DOE OSTI2022

The effect of Ti content on age hardening and mechanical properties of uranium-titanium alloys

Here, the effect of Ti content on age hardening and the resulting mechanical properties are described for -quenched U-Ti alloys containing 0.3 wt.% to 2.0 wt.%Ti. Age hardening occurs between ~250°C and ~450°C. Overaging occurs at higher temperatures by cellular decomposition. Age hardening kinetics suggest that different mechanisms occur depending on Ti content and initial microstructure. Strengthening in 'a acicular martensites begins by the formation of Ti clusters which evolve into thin U 2 Ti disc shaped precipitates and later mature into continuous U 2 Ti rods beginning at peak hardness. The mechanism of hardening in 'b banded martensite is more elusive, as significant hardening occurs where atomic mobility is lower than that required for precipitate formation, similar to that reported for age hardening in ''b banded martensite in U-6%Nb. The activation energy for aging varies with Ti content and microstructure. In fully martensitic alloys containing 0.75% to 2.0%Ti it is in the vicinity of ~44 kcal/mole (184 kJ/mole). But it is lower in alloys containing less than 0.6%Ti where quenched microstructures are less than fully martensitic. Tensile ductility is high prior to aging, decreases with age hardening, is effectively zero at peak hardness, and remains low in overaged conditions. Attractive combinations of strength and ductility are best obtained in alloys containing 0.6% to 1.0%Ti which have been partially aged to fractional hardening levels no greater than ~0.6. This corresponds to the very early stages of aging, associated with clustering and the earliest stages of U 2 Ti disc formation. Alloys containing 0.45%Ti or less are not as responsive to age hardening. Alloys containing 1.5% and 2.0%Ti can be aged to higher strengths, but extreme quench rate sensitivity prevents them from being effectively heat treated in realistic section thicknesses.

36 MATERIALS SCIENCE↗

DOE OSTI2021

The effects of Ti content and quenching on phase transformations, microstructures, and mechanical properties in uranium-titanium alloys

In this work, the effect of Ti content on phase transformations, microstructures, and mechanical properties of U-Ti alloys are described for alloys containing 0.3 wt.% to 2.0 wt.%Ti. Rapid cooling is required to overcome diffusional decomposition of γ-phase and facilitate diffusionless transformation to supersaturated variants of α-phase. Critical cooling rate increases with increasing Ti content, opposite to the trend observed in U-Mo and U-Nb alloys. This difference occurs because the martensite transformation temperatures in these relatively dilute U-Ti alloys are above the knee of the C-curve for diffusional decomposition, unlike those in the more concentrated U-Mo and U-Nb alloys. In these U-Ti alloys critical cooling rate depends on the amount of undercooling required to reach M s , which increases with increasing Ti content, and the time for diffusional decomposition to occur just above M s , which decreases with increasing Ti content. The net result is that higher cooling rates are required as Ti content increases. Full quenching results in diffusionless transformation of γ-phase to supersaturated variants of α-phase. Very dilute alloys transform via a γ → β → α m sequence of massive transformations. Martensitic γ → α' a transformation begins at ~0.4%Ti, and 100% α' a microstructures are obtained from ~0.65% to ~1.4% Ti. A transition to banded α'b martensite occurs at ~1.5%Ti. Evidence suggests that the α' a to α' b transition may occur when the cubic γ-phase first transforms to tetragonal γ°, which in turn transforms to orthorhombic α' b via the sequence γ → γ° → α' b . Fully quenched alloys exhibit moderate strengths and ductilities, and their supersaturation with Ti makes them amenable to subsequent age hardening. Subcritical quenching typically results in two-phase microstructures with lower ductilities and near-zero Ti-supersaturation, eliminating the possibility of subsequent age hardening.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Uranium-Titanium Alloys: The Effect of Ti Content on Phase Transformations, Microstructures, and Mechanical Properties

This report documents the findings of collaborative research done at Sandia National Laboratory and the Y-12 Development Division during the 1980s. Ongoing progress reports were presented at various U. S. Department of Energy (DOE) meetings throughout the 1980s, but the findings were never integrated into an inclusive final report. This report provides a summary of the key findings and implications of this research. This work was supported by the DOE National Nuclear Security Administration. The effect of titanium content on phase transformations, microstructures, and mechanical properties of uranium-titanium alloys has been investigated in alloys containing 0.3 wt.% to 2.0 wt.% Ti.

36 MATERIALS SCIENCE↗