Corrosion resistive materials, systems, and methods of forming and using the materials and systems
A method to reduce corrosion rates of materials at high temperatures may include heating a mixture and applying the heated mixture to a material to be rendered thermodynamically noble. The mixture may include carbon monoxide and carbon dioxide and the material rendered thermodynamically noble may include copper or other material having similar physical properties. The copper or other similar material may be applied to a structural material and provide a surface interfacing with the mixture of carbon monoxide and carbon dioxide to prevent corrosion of the structural material. In some cases, the structural material may form a heat exchanger defining passageways for a working fluid of a power system and/or may form other passageways of the power system. The copper may be applied to the passageways as a protective coating and then made thermodynamically noble at high temperatures after interactions with the mixture of carbon monoxide and carbon dioxide.
Cold Spray of C22Gd Coatings for Nuclear Waste Storage
C22-Gd films were deposited onto 316 stainless steel up to 2.4mm thick using three different cold spray conditions. No differences in visible coating adhesion was observed between grit-blasted and as-received 316 stainless steel substrates. All of the coatings produced had a density greater than 95% of bulk. EDS and backscattered imaging suggest that no secondary phases precipitated during coating fabrication, but potential micro-segregation of phases were likely present in the as-received material. The phase segregation was still observable in the as-deposited coatings. EDS could not resolve the differences in composition of the two phases.