancing Ni‐rich cathode through an innovative acid etching process that promotes Mn shell self‐assembly, inducing a rock‐salt phase on the surface. This method not only simplifies the Ni‐rich cathode modification process, but also significantly improves the structural stability and electrochemical performance of Ni‐rich cathode. Our findings demonstrate that developed single‐crystal Ni‐rich cathode shows 3–34 % better stability compared to both commercial modified Ni‐rich cathode and unmodified counterparts. The unique Mn shell effectively mitigates reversible phase shifts during cycling, contributing to a remarkable enhancement in cycling stability. Additionally, this novel fabrication technique paves the way for cost‐effective production of high‐performance cathode materials, offering substantial benefits for lithium‐ion battery technology. And this study proves the potential of this method in advancing the design and development of durable, high‐capacity cathode materials for next‐generation batteries.

Ni-rich cathode↗

DOE OSTI2024

Understanding the Effects of Bi Modification on the Properties of Ni-Rich Cathodes

With the skyrocketing market demands for energy storage, lithium ions batteries (LIB) with higher energy density are urgently needed. Cathodes play a critical role in determining the energy density of LIB, and the most popular one is Ni-rich cathode due to its high capacity. However, due to the fast structural degradation, Ni-rich cathode materials should be further modified to achieve higher stability. Herein, we introduce bismuth ions in LiNi 0.83 Co 0.11 Mn 0.06 O 2 cathodes by adding Bi 2 O 3 during sintering to optimize the specific capacity and cycle stability. By adding 0.1% mol Bi, the Li + diffusion and structural stability are effectively optimized, leading to improved electrochemical performances. Further, the modified sample delivers much higher specific capacity (222.9 mAhg -1 , 0.05 C) than unmodified sample (204 mAhg -1 , 0.05 C). Meanwhile, the specific capacity of optimized sample after 100 cycles at 0.33 C is 27.75 mAhg -1 higher than that of unmodified sample. Therefore, this work demonstrates that Bi modification can be regarded as a possible solution to optimizing the electrochemical performance of Ni-rich cathodes.

25 ENERGY STORAGE↗

DOE OSTI2023

Facile etching for single crystal cathode materials

A recycling and synthesis of charge material for secondary batteries generates single-crystal charge materials for producing batteries with greater charge cycle longevity. Charge material particles undergo a heating for fusing or enhancing grain boundaries between polycrystalline particles. The resulting, more well-defined grain boundaries are easily etched by a relatively weak mineral acid solution. The acid solution removes material at the grain boundaries to separate secondary particles into primary particles along the grain boundaries. The resulting single crystal (monocrystalline) charge material particles are washed and filtered, and typically re-sintered to accommodate any needed lithium (lithium carbonate), and result in a charge material with larger surface area, higher lithium diffusivity and lower cation ordering.

Wang, Yan↗

DOE OSTI2023

Regulating Anionic Redox via Mg Substitution in Mn-Rich Layered Oxide Cathodes Enabling High Electrochemical Stability for Sodium-Ion Batteries

Here, with the limited resources and high cost of lithium-ion batteries (LIBs) and the ever-increasing market demands, sodium-ion batteries (SIBs) gain much interest due to their economical sustainability, and similar chemistry and manufacturing processes to LIBs. As cathodes play a vital role in determining the energy density of SIBs, Mn-based layered oxides are promising cathodes due to their low cost, environmental friendliness, and high theoretical capacity. However, the main challenge is structural instability upon cycling at high voltage. Herein, Mg is introduced into the P2-type Na 0.62 Ni 0.25 Mn 0.75 O 2 cathode to enhance electrochemical stability. By combining electrochemical testing and material characterizations, it is found that substituting 10 mol% Mg can effectively alleviate the P2–O2 phase transition, Jahn-Teller distortion, and irreversible oxygen redox. Moreover, structural integrity is greatly improved. These lead to enhanced electrochemical performances. With the optimized sample, a remarkable capacity retention of 92% in the half cell after 100 cycles and 95% in the full cell after 170 cycles can be achieved. Altogether, this work provides an alternative way to stabilize P2-type Mn-based layer oxide cathodes, which in turn, put forward the development of this material for the next-generation SIBs.