Maloy, Stuart A.

Publications and source records attributed to Maloy, Stuart A..

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2026

Thermal Stability and Ion Irradiation Response of Refined Grained V – 4Cr – 4Ti

Since the 1960’s, there has been interest in V-4Cr-4Ti and similar alloys as candidates for low activation structural materials for advanced nuclear reactors. V-4Cr-4Ti was produced using arc melting and subsequently subjected to large strain extrusion machining to produce a multimodal microstructure largely composed of nanocrystalline and ultrafine grain sizes. In-situ thermal stability of the multimodal V-4Cr-4Ti to 800 °C shows the formation of vanadium carbides with negligible grain growth. In-situ dual-beam 16 KeV He+ and 1 MeV Kr2+ ion irradiation performed at 700 °C to a final dose of ~5 displacements per atom show the formation of small He cavities well distributed throughout the system, with preferential clustering at grain boundaries. This work provides insight into how the increased fraction of grain boundaries affect the simultaneous dual beam ion irradiation response of multimodal V – 4 wt.% Cr – 4 wt.% Ti at elevated temperatures. Analysis of the cavities reveal an areal density of 0.024±0.007 cavities/nm2 and swelling of 0.236% after the dual-beam ion irradiation. Nanoindentation shows a ~50% increase in hardening after the ion irradiation at 700 °C.

TEM↗
DOE OSTI2024

Thermomechanical Processing for Improved Mechanical Properties of HT9 Steels

Thermomechanical processing (TMP) of ferritic–martensitic (FM) steels, such as HT9 (Fe–12Cr–1MoWV) steels, involves normalizing, quenching, and tempering to create a microstructure of fine ferritic/martensitic laths with carbide precipitates. HT9 steels are used in fast reactor core components due to their high-temperature strength and resistance to irradiation damage. However, traditional TMP methods for these steels often result in performance limitations under irradiation, including embrittlement at low temperatures (<~430 °C), insufficient strength and toughness at higher temperatures (>500 °C), and void swelling after high-dose irradiation (>200 dpa). This research aimed to enhance both fracture toughness and strength at high temperatures by creating a quenched and tempered martensitic structure with ultrafine laths and precipitates through rapid quenching and unconventional tempering. Mechanical testing revealed significant variations in strength and fracture toughness depending on the processing route, particularly the tempering conditions. Tailored TMP approaches, combining rapid quenching with limited tempering, elevated strength to levels comparable to nano-oxide strengthened ferritic alloys while preserving fracture toughness. For optimal properties in high-Cr steels for future reactor applications, this study recommends a modified tempering treatment, i.e., post-quench annealing at 500 °C or 600 °C for 1 h, possibly followed by a brief tempering at a slightly higher temperature.

36 MATERIALS SCIENCE↗
DOE OSTI2024

The effect of neutron irradiation on conventional and nanocrystalline nickel: NSUF Work Package UA-22PN080501 Milestone M3UA-22PN0805012 (Final Report)

Even though nanocrystalline materials (20-100 nm) present an unprecedented potential, scientific knowledge related to the effect of neutron irradiation on the mechanical properties and microstructure is still scarce. Most of the past studies were conducted using ion irradiation which may not have the same effect as neutron irradiation because of the smaller irradiation volume and the higher dose rate. To reach a firm conclusion on the potential of nanocrystalline materials for nuclear reactor applications, extensive study of model metals with different stacking fault energy (SFE) is required to elucidate their behavior in radiation environments. Nanocrystalline copper and nickel are typically chosen because they are commonly used as model FCC metals in studies of radiation effects. Nickel is an FCC metal with a high stacking-fault energy (~125 mJ/m 2 ) compared to copper (~45 mJ/m 2 ). Hence, microcrystalline and nanocrystalline nickel samples were irradiated in the INL’s Advanced Test Reactor (ATR), as a part of FY08 North Carolina State University NSUF Irradiation Experiment# 96 to evaluate the irradiation behavior of these materials. The objective of this FY20 NSUF project# 19122 is to perform PIE (at PNNL NSUF facility) on previously ATR-neutron irradiated (1.2 and 2.6 dpa; 80-89°C) nanocrystalline and microcrystalline nickel samples to investigate the changes in mechanical properties and microstructures and evaluate whether nanocrystalline nickel is relatively more radiation resistant compared to conventional microcrystalline nickel. To perform PIE at PNNL, sixteen neutron irradiated specimens (microcrystalline and nanocrystalline) were transferred from the NSUF Nuclear Fuels and Materials Library at INL. Experimental techniques such as SEM/EBSD, XRD, TEM, Vickers microhardness and tensile testing were employed to characterize the effect of neutron irradiation on the microstructure and mechanical properties of nanocrystalline nickel and compared them with corresponding characteristics of microcrystalline nickel.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Investigating microstructural evolution in SolidStir™ extruded oxide dispersion strengthened 14YWT alloy fuel cladding tube

Structural components for extreme environments require advanced materials and manufacturing processes. One such advanced material is oxide dispersion strengthened (ODS) Fe–14 wt.%Cr–3W–0.4Ti–0.3Y 2 O 3 (14YWT), which is developed for components to be used in Gen IV and fusion nuclear reactors. However, the conventional manufacturing processes to produce components, such as fuel cladding tubes, either do not retain the desired microstructural attributes or are costly and less efficient. As a result, a more attractive option is a novel manufacturing process developed on the principle of friction stir welding or processing (FSW/P) and commercially referred to as SolidStir™ Extrusion (SSE). Here this study used the SSE technique to study the manufacturing and microstructural evolution of a fuel cladding tube made of ODS 14YWT alloy. The cladding extrusion by the SSE technique involved the use of ball-milled 14YWT powders with Y, Ti, and O in the solid solution and the use of a specially designed W-25Re-Hf tool for consolidation and extrusion of the powders. A scanning electron microscope (SEM), electron backscattered diffraction (EBSD), and transmission electron microscope (TEM) were utilized for microstructural characterization. A Keyence microscope captured macrostructural photographs of the extruded tube. EBSD examination of the extruded tube on both transverse and longitudinal cross-sections showed the presence of dynamically recrystallized grains and revealed that the average grain size of the transverse cross-section was smaller than that of the longitudinal cross-section. The texture was weak and consisted of some amount of shear texture. The presence of nano-oxide clusters or precipitates of Y, Ti, and O (pyrochlores) in the extruded tube was determined by TEM. Aging heat treatment caused the average precipitate size to decrease and the density to increase compared to the as-processed condition. The results indicated that SSE is a viable tool for manufacturing fuel cladding tubes with the desired microstructural attributes.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Assessing Manufacturability of the Oxide Dispersion Strengthened (ODS) 14YWT Alloy Fuel Cladding Tube Using SolidStir™ Technology

The 14YWT (Fe–14Cr–3W–0.4Ti–0.3Y2O3 (wt.%)) alloy is a potential candidatematerial for fabricating fuel cladding tubes and other structural components to be used in next-generation advanced nuclear reactors. Due to inherent limitations of current processing routes, this research explored a new variant of friction stir processing, commercially referred to as SolidStir™ Extrusion (patent pending) technology from Enabled Engineering to consolidate and extrude 14YWT powder into a fuel cladding tube. Several single-layer and multiple-layer consolidation experiments were carried out in an Inconel 625 die to determine the suitable processing parameters for SolidStir™ extrusion of the 14YWT alloy cladding tube. With these processing parameters, a 16–18 mm long tube of the 14YWT alloy with no visible defects was successfully extruded using this novel technology. Microstructural characterization results obtained using optical microscopy, scanning electron microscopy, energy dispersive spectroscopy, electron backscatter diffraction, and transmission electron microscopy will be presented.

Advanced Materials and Manufacturing Technology↗
DOE OSTI2022

Heavy ion irradiation effects on CrFeMnNi and AlCrFeMnNi high entropy alloys

Co-free but Al-included medium/high entropy alloys (M/HEAs) have gained increasing interests due to their lower cost and the potential to tune the multi-phase microstructure. The irradiation response of two Co-free HEAs, face-centered cubic (FCC) CrFeMnNi with limited Cr enriched α' phase and body-centered cubic (BCC) AlCrFeMnNi with B2s phase and nanoprecipitates were explored. Ion irradiations using 5 MeV Fe 2+ ions were performed at 500°C to a peak fluence of 50 and/or 100 displacements per atom (dpa). In dual-phase AlCrFeMnNi, there was no significant radiation induced segregation or chemical intermixing at the coherent matrix (FeCrMn-rich)/second phase (AlNi-rich) boundaries. In CrFeMnNi, limited voids were only detected at the peak damage location of ~ 50 dpa. On the other hand, voids were widely distributed in AlCrFeMnNi: under 50 and 100 dpa irradiation conditions, voids were found with larger dimension and denser distribution in the FeCrMn-rich matrix, smaller and slightly lower density in an AlNi-rich second phase. In addition, the diameter of the FeCMn-rich nanoprecipitates didn't reveal any tendency of dissolution or growth. This is correlated with their superior structural stability against irradiation. Significant radiation-induced hardening (increases from 3.8 ± 0.2 GPa to 4.7 ± 0.6 GPa) was measured in CrFeMnNi, but only ~ 4% hardness increase (from 7.4 ± 0.8 GPa to 7.7 ± 0.4 GPa) was noted in AlCrFeMnNi. Finally, in addition to the radiation-induced defects, such as voids, dislocation loops and point defects, other factors, such as chemical short-range ordering may play an important role.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Draft Critical Minerals Evaluation Report: Advanced Materials and Manufacturing Technology

Future energy production by sustainable clean energy technologies will be influenced by the availability and projected supply risks of critical minerals. In this report we discuss this context from the perspective of a sustainable nuclear energy technology and the benefits from the deployment of advanced manufacturing. In the past, the demand of critical minerals in the energy sector was minor, but in recent years renewable energy systems do force a substantial increase in the requirements for critical minerals which further induces pressure on the supply of critical minerals such as chromium, cobalt, nickel, niobium, tantalum, titanium, tungsten, vanadium, and zirconium for nuclear energy technology. The demand of critical minerals for nuclear technology is, besides beryllium and hafnium, minor and less than 1 % of the world supply. This alleviates the negative impact as the nuclear industry may not be able to provide the most compelling priority for the suppliers and to other policymakers looking at the overall needs. In this draft report, detailed background information is provided on the mineralogy of the identified critical minerals, supply chain risks followed by the discussion of specific minerals applicable to material relevant to nuclear energy technology. Briefly, the impact of advanced manufacturing on savings of critical minerals and electric energy is discussed and its effect to nuclear energy technology evaluated. This report will be followed with a final report providing a strategic vision for executable actions to implement the savings through advanced manufacturing, which will be further explored in the upcoming months. The Gen-IV relevant critical minerals will also be evaluated in the context of the AMMT programs material priorities as identified in the material score cards, to determine priorities for future actions. Material savings will become even more substantial when commercial Gen-IV reactor technology becomes available because of their needs for structural materials with higher content in alloying elements for enhanced high-temperature properties and improved corrosion resistance. The requirement for critical minerals in nuclear technology (in kg/MWe) will therefore significantly increase by 2050, even though its contribution to the worldwide electric energy production capacity will remain at about 5 %. The share of nuclear on world’s electric energy production is, on grounds of high utilization and availability 10.2 % and is expected to increase to 12 % by 2050. Advanced manufacturing could aid the deployment of Gen-IV nuclear technology since critical materials savings of up to 30 % seems possible, promoting nuclear energy as a true sustainable clean energy technology together with hydroelectric power.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Tempering kinetics during multilayer laser additive manufacturing of a ferritic steel

Grade 91 steel forms martensite during additive manufacturing and the extent of tempering of martensite significantly affects the mechanical properties of parts. Currently, there is a lack of quantitative understanding of the tempering kinetics for Grade 91 steel, and as a result, the effects of repeated thermal cycles on properties for different processing conditions cannot be determined. Here we evaluate the tempering kinetics by determining the constant terms in the Johnson Mehl Avrami kinetic equation from the tempering data available in the literature and the thermal cycles computed using a rigorously-tested heat and fluid flow model of multi-layer additive manufacturing. The raw tempering data are cleaned using a neural network to enhance accuracy. The lower layers experience repeating cycles of heating and cooling when the upper layers are added. As a result, the hardness is reduced owing to the tempering of martensite. In contrast, martensite formed in the upper layers is not tempered to the same extent and the hardness remains high. Therefore, the hardness of the part increases with the distance from the substrate. Variations in the heat input at different laser powers and scanning speeds significantly affect the extent of tempering. Finally, since the method used here can provide a quantitative understanding of the tempering of martensite and the spatial variation in hardness, it can be used to tailor the microstructure and hardness of heat treatable printed metallic parts.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Materials Scorecards, Phase 2: Advanced Materials and Manufacturing Technology

This report presents updated material score cards with detailed justification of the proposed rating provided and quantifies the readiness of the advanced manufacturing of materials for nuclear applications. Based on an expanded literature review of available data, the scores in this report (Phase 2) have either been modified or remained constant as compared with Phase 1 scoring. The rating justification are provided for each scoring criteria whereas the maturity quantification of additively manufactured alloys and the knowledge gaps are discussed with reference traceability. This report focuses on the detailed justification and traceability for the adoption of additively manufactured 316SS, SS304, Alloy 800H, Graphite C/C, Alloy N, Silicon Carbide, HT9, Alloy 617, and Alloy 718. Significant variability in data and knowledge gaps exist among the identified materials. The scorecards are therefore based on published literature data, industry response to a survey, stakeholder input collected at workshops, and expert opinion. The interpretation and assessment were somewhat challenged as experimental process parameters and methodology varied and best judgment was exercised for score quantification. This assessment reflects the overall level of technical maturity for AM materials and their deployment in Gen-VI nuclear systems. These Phase 2 scorecards are likely to be revised based on additional input from stakeholders and as new research results become available.

36 MATERIALS SCIENCE↗
DOE OSTI2022

High-Throughput Nanoindentation Mapping of Additively Manufactured T91 Steel

Here, this work aims to adapt nanoindentation mapping combined with a k-means algorithm as a high-throughput technique to study the nano-scale spatial changes in mechanical properties for a heterogeneous material. This technique can also classify the individual data points based on their properties. Hundreds to thousands of indents were performed on additively manufactured T91 at room temperature, 300°C, 400°C, and 500°C across a square area with a side length of 120 μm to 400 μm. From this data, the hardness and reduced modulus at each point could be calculated and mapped. Using k-means clustering, we were able to arrange the data into three or four clusters corresponding roughly to the ferritic and martensitic phases as well as one or two intermediate clusters sampling both the phases. The hardness of these two phases appears to be quite stable as a function of temperature. Nanoindentation mapping and the k-means algorithm can therefore be used to rapidly assess the feasibility of heterogeneous materials under extreme conditions, such as nuclear reactor steels.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Helium-bubble-enhanced disordering of intermetallic phase under irradiation

Understanding and controlling phase transformations in metals and alloys under irradiation is vital to the design of irradiation-tolerant materials. The L1 2 -ordered intermetallic phase in nickel-based superalloys provides superior high-temperature mechanical properties and corrosion resistance. Here, we studied the order-disorder transformation kinetics of an L1 2 -structured gamma-prime phase in nickel-based superalloy Rene N4 under krypton ion irradiation and the effect of pre-implanted helium gas bubbles on the kinetics of phase transformation. Furthermore, the presence of pre-implanted helium gas bubbles significantly enhances the order-disorder transformation of L1 2 -structured gamma-prime phase under irradiation at 300 °C. The evolution of pre-implanted helium gas bubbles under irradiation implies that helium gas bubbles could effectively trap irradiation-induced vacancies and impede the reordering process of anti-site defects in gamma-prime phase.

36 MATERIALS SCIENCE↗
DOE OSTI2020

In Situ Micro-Pillar Compression to Examine Radiation-Induced Hardening Mechanisms of FeCrAl Alloys

Here, the effects of 5 MeV Fe 2+ ion irradiation at 300°C on the microstructure evolution and deformation behavior of a FeCrAl C26M alloy are presented. It has been found that dislocation loop density increases an order of magnitude from 1 dpa to 16 dpa irradiations, whereas, the dislocation loop size saturates with increasing damage. Micropillars, 600 nm in diameter and 1.3 µm in height, were fabricated and compressed inside grains with <001>, <011> and <111> crystallographic orientations, respectively. {112} <111> has been identified as the primary slip system in both unirradiated and irradiated alloy. The increase in yield stress after irradiation is observed with measurable variation along <001> and <011> vs. along <111>. By applying the Orowan dispersed barrier model, the increase of yield stress is found mainly due to the slip resistance of radiation generated defect loops. Detailed transmission electron microscopy (TEM) studies were performed to quantify the Burgers vector and the distribution of irradiation induced dislocations at elevated strains. It is revealed that localized shear instability is caused by avalanche slip events of ½<111> dislocations gliding out of tested pillars. Simultaneously, a large number of sessile/immobile <100> dislocations formed in the vicinity of slip band, leading to the hardening at elevated strains.

36 MATERIALS SCIENCE↗