Smoke density studies on twelve cellulosic and five synthetic materials using the Arapahoe and NBS smoke chambers show an empirical relationship between smoke weight as per cent of initial weight in the Arapahoe test and maximum specific optical density under piloted conditions in the NBS test. The NBS optical density data under piloted conditions exhibited sensitivity to test artifacts such as type of pilot burner.
Statistical examination of animal response data obtained using Procedure B of the USF toxicity screening test method indicates that the data deviate only slightly from a normal or Gaussian distribution. This slight departure from normality is not expected to invalidate conclusions based on theoretical statistics. Comparison of times to staggering, convulsions, collapse, and death as endpoints shows that time to death appears to be the most reliable endpoint because it offers the lowest probability of missed observations and premature judgements.
The density of smoke produced by burning or smoldering materials is a factor that affects the ability of occupants to escape from a burning structure and the effectiveness of firefighters. Accordingly, considerable effort is being spent on developing materials that minimize the amount of smoke without impairing their performance characteristics. In the present paper, laboratory tests on such materials are described and evaluated. It is seen that the National Bureau of Standards smoke test and the Ohio State University release-rate test are the most promising for screening materials for smoke evolution. It is shown that, for plastics, smoke obscuration is a more realistic concern than smoke toxicity.
Various samples of cellular polymers were evaluated for toxicity of pyrolysis gases, using the screening test method developed at the University of San Francisco. The cellular polymer samples included polyimide, polymethacrylimide, polybismaleimide, polyurethane, polyisocyanurate, polyethylene, polychloroprene, polyvinyl chloride, polystyrene, polysiloxane, and polyphosphazene. The cellular polymers exhibited varying levels of toxicity under these test conditions. Among the rigid cellular polymers, times to death were shortest with the imide type foams and longest with polyvinyl chloride and polystyrene. Among the flexible cellular polymers, times to death were shortest with polyimide and polyester, and longest with polychloroprene and polysiloxane. Increased char yield was not necessarily associated with reduced toxicity.
Explore the source record for details and available documents.
Times to incapacitation and death and LC50 values were determined for male Swiss albino mice exposed to different concentrations of sulfur dioxide in a 4.2 liter hemispherical chamber. The LC50 for a 30 minute exposure was about 3000 ppm SO2.
Times to incapacitation and death and LC50 values were determined for male Swiss albino mice exposed to different concentrations of nitrogen dioxide in a 4.2 liter hemispherical chamber. The LC50 for a 10 minute exposure was about 1000 ppm NO2.