NASA NTRS2008

The Repair and Return to Flight of Solid Rocket Booster Forward Skirt Serial Number 20022

On April 5, 1991, a solid rocket booster (SRB) forward skirt serial number (S/N) 20022 sustained buckling damage during water impact after the launch of Space Transportation System Flight 37 (STS-37). As of that date, five forward skirts had been lost during water impact. Repair attempts began with the least damaged skirt available (S/N 20022). Sp ecial hydraulic tooling was used to remove buckled areas of the skirt. Afterwards, its aft clevis pinholes were found to be out of alignment with the redesigned solid rocket motor (RSRM) check gauge, but weld passes were used to correct this condition. Meanwhile, USA Analytics generated mechanical property data for buckled and subsequently debuckled material. Their analysis suggested that structural integrity might be improved by adding stringer reinforcements, stiffeners, to the aft bay section of the skirt. This improvement was recommended as a fleet modification to be implemented on a case-by-case basis.

Malone, T. W.↗

NASA NTRS2007

Capabilities and History of NASA Marshall Space Flight Center's Hydrogen Test Facility

The Hydrogen Test Facility (HTF) has conducted mechanical testing for aerospace materials at NASA's Marshall Space Flight Center for many years. One of the first facilities of its kind to run high-pressure cryogenic permeability tests in liquid hydrogen, HTF is now characterized as a unique national resource capable of overcoming hazardous conditions to perform tests directly in various hydrogen environments. At HTF, custom test systems are operated in eight structurally reinforced test cells from 0 to 68,948 kPa (0 to 10,000 psi) at -253 to 982 C (--423 to 1800 F) in hydrogen, air, helium, and nitrogen, with other environments available upon request. Standard mechanical procedures include compression, fatigue crack growth rate, four-point bend, high/low cycle fatigue, fracture toughness, shear, strain-to-crack, and tensile testing. Cryogenic permeability and thermal conductivity and gaseous creep testing are offered, as well as simulated service under different combinations of operating environment(s), stress, pressure, and ambient-to-extreme temperatures. Advanced tests are routinely developed upon demand, and special component testing is also available. Current efforts include the renovation of two high-pressure gaseous test cells to generate data for a J-2X engine designed for Constellation's Ares I and V vehicles. In the past, HTF has supported other critical NASA programs, such as Apollo, Space Shuttle, and Next Generation Launch Technologies. During the 1990's, hundreds of tests were conducted in liquid hydrogen and liquid nitrogen during development of the Space Shuttle's super lightweight tank, which provided the thrust required to achieve low Earth orbit for the International Space Station. This facility was designed and built in 1963. Originally called the Low Temperature Test Facility, it became known as the Cryogenic Test Facility in the late 1980's and HTF in the early 1990's.

Malone, T. W.↗

NASA NTRS2006

Qualification Testing of Solid Rocket Booster Diagonal Strut Restraint Cable Assembly Part Number 10176-0031-102/103

This Technical Memorandum presents qualification test results for solid rocket booster diagonal strut restraint cable part number 101276-00313-102/103. During flight this assembly is exposed to a range of temperatures. MIL-W-83420 shows the breaking strength of the cable as 798 kg (1,760 lb) at room temperature but does not define cable strength at the maximum temperature to which the cable is exposed during the first 2 min of flight; 669 C (1,236 F). The cable, which can be built from different corrosion resistant steel alloys, may also vary in its chemical, physical, and mechanical properties at temperature. Negative margins of safety were produced by analysis of the cable at temperature using standard knockdown factors. However, MSFC-HDBK-5 allows the use of a less conservative safety factor of 1.4 and knockdown factors verified by testing. Test results allowed a calculated knockdown factor of 0.1892 to be determined for the restraint cables, which provides a minimum breaking strength of 151 kg (333 lb) at 677 C (1,250 F) when combined with the minimum breaking strength of 0.317-cm (0.125- or 1/8-in) diameter, type 1 composition rope.

Malone, T. W.↗

NASA NTRS2004

Evaluation of Training Samples Manually Welded With the Universal Handtool in a Space Simulation Chamber

The international space welding experiment was designed to evaluate the universal handtool (UHT) functions as a welding, brazing, coating, and cutting tool for in-space operations. The UHT is an electron beam welding system developed by the Paton Welding Institute (PWI), Kiev, Ukraine, and operated a 8 kV with up to 1 kW of power. In preparation for conducting the space welding experiment, cosmonauts were trained to properly operate the UHT and correctly process samples. This Technical Memorandum presents the results of the destructive and nondestructive evaluation of the training samples made in Russia in 1998. It was concluded that acceptable welds can be made with the UHT despite the constraints imposed by a space suit. The lap joint fillet weld configuration was more suitable than the butt joint configuration for operators with limited welding experience. The tube braze joint configuration designed by the PWI was easily brazed in a repeatable manner.

Russell, C. K.↗

NASA NTRS1993

Pulsed-Current Welding Of Nickel-Based Alloy

Joints as strong (or stronger than) joints made with constant current. Report based on study of pulsed-current versus constant-current gas/tungsten arc welding of butt joints between panels of nickel-based alloy 718. In pulsed-current welding, arc current alternated between high and low value. Enables greater control of freezing and depth of penetration of weld puddle at given heat input. Thicker sections joined. Readily incorporated into automated welding system, with resultant greater uniformity and reproducibility of welds than attained in manual welding.

Gamwell, W. R.↗

NASA NTRS1991

An evaluation of GTAW-P versus GTA welding of alloy 718

Mechanical properties were evaluated to determine statistically whether the pulsed current gas tungsten arc welding (GTAW-P) process produces welds in alloy 718 with room temperature structural performance equivalent to current Space Shuttle Main Engine (SSME) welds manufactured by the constant current GTAW-P process. Evaluations were conducted on two base metal lots, two filler metal lots, two heat input levels, and two welding processes. The material form was 0.125-inch (3.175-mm) alloy 718 sheet. Prior to welding, sheets were treated to either the ST or STA-1 condition. After welding, panels were left as welded or heat treated to the STA-1 condition, and weld beads were left intact or machined flush. Statistical analyses were performed on yield strength, ultimate tensile strength (UTS), and high cycle fatigue (HCF) properties for all the post welded material conditions. Analyses of variance were performed on the data to determine if there were any significant effects on UTS or HCF life due to variations in base metal, filler metal, heat input level, or welding process. Statistical analyses showed that the GTAW-P process does produce welds with room temperature structural performance equivalent to current SSME welds manufactured by the GTAW process, regardless of prior material condition or post welding condition.

Gamwell, W. R.↗