Capability to Process and Characterize Uranium-Zirconium (U-Zr) and Uranium-Zirconium-Plutonium (U-Zr-Pu) Alloys

This work investigated co-reduction of anhydrous compounds of uranium, zirconium, and plutonium to produce uranium rich ternary nuclear fuel alloys. Metallothermic co-reduction is a novel method to produce all-metal nuclear fuels. Metal fuels offer thermal, fissility, compatibility, and security benefits over oxide fuels. Alloys of uranium–10% zirconium with plutonium contents of 0%, 2.5%, 5%, and 10% were produced, with yields of 60–85% of theoretical values in a traditional calciothermic bomb reduction apparatus. Microstructural analysis indicated transformation of uranium phase from gamma to beta and then alpha, in alternating lamellar plates typical of alpha phase uranium and delta phase uranium-zirconium, with zirconium and carbides at prior grain boundaries. Some of the analyses were inconclusive in their results and therefore require additional testing. Successful ternary co-reduction would simplify production of homogeneous feedstock and thereby streamline manufacture of homogeneous ternary metallic fuel.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

PNNL FY2021 Sibling Pin Testing Results

The post-irradiation examination, axial tensile, burst, and four-point bend testing results of the first two sibling pins, 6U3/L8 and 5K7/P2 are presented.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2021

Thermal properties of U-Mo alloys irradiated under high fission power density

A variety of physical and thermal property measurements made on irradiated U-Mo alloy monolithic fuel samples with a Zr diffusion barrier and clad in Al alloy 6061 are reported. These properties form the basis for additional investigations in thermal behavior of U-Mo fuel under high performance research reactor irradiation conditions. Measurements were performed on samples harvested from fuel plates irradiated under high fission power density and surface heat flux and complement previous measurements on samples subjected to moderate fission power density and surface heat flux. Specific heat capacity of irradiated monolithic U-Mo increases with increasing temperature and fission density, but carries large uncertainties associated with thickness measurements used to determine the mass fraction of the layer constituents for extraction of the U-Mo specific heat capacity, specifically the very thin and nonuniform Zr diffusion barrier. Density of irradiated monolithic U-Mo decreases with increasing fission density resulting from fission gas swelling and porosity formation. Thermal diffusivity of irradiated monolithic U-Mo increased with increasing temperature and decreased with increasing fission density. Thermal conductivity of irradiated monolithic U-Mo increased with increasing temperature, and in general, appeared to decrease and become less sensitive to temperature with increasing fission density. Thermal conductivity measurements compared to a semi-empirical model agreed within ±30%. It is suspected that the main driver in deviation between model calculations and measurements is the fission gas swelling determination, which does not account for fission power density or irradiation temperature.

uranium (U), molybdenum, nuclear fuel, thermal con↗