Engineering topics
Mandujano, H. Cein
Publications and source records attributed to Mandujano, H. Cein.
Resilience of the Aurivillius structure upon La and Cr doping in a Bi 5 Ti 3 FeO 15 multiferroic
Here, combining the experimental techniques of high-resolution X-ray diffraction, magnetometry, specific heat measurement, and X-ray photoelectron, Raman and dielectric spectroscopy techniques, we have studied the influence of La and Cr doping on the crystal structure and magnetism of the room temperature Aurivillius multiferroic Bi 5 Ti 3 FeO 15 by investigating the physical properties of (Bi 4 La)Ti 3 FeO 15 and Bi 5 Ti 3 (Fe 0.5 Cr 0.5 )O 15 . The parent (Bi 5 Ti 3 FeO 15 ) and the doped ((Bi 4 La)Ti 3 FeO 15 and Bi 5 Ti 3 (Fe 0.5 Cr 0.5 )O 15 ) compounds crystallize in the A2 1 am space group, which is confirmed through our analysis of high-resolution synchrotron X-ray diffraction data obtained on phase-pure polycrystalline powders. We determined the oxidation states of the metal atoms in the studied compounds as Fe 3+ , Ti 4+ , Cr 3+ , and La 3+ through the analysis of X-ray photoelectron spectroscopy data. The magnetic susceptibilities of the three compounds are marked by the absence of a long-range ordered ground state, but dominated by superparamagnetic clusters with dominant antiferromagnetic interactions. This signature of short-range magnetism is also seen in specific heat as a low temperature enhancement which is suppressed upon the application of external magnetic fields up to 8 T. Our dielectric spectroscopy experiments showed that the three studied compounds display similar features in the dielectric constant measured as a function of frequency. However, upon doping La at the Bi site, the width of the ferroelectric hysteresis loop increases for (Bi 4 La)Ti 3 FeO 15 compared to that of the parent compound Bi 5 Ti 3 FeO 15 , and with Cr doping, Bi 5 Ti 3 (Fe 0.5 Cr 0.5 )O 15 becomes a leaky dielectric. The resilience of the Aurivillius crystal structure towards doping of La at the Bi site and Cr at the Fe site is clearly seen in the bulk properties of magnetic susceptibility, specific heat and the average crystal structure. The relevance of changes in the local structure is evident from our Raman spectroscopy and X-ray pair distribution function studies.
Structural modulation and spin glassiness upon oxidation in oxygen storage material LnFeMnO 4+x for Ln = Y, Lu, and Yb
The mixed valence multiferroic LnFe 2+ Fe 3+ O 4 (where Ln = Y, Lu, and Yb) can reversibly uptake oxygen into its lattice, which is evidenced by a crystallographic phase transition along with the appearance of structural modulations. In this study, we show that the Mn-substituted version of this multiferroic can also be readily oxidized to LnFe 3+ Mn 3+ O 4.5 revealing similar oxygen storage behavior. Through neutron, electron, and synchrotron x-ray diffraction studies, we observe a structural modulation that we attribute to a displacement wave in the fully oxidized compound. This wave exhibits commensurability with a wavevector q = (-2/7, 1/7, 0). Bond valence summation analysis of plausible interstitial oxygen positions suggests that oxygen insertion likely occurs at the middle of the Fe/Mn–O bipyramid layers. The structural modulation of LnFeMnO 4.5 is two-dimensional, propagates along the ab-plane, and is highly symmetric as 12 identical modulation vectors are observed in the diffraction patterns. The nature of the lanthanide, Ln 3+ , does not seem to influence such modulations since we observe identical satellite reflections for all three samples of Ln = Y, Lu, and Yb. Both LnFeMnO 4 and LnFeMnO 4.5 display spin glassy behavior with 2D short-range magnetic ordering being observed in LnFeMnO 4 . Analysis of the neutron diffraction data reveals a correlation length of ~10 nm. Upon oxidation to LnFeMnO 4.5 , the short-range magnetic order is significantly suppressed.
Absence of long-range magnetic order in lithium-containing honeycombs in the Li–Cr–Sb(Te)–O phases
Li 3 ((LiCr)(Te/Sb))O 6 compounds where Cr atoms along with Li and Te or Sb are part of a honeycomb and are studied using magnetic susceptibility, specific heat, x-ray photoelectron spectroscopy and neutron diffraction. The oxides stoichiometries as determined from the neutron diffraction studies are Li 4.47 Cr 0.53 TeO 6 and Li 3.88 Cr 1.12 SbO 6 with a stable oxidation state of +3 for Cr. Both the compounds crystallize in space group C2/m with intermixing of cations at the 4g sites leaving the 2a sites preferentially for Te or Sb. Again, the Li + ions alone predominantly occur in the interlayer sites. Both the compounds show a broad anomaly in specific heat at 8 K, which is robust against 8 T. A corresponding anomaly is absent in the magnetic susceptibility but recovers from its derivative, dχ(T)/dT. Here, we ascertain the magnetic anomaly temperatures (T a ) of Li 4.47 Cr 0.53 TeO 6 and Li 3.88 Cr 1.12 SbO 6 as 5.9 K and 6.7 K respectively from specific heat. Although the physical properties indicated a low temperature anomaly, neutron diffraction data did not reveal a magnetic signal or a structural anomaly down to 1.5 K. This rules out a conventional long-range ordered magnetic ground state in either compounds. Combining the results from specific heat, neutron diffraction and electron paramagnetic resonance, we put forth a scenario of depleted honeycomb lattice of Cr 3+ with predominant short-range magnetic correlations as the magnetic ground states of the title compounds.