Understanding the Feasibility of MAB Phase Structures for Lunar Applications
During the ten-week internship, my work focused on synthesis, characterization, and tailoring the flowability of the MAB phase powders for improving the surface finish and decreasing porosity of 3D-printed MAB phase structures. My mentor for the project was Dr. Samuel Hocker from NASA Langley and my faculty advisor was Dr. Surojit Gupta from the University of North Dakota. I also collaborated with Daniel Trieff from the University of North Dakota in developing characterization paradigm of 3D printed samples. The microencapsulation was performed via novel solvent casting-based microencapsulation process pioneered in UND, wherein a polymer (PLA, PHA) was dissolved into dichloromethane and precipitated onto the surface of the MoAlB particles. Two 100mL samples of microencapsulated powder was outsourced to Particle Technology Labs for flowability testing along with a 100mL control sample to determine if microencapsulation is a valid method for improving the flowability. The microencapsulated powders were characterized using SEM, Differential Scanning Calorimetry, and optical microscopy. The SEM images showed no change between the pure and microencapsulated powders. The optical microscopy analysis indicated a reduction in reflectivity for the PLA microencapsulated powders as well as hydrophobic properties. Both results suggest that microencapsulation was successful as PLA is a hydrophobic polymer and the change in reflectivity could be a result of the light being dispersed through the polymer coating. A reflectivity analysis will be done to bring more perspective to these observations. If powder flowability is improved, then the project will move forward with testing the printability of the microencapsulated powders and characterizing the structures using the designed characterization protocol. We are waiting for the DSC results. The characterization protocol for the 3D-printed MAB structures included a visual inspection of the plates to rule out any samples that had spalled or delaminated, optical microscopy to document surface features, porosity, and decomposition, and cleaning of the plates using an ultrasonic bath in preparation for SEM, EDS, and profilometry analyses.